A kind of high hardness thermosetting self-healing polyurethane and preparation method thereof

A thermosetting, self-healing technology, applied in the field of self-healing polyurethane materials, to achieve high chemical and physical cross-linking, high repair efficiency, and high self-healing efficiency

Active Publication Date: 2021-08-31
JIANGXI SCI & TECH NORMAL UNIV
View PDF9 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Self-healing thermosetting polyurethane is expected to solve this problem, however, how to prepare a kind of thermosetting polyurethane with exact self-healing ability, there is no prior art that can be used for reference; moreover, how to ensure the hardness, toughness, transparency of self-healing thermosetting polyurethane It has good performance in terms of repair efficiency and repair efficiency, and it has also become a technical problem to be solved urgently.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of high hardness thermosetting self-healing polyurethane and preparation method thereof
  • A kind of high hardness thermosetting self-healing polyurethane and preparation method thereof
  • A kind of high hardness thermosetting self-healing polyurethane and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] Take 4.4g of polyvinyl alcohol with a molecular weight of about 1750g / mol and place it in a reaction kettle, dissolve it in 20g of dimethyl sulfoxide at 90°C, add 11.4g of ε-caprolactone and 0.1 g zinc chloride, the reaction system was under the protection of nitrogen, stirred at 25°C for 4h, so that the solution was fully mixed, heated to 140°C for 5h, and a colorless transparent liquid was obtained, and then the obtained liquid was added to the separatory funnel, and the extraction agent 2 was added. Chloromethane, the obtained product is a white polymer. The obtained product is washed with methanol and dried in a vacuum oven at 25°C for 24 hours to obtain a polyvinyl alcohol-grafted polycaprolactone crosslinking agent.

[0048] See attached figure 2 , which is the infrared spectrum of the polyvinyl alcohol grafted polycaprolactone crosslinking agent prepared in Example 1 of the present invention. It can be seen from the figure that the characteristic peak of -C-O-C...

Embodiment 2

[0050] (1) Take 20g of polytetrahydrofuran with a molecular weight of about 1000 in the reaction kettle, pass nitrogen into the reaction kettle for 10 minutes, place the reaction kettle at 120°C for 2 hours in vacuum, completely remove the moisture in the reaction kettle, and put it under the protection of nitrogen , add 10.49g dicyclohexylmethane 4,4'-diisocyanate, 40g solvent N,N-dimethylformamide, 0.04g catalyst dibutyltin dilaurate into the reaction system, react the reaction system at 70°C for 1h, An isocyanate-terminated prepolymer is obtained.

[0051] (2) Add 8.48g of chain extender 2,2'-dithiodiethanol and 15.74g of dicyclohexyl 4,4'-diisocyanate into the reaction system, and react at 70°C for 1.5h under the protection of nitrogen to obtain isocyanate-blocked terminal linear polymer.

[0052] (3) Dissolve 4.74g of polyvinyl alcohol-grafted polycaprolactone in 30g of N,N-dimethylformamide, add the resulting solution into the system, and mix and react at 60°C for 20min...

Embodiment 3

[0061] (1) Take 30g of polytetrahydrofuran with a molecular weight of about 1000 in the reactor, pass nitrogen into the reactor for 10 minutes, place the reactor at 120°C for 2 hours in vacuum, completely remove the moisture in the reactor, and put it under the protection of nitrogen , add 15.74g dicyclohexyl methane 4,4'-diisocyanate, 40g solvent N,N-dimethylformamide, 0.04g catalyst dibutyltin dilaurate to the reaction system, react the reaction system at 70°C for 1h, An isocyanate-terminated prepolymer is obtained.

[0062] (2) Add 8.48g of chain extender 2,2'-dithiodiethanol and 10.49g of dicyclohexyl methane 4,4'-diisocyanate into the reaction system, and react at 70°C for 1.5h under the protection of nitrogen to obtain isocyanate-blocked terminal linear polymer.

[0063] (3) Dissolve 1.58g of polyvinyl alcohol-grafted polycaprolactone in 30g of N,N-dimethylformamide, add the resulting solution into the system, and mix and react at 60°C for 20min under the protection of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
elongation at breakaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to view more

Abstract

The invention provides a high-hardness thermosetting self-repairing polyurethane and a preparation method thereof. The technical scheme uses isocyanate-terminated polyurethane containing 2-hydroxyethyl disulfide as a functional group to cross-link and cure polyvinyl alcohol-grafted polycaprolactone to synthesize a thermosetting self-healing material with high self-healing efficiency and high hardness and transparency. Repair polyurethane. The invention realizes the self-healing of the material based on the disulfide bond exchange reaction, and provides a cross-linked network by grafting polycaprolactone with polyvinyl alcohol as a cross-linking agent, and the obtained material has excellent mechanical properties, high Young's modulus, and at the same time The material has good transparency, high self-healing efficiency, shape memory, reprocessing and other properties. In addition, the present invention also discloses a synthesis method of polyvinyl alcohol-grafted polycaprolactone. The polyvinyl alcohol-grafted polycaprolactone prepared by the method has multiple hydroxyl sites, which increases the interaction of hydrogen bonds between molecular chains. role, can provide a higher degree of chemical and physical cross-linking.

Description

technical field [0001] The invention relates to the technical field of self-repairing polyurethane materials, in particular to a high-hardness thermosetting self-repairing polyurethane and a preparation method thereof. Background technique [0002] Self-healing materials are a new class of materials that can achieve self-healing at the molecular level when the material is damaged, and have been extensively studied in recent years. Self-healing materials can prolong the service life of materials, thereby improving the durability of materials. [0003] Self-healing materials can be divided into two types according to their healing mechanism: exogenous self-healing and intrinsic self-healing. The external aid self-healing system relies on cross-linking agents, initiators and functional molecules wrapped in microcapsules, microspheres, microvessels and other structures as therapeutic agents. When the material is damaged, these microstructures release the internal therapeutic age...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08G18/66C08G18/48C08G18/42C08G18/32C08G63/08C08G63/78
CPCC08G18/3855C08G18/4277C08G18/4854C08G18/66C08G63/08C08G63/78C08G2280/00
Inventor 钟江柳茂陈荣金闯申亮
Owner JIANGXI SCI & TECH NORMAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap