Preparation method of modified starch ether for improving slip performance of ceramic tile glue

A technology of starch ether and tile adhesive, applied in the directions of starch-derived adhesives, adhesive types, adhesive additives, etc., can solve problems such as unfavorable industrial production and cumbersome operation, improve the sliding performance of tile adhesive, and simplify the process. , easy to operate effect

Active Publication Date: 2019-12-20
SHANDONG YITENG NEW MATERIAL CO LTD
View PDF4 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] However, the preparation of starch ether products by the existing dry method is mainly a multi-step etherification operation, which is cumbersome and unfavorable for industrial production, and generally only chemical modification is carried out.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of modified starch ether for improving slip performance of ceramic tile glue
  • Preparation method of modified starch ether for improving slip performance of ceramic tile glue
  • Preparation method of modified starch ether for improving slip performance of ceramic tile glue

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0064] A kind of preparation method of the modified starch ether that promotes tile adhesive sliding performance, comprises the following operation steps:

[0065] (1) chemical modification: starch is etherified, dried and pulverized;

[0066] Add tapioca starch, alkalizing agent NaOH, ethanol and inhibitor Na 2 SO 4 , the reactor was evacuated and purged with nitrogen to remove oxygen, evacuated again, and then etherification agents were added to the reactor: chloroacetic acid, propylene oxide and ethylene oxide, reacted at 20 ° C for 1.5 hours, and the temperature was raised to 40 React at ℃ for 2.5 hours, and at 60℃ for 4 hours. After the reaction is completed, dry and recover ethanol, and pulverize;

[0067] The mass ratio of above-mentioned tapioca starch, sodium hydroxide, chloroacetic acid, propylene oxide and ethylene oxide is=1:0.09:0.10:0.12:0.02;

[0068] The tapioca starch and inhibitor Na 2 SO 4 The mass ratio is 1:0.05;

[0069] The mass ratio of described ...

Embodiment 2

[0088] A kind of preparation method of the modified starch ether that promotes tile adhesive sliding performance, comprises the following operation steps:

[0089] (1) prepare another kind of starch ether of the present invention according to the description of embodiment 1 step (1), the difference is that the etherification agent is chloroacetic acid and propylene oxide, starch, sodium hydroxide, chloroacetic acid and cyclic The mass ratio of oxypropane is = 1:0.09:0.10:0.12, and the reaction temperature of etherification is 40°C for 3 hours and 60°C for 5 hours;

[0090] The amylose content of the raw starch is 17.23%, the amylopectin content is 68.78%, and the total starch content is 86.01%. The obtained carboxymethyl hydroxypropyl starch structure diagram is shown in Figure 4 , wherein the carboxymethyl substitution degree is 0.16, the hydroxypropoxy content is 12.6%, the 5% viscosity is 7000cp, and the ash content is 16%;

[0091] (2) Physical modification: mix the pre...

Embodiment 3

[0110] A kind of preparation method of the modified starch ether that promotes tile adhesive sliding performance, comprises the following operation steps:

[0111] (1) prepare another kind of starch ether of the present invention according to the description of embodiment 1 step (1), the difference is that the etherifying agent is propylene oxide and ethylene oxide, starch, sodium hydroxide, epoxy The mass ratio of propane to ethylene oxide is =1:0.02:0.12:0.05, and the etherification reaction temperature is 2.5 hours at 20°C, 2.5 hours at 40°C, and 4 hours at 60°C;

[0112] The amylose content of the raw starch is 17.16%, the amylopectin content is 68.73%, and the total starch content is 85.89%. The structure diagram of the prepared hydroxypropyl hydroxyethyl starch is shown in Figure 5 , marked as 1# hydroxypropyl hydroxyethyl starch, wherein the hydroxypropoxy content is 12.5%, the hydroxyethoxy content is 6.5%, the 5% viscosity is 7000cp, and the ash content is 8%;

[01...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Ash contentaaaaaaaaaa
Ash contentaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of building additives, in particular to a preparation method of a modified starch ether for improving slip performance of ceramic tile glue. The preparation method comprises the following steps: carrying out one-step etherification chemical treatment modification on starch to obtain starch ether, and carrying out physical modification treatment. According to the preparation method, the complex operation of multi-step etherification in existing modified starch ether preparation process is changed, a starch ether modified product with better performance can be obtained only by one-step simultaneous etherification, and when the obtained product is used for the ceramic tile glue, the slippage performance of ceramic tile glue can be remarkably improved because of adoption of the physical modification treatment; meanwhile, compared with the prior art, the operation conditions of one-step simultaneous etherification treatment are obviously different.

Description

technical field [0001] The invention relates to the technical field of building additives, in particular to a preparation method of modified starch ether for improving the sliding performance of tile adhesives. Background technique [0002] As a decorative material, tiles have a broad market, but with the continuous improvement of the specialization of the tile market, more and more consumers are pursuing the seamless effect of wall decoration, making large-size tiles more and more popular. At the same time, the increasing popularity of large-scale residential buildings has also promoted the popularity of large-scale tiles. The size and quality of tiles are getting bigger and bigger, and the safety requirements are getting higher and higher. Traditional tile adhesives have been difficult to meet the requirements, so new tile adhesives have been developed rapidly. [0003] The new tile adhesive composition includes cement, sand, heavy calcium, redispersible latex powder, cel...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08B31/12C09J11/08
CPCC08B31/12C09J11/08C04B24/38C04B2111/00672C08L3/08C08B31/10C09J103/08
Inventor 滕鲲赵明李青华李长胤李茂丰赵洪山张开民
Owner SHANDONG YITENG NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap