A kind of degradable polymer microsphere with surface pits and its preparation method and application

A polymer microsphere and polymer technology, applied in the field of medicine, can solve the problems of unpredictable degradation rate of the internal structure of the microsphere, unpredictable performance evolution, complicated preparation process, etc., achieving good application prospects, improved biological response characteristics, simple craftsmanship

Active Publication Date: 2022-03-18
GUANGDONG PROV MEDICAL INSTR INST
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the microspheres prepared by the above-mentioned prior art generally have the following problems: 1) multi-component, and the performance evolution during application is difficult to predict; 2) porous microspheres are prepared instead of surface pit microspheres, and the internal structure of the microspheres changes It has an unpredictable impact on its degradation rate; 3) The preparation process is complex and difficult to industrialize

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of degradable polymer microsphere with surface pits and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0030] Example 1 of the present invention is: a preparation method of degradable polymer microspheres with pits on the surface, comprising the following steps: weighing 3.0 g of poly 3-hydroxybutyrate-co-3-hydroxyvalerate and dissolving it in 10ml volatile organic solvent (chloroform); add poly-3-hydroxybutyrate-co-3-hydroxyvalerate solution to 700ml aqueous solution containing 1.5% gelatin, keep stirring at 600rpm at 45°C; after 45min Add 3.5g Freon; stop stirring after 10h of adding poly 3-hydroxybutyrate-co-3-hydroxyvalerate solution, wash with water and dry at 45°C for 24h to obtain poly 3-hydroxybutyrate-co-3-hydroxyvalerate with surface pits co-3-hydroxyvalerate microspheres.

[0031] Example 2 of the present invention is: a preparation method of degradable polymer microspheres with pits on the surface, comprising the following steps: dissolving 5.0 g of polytrimethylene carbonate in 10 ml of tetrahydrofuran; Add the ester solution to 1000ml of an aqueous solution conta...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a degradable polymer microsphere with surface pits and its preparation method and application. The preparation method includes the following steps: S1, dissolving the degradable polymer in an organic solvent to prepare a degradable polymer solution; S2 1. Add the degradable polymer solution into the aqueous solution containing surfactant, after stirring for (15-45) min, add gas foaming agent; S3, after continuing to stir for (315-705) min, wash with water and dry to obtain the obtained The degradable polymer microspheres with pits on the surface are described. The microspheres prepared by the scheme of the present invention not only have good biocompatibility and degradability, but also have surface pits suitable for cell adhesion, and have good application prospects in the field of tissue defect repair and reconstruction.

Description

technical field [0001] The invention relates to the technical field of medicine, in particular to a degradable polymer microsphere with pits on the surface and a preparation method and application thereof. Background technique [0002] Polymer microspheres usually refer to polymer aggregates with diameters ranging from nanometers to micrometers and spherical shapes. Polymer microspheres have attracted more and more scientists' interest due to their designability and multifunctionality. Among them, the spherical shape is divided into solid sphere and hollow sphere. Degradable biomicrospheres have very important applications in the medical field, some can be used as bone fillers, and some can be used as drug carriers, with great application prospects. Related research shows that compared with ordinary microspheres, microspheres with specific morphology have a larger surface area, and for tissue repair, in addition to being non-toxic to tissues and cells, it is also necessary...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): A61L27/18A61L27/22A61L27/16A61L27/20A61L27/02A61L27/50A61L27/58
CPCA61L27/18A61L27/222A61L27/16A61L27/20A61L27/025A61L27/50A61L27/58C08L67/04C08L69/00C08L29/04C08L1/02
Inventor 许为康陈龙胜邹丽丽伊翔
Owner GUANGDONG PROV MEDICAL INSTR INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap