Urethane (meth)acrylate blends and urethane (meth)acrylate compositions

A technology of urethane and acrylate, applied in the direction of polyurea/polyurethane coatings, coatings, etc., can solve the problems of insufficient and non-self-healing properties, and achieve less anti-adhesion, excellent self-healing properties, and maintenance The effect of scratch resistance

Active Publication Date: 2017-12-15
NOF CORP
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In this method, a certain degree of improvement in curing shrinkage and flex resistance can be observed, but it is not sufficient, and it does not have self-healing properties

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Urethane (meth)acrylate blends and urethane (meth)acrylate compositions
  • Urethane (meth)acrylate blends and urethane (meth)acrylate compositions
  • Urethane (meth)acrylate blends and urethane (meth)acrylate compositions

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1）

[0074] Into a 1000ml long-necked flask equipped with a stirrer, a thermometer, and a condenser, 300g of a polymerizable polyoxyethylene derivative mixture, 0.1g of dibutyltin dilaurate as a urethanization catalyst, and 0.1g of 2,6-di-tert-butyl-4-methylphenol as a polymerization inhibitor. Add 217g of polyisocyanate (an isocyanurate-modified product of hexamethylene diisocyanate produced by Asahi Kasei Chemical Co., Ltd. (trade name: DURANATE TPA-100, isocyanate group content: 23.1%)) to make the polymerizable polyoxygen The hydroxyl group of the vinyl derivative mixture 1 and the isocyanate group of the polyisocyanate were 1.05:1.00, and the reaction was carried out at 60°C for 5 hours. And the reaction was carried out until the content of the isocyanate group was 0.1% or less according to the method of JIS K7301, and the urethane acrylate mixture (UA-1) which was the target product was obtained.

Embodiment 2～7）

[0076] Using the polymerizable polyoxyethylene derivative mixture or 2-hydroxyethyl acrylate described in Table 3, and polyisocyanate, urethanization catalyst, and polymerization inhibitor, the same operation as in Example 1 was carried out to obtain carbamic acid Ester acrylate mixture UA-2~UA-7.

[0077] [table 3]

[0078]

Example 1

Example 2

Example 3

Example 4

Example 5

Example 6

Example 7

urethane acrylate

UA-1

UA-2

UA-3

UA-4

UA-5

UA-6

UA-7

Mixture 1

300

-

-

-

-

-

-

mixture 2

-

350

-

-

-

-

-

Mixture 3

-

-

270

-

-

-

-

Mixture 4

-

-

-

330

-

-

-

Mixture 5

-

-

-

-

300

-

-

Mixture 6

-

-

-

-

-

320

-

2-Hydroxyethyl Acrylate

-

-

-

-

-

-

200

polyisocyanate*)

2...

Embodiment 8）

[0083] In 50 parts of the urethane acrylate mixture (UA-1) obtained in Example 1, 1.5 parts of a photopolymerization initiator (IRGACURE184 produced by BASF Corporation) was mixed, and 50 parts of methyl ethyl ketone was added to obtain a solid component Photocurable composition 1 with a content of 50%.

[0084] (Preparation of cured film 1)

[0085] On an acrylic plate having a thickness of 2 mm, the photocurable composition 1 was coated with a spin coater so that the film thickness of the coating film after drying was 10 μm. After standing still in a drying oven at 80°C for 1 minute, use an 80W / cm ultraviolet irradiation device to move it at a conveying speed of 2.0m / min and at the same time 300mJ / cm 2 The cumulative amount of light makes it solidify.

[0086] This sample is used for the evaluation of self-healing property and scratch resistance.

[0087] (self-healing)

[0088] Using a microhardness tester (Dynamic Microhardness Tester DUH-W201S produced by Shimadzu Cor...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
peel strengthaaaaaaaaaa
peel strengthaaaaaaaaaa
peel strengthaaaaaaaaaa
Login to View More

Abstract

The present invention provides a urethane (meth)acrylate capable of forming a cured film with self-healing properties, excellent scratch resistance, low curing shrinkage, and flex resistance. The urethane (meth)acrylate mixture (C) of the present invention is obtained by reacting (A) a polymerizable polyoxyethylene derivative mixture with (B) a polyisocyanate compound represented by formula (2) The (A) polymerizable polyoxyethylene derivative mixture is composed of 85-95% by mass of the polymerizable polyoxyethylene derivative represented by (A1) formula (1) and 5-15% by mass of (A2) (meth) hydroxyethyl acrylate; in the formula, R1 represents a hydrogen atom or a methyl group, n is the average number of moles added, n=3-9. In the formula, R3 each independently represents an alkylene group having 1 to 10 carbon atoms.

Description

technical field [0001] The invention relates to a urethane (meth) acrylate mixture (Urethane (meth) acrylate mixture) and a urethane (meth) acrylate composition (Urethane (meth) acrylate composition), which can form a self- A cured film that exhibits repairability, excellent scratch resistance, low cure shrinkage, flex resistance, and blocking resistance. Background technique [0002] Cases of mobile phones or personal computers, plastic products such as audio equipment, electronic material components such as touch panels and LCD screens, home appliances such as TVs, refrigerators, and washing machines, woodworking products such as furniture such as tables, chairs, and wardrobes, floors and doors The surfaces of building interiors such as handles, sporting goods such as golf clubs and tennis rackets, and automobile interiors and exteriors are easily scratched. Therefore, it is necessary to impart scratch resistance to these easily scratched products. [0003] As a method of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G18/79C08G18/67C09D175/14C09D183/07
CPCC08G18/284C08G18/792C09D175/14C08F8/30C08F220/20C08F220/34C08F220/36C08F220/281C08F220/283C08F220/286C08F220/343
Inventor 楠本光司石川正和玉井哲也
Owner NOF CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com