A kind of mortar substrate and its preparation method

A base material and mortar technology, which is applied in the field of mortar base material and its production, can solve the problems of high production cost, lack of moisture resistance and impermeability, complicated preparation process, etc., achieve low cost, eliminate follow-up effects, and reduce water absorption.

Active Publication Date: 2022-04-05
广州六润建材有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the preparation process of the existing mortar base material, there are high production costs, complicated preparation process, and no functions such as moisture resistance and impermeability. Therefore, we propose a mortar base material and its manufacturing method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A mortar substrate proposed by the present invention comprises the following raw materials in parts by weight: 100 parts of cement, 120-200 parts of quartz sand, 0.3-0.5 parts of waterproofing agent, 0.1-0.15 parts of defoaming agent, 30-50 parts of water, hydroxyethyl 5-10 parts of base cellulose, 15-25 parts of Shuangfei powder, 30-40 parts of styrene-acrylic emulsion, 1-3 parts of fungicide and 1-3 parts of anti-fungal agent.

[0025] In an optional embodiment, the waterproofing agent is a silicone waterproofing agent.

[0026] In an optional embodiment, the defoamer is a silicone defoamer.

[0027] In an optional embodiment, the fungicide is an oxazoline fungicide.

[0028] In an optional embodiment, the antifungal agent is a broad-spectrum antifungal agent.

[0029] The present invention also proposes a preparation method of mortar base material, comprising the following steps:

[0030] S1. Weigh the above-mentioned raw materials according to the above-mentioned...

Embodiment 2

[0037] A mortar substrate, comprising the following raw materials in parts by weight: 100 parts of cement, 120 parts of quartz sand, 0.3-part of waterproofing agent, 0.1 part of defoamer, 30 parts of water, 5 parts of hydroxyethyl cellulose, 15 parts of Shuangfei powder, 30 parts of styrene-acrylic emulsion, 1 part of fungicide and 1 part of antifungal agent;

[0038] In an optional embodiment, the waterproofing agent is a silicone waterproofing agent.

[0039] In an optional embodiment, the defoamer is a silicone defoamer.

[0040] In an optional embodiment, the fungicide is an oxazoline fungicide.

[0041] In an optional embodiment, the antifungal agent is a broad-spectrum antifungal agent.

[0042] The present invention also proposes a preparation method of mortar base material, comprising the following steps:

[0043] S1. Weigh the above-mentioned raw materials according to the above-mentioned parts by weight;

[0044] S2. After dry mixing cement, quartz sand, hydroxye...

Embodiment 3

[0050] A mortar substrate, comprising the following raw materials in parts by weight: 100 parts of cement, 160 parts of quartz sand, 0.4 parts of waterproofing agent, 0.12 parts of defoaming agent, 40 parts of water, 8 parts of hydroxyethyl cellulose, 20 parts of Shuangfei powder, benzene 35 parts of acrylic emulsion, 2 parts of fungicide and 2 parts of antifungal agent.

[0051] In an optional embodiment, the waterproofing agent is a silicone waterproofing agent.

[0052] In an optional embodiment, the defoamer is a silicone defoamer.

[0053] In an optional embodiment, the fungicide is an oxazoline fungicide.

[0054] In an optional embodiment, the antifungal agent is a broad-spectrum antifungal agent.

[0055] The present invention also proposes a preparation method of mortar base material, comprising the following steps:

[0056] S1. Weigh the above-mentioned raw materials according to the above-mentioned parts by weight;

[0057] S2. After dry mixing cement, quartz sa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A mortar base material comprises the following raw materials: cement, quartz sand, waterproofing agent, 0.1-0.15 parts of defoaming agent, water, hydroxyethyl cellulose, double fly powder, styrene-acrylic emulsion, bactericide and anti-mold agent. A method for preparing a mortar base material is also proposed, comprising the following steps: after dry mixing cement, quartz sand, hydroxyethyl cellulose and Shuangfei powder, adding water for stirring and mixing; obtaining mixture a; mixing waterproofing agent, defoaming agent Add the agent, styrene-acrylic emulsion, bactericide and anti-fungal agent to the water in order to stir and mix; obtain the mixture b; add the mixture b to the mixture a and stir to obtain the slurry; pour the slurry into the test mold and scrape it flat, put Curing with the mold in the curing box, take out the test mold and remove the mold to obtain the test piece; put the test piece in saturated lime water for curing, take it out and rinse it with water, dry it, and then cool it to room temperature to get the mortar base material. The invention is easy to form, low in cost, and low in shrinkage rate and water absorption rate, so that the wall surface is dry and not easy to be damp and moldy.

Description

technical field [0001] The invention relates to the field of mortar base materials, in particular to a mortar base material and a manufacturing method thereof. Background technique [0002] Waterproof coating film is a building waterproof material made of cement and fine aggregate as the main component, polymer emulsion or redispersible latex powder as modifier, and an appropriate amount of additives. It has a certain degree of extensibility, waterproofness, and strong bonding ability with the base surface. It is widely used in exterior walls, roofs, basements and toilets, etc. where waterproofing is required. When tiny cracks occur in the base mortar or concrete, the waterproof coating film applied on it should have a certain ability to fill the cracks, so as to resist the failure of the waterproof function caused by the spread of cracks. However, in the preparation process of the existing mortar base material, there are high production costs, complicated preparation proce...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/02C04B111/20
CPCC04B28/02C04B2111/2092C04B14/06C04B2103/65C04B2103/50C04B24/383C04B14/26C04B24/26C04B2103/67
Inventor 陈耀恒
Owner 广州六润建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com