Gutta-percha/natural latex sponge product and preparation method thereof

A technology of sponge products and natural latex, which is applied in the field of eucommia gum/natural latex sponge products and its preparation, can solve the problems of less application and less registration, and achieve the effect of expanding application prospects

Active Publication Date: 2019-11-12
CHEMCHINA ZHUZHOU RUBBER RES & DESIGN INST
View PDF6 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there are not many reports and applications of sponges prepared from Eucommia latex at home and abroad.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Gutta-percha/natural latex sponge product and preparation method thereof
  • Gutta-percha/natural latex sponge product and preparation method thereof
  • Gutta-percha/natural latex sponge product and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Preparation of Eucommia gum / natural rubber composite sponge with a ratio of 5 / 95:

[0035] (1) Preparation of mixed glue:

[0036] Calculated by mass

[0037]

[0038] Add Eucommia latex to natural rubber latex and mix evenly, add Pingping and O, stir evenly and remove ammonia to 0.1%, then add other rubber additives, stir for 8-12 hours at 30-35°C, and mature , the ripening time is 24 hours;

[0039] (2) Preparation of gel:

[0040] Calculated by mass

[0041]

[0042] After the mature composite glue is mixed at a speed of 500-1500 rpm and filled with air to quickly foam to a specified volume, it is soaked at a slow speed of 100-200 rpm, and then diluted with double the amount of soft water. The active agent zinc oxide is soaked at a speed of 200-400 rpm at a medium speed for 2 minutes, and finally sodium fluorosilicate and potassium hydroxide are added together, and treated at a speed of 200-400 rpm at a medium speed. After 2 minutes, the foam is finally po...

Embodiment 2

[0046] Preparation of Eucommia gum / natural rubber composite sponge with a ratio of 10 / 90:

[0047] (1) Preparation of mixed glue:

[0048] Calculated by mass

[0049]

[0050] Add Eucommia latex to natural rubber latex and mix evenly, add Pingping and O, stir evenly and remove ammonia to 0.1%, then add other rubber additives, stir for 8-12 hours at 30-35°C, and mature , the ripening time is 24 hours;

[0051] (2) Preparation of gel:

[0052] Calculated by mass

[0053]

[0054] After the mature composite glue is mixed at a speed of 500-1500 rpm and filled with air to quickly foam to a specified volume, it is soaked at a slow speed of 100-200 rpm, and then diluted with double the amount of soft water. The active agent zinc oxide is soaked at a speed of 200-400 rpm at a medium speed for 2 minutes, and finally sodium fluorosilicate and potassium hydroxide are added together, and treated at a speed of 200-400 rpm at a medium speed. After 2 minutes, the foam is finally p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
Login to View More

Abstract

The invention provides a gutta-percha / natural latex sponge product. The gutta-percha / natural latex sponge product is prepared from the following components: gutta-percha emulsion, natural latex, a vulcanizing agent, an active agent, an accelerant, an antiager, a filler, a stabilizer, a PH value adjust, a gelatinizer, a foaming agent, a foam stabilizer, and a blowing agent in proportion, and the gutta-percha emulsion and the natural latex are correspondingly concentration emulsion. A preparation method of the gutta-percha / natural latex sponge product comprises the steps that first, the gutta-percha emulsion and the natural latex are mixed in proportion, deammoniation is conducted through a simultaneous ongoing method of mechanical stirring and air drafting, thenvarious kinds of powder typeauxiliaries and emulsifying oil auxiliaries which are grinded into dispersoid are added into a mixture latex material, after ripening, air is inflated under the mechanical stirring, foam is generatedto expand foam, after foaming, the foam is solidified with the gelatinizer, after vulcanization, washing and dewatering and drying of the solidified foam, the gutta-percha / natural latex sponge is obtained. According to the gutta-percha / natural latex sponge product and the preparation method thereof, successfully development of the gutta-percha / natural latex sponge product expands application prospects of gutta-percha, and promotes the technical progress of the gutta-percha.

Description

technical field [0001] The invention relates to a latex sponge and a preparation method thereof, in particular to a eucommia gum / natural latex sponge product and a preparation method thereof. Background technique [0002] Eucommia gum originates from the Eucommia ulmoides tree, and mainly exists in the leaves, bark and seeds of Eucommia ulmoides, among which the leaves contain 2% to 4% of glue, the skin contains 8% to 10% of glue, and the seeds contain 10% to 30% of glue. Precious high-quality natural rubber resources, currently my country's eucommia cultivation area is about 350,000 hectares, accounting for more than 99% of the world's total eucommia planting area, with unique resource advantages. Eucommia gum, like palaquium gutta in the tropical rain forests of Southeast Asia and mimusops balata in the tropical rain forests of South America, both contain trans-1,4-polyisoprene, so Eucommia gum is also known as guttapercha or balata. The chemical composition of eucommia g...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L7/02C08K13/02C08K3/34C08K3/22C08J9/14
CPCC08J9/142C08J9/0095C08J9/0066C08J2203/12C08J2307/02
Inventor 郭舜华陈俐蔡克平
Owner CHEMCHINA ZHUZHOU RUBBER RES & DESIGN INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com