Environment-friendly artificial leather and preparation method thereof

An artificial leather and environmentally friendly technology, applied in the field of synthetic leather, can solve the problems of affecting performance stability and service life, poor processing fluidity, and many fillers, etc., and achieve great promotion and application value, high preparation efficiency and yield rate, and softness Good results

Inactive Publication Date: 2020-05-22
路雪芹
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are many fillers, the processing fluidity is not good, and extravasation is prone to occur during long-term use, which affects performance stability and service life.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] An environment-friendly artificial leather is characterized in that it comprises a base cloth layer and a surface layer, the base cloth layer and the surface layer are connected by an adhesive layer, and the raw materials of the surface layer include the following components by weight: polychloride 100 parts of vinyl resin, 15 parts of pyrido[1,5-A]-1,3,5-triazine-2,4(1H,3H)-dione / isocyanate sulfone polycondensate, amino-terminated hyperbranched polymer 10 parts of amide, 10 parts of epoxy glycerol tricarboxylate, 3 parts of silicon boride, 8 parts of pearl powder, 1 part of silane coupling agent KH5501, 2 parts of AC foaming agent; the particle diameter of described pearl powder is 300 orders, The particle size of the silicon boride is 200 mesh; the amino-terminated hyperbranched polyamide is the amino-terminated hyperbranched polyamide HyperN101.

[0034] The preparation method of the pyrido[1,5-A]-1,3,5-triazine-2,4(1H,3H)-dione / isocyanate sulfone polycondensate comp...

Embodiment 2

[0041] An environment-friendly artificial leather is characterized in that it comprises a base cloth layer and a surface layer, the base cloth layer and the surface layer are connected by an adhesive layer, and the raw materials of the surface layer include the following components by weight: polychloride 100 parts of vinyl resin, 17 parts of pyrido[1,5-A]-1,3,5-triazine-2,4(1H,3H)-dione / isocyanate sulfone polycondensate, amino-terminated hyperbranched polymer 11 parts of amide, 12 parts of epoxy furfuryl oleate, 3.5 parts of silicon boride, 9 parts of pearl powder, 1.5 parts of silane coupling agent KH560, 2.5 parts of phosphate-based betaine; the particle size of the pearl powder is 350 mesh , the particle size of the silicon boride is 250 mesh; the amino-terminated hyperbranched polyamide is the amino-terminated hyperbranched polyamide HyperN102.

[0042] The preparation method of the pyrido[1,5-A]-1,3,5-triazine-2,4(1H,3H)-dione / isocyanate sulfone polycondensate comprises ...

Embodiment 3

[0049] An environment-friendly artificial leather is characterized in that it comprises a base cloth layer and a surface layer, the base cloth layer and the surface layer are connected by an adhesive layer, and the raw materials of the surface layer include the following components by weight: polychloride 100 parts of vinyl resin, 20 parts of pyrido[1,5-A]-1,3,5-triazine-2,4(1H,3H)-dione / isocyanate sulfone condensation polymer, amino-terminated hyperbranched polymer 13 parts of amide, 15 parts of epoxy soybean oleate, 4 parts of silicon boride, 10 parts of pearl powder, 2 parts of silane coupling agent KH5702, 3.5 parts of sodium silicate; the particle diameter of the pearl powder is 400 mesh, and the The particle size of the silicon boride is 300 mesh; the amino-terminated hyperbranched polyamide is the amino-terminated hyperbranched polyamide HyperN103.

[0050] The preparation method of the pyrido[1,5-A]-1,3,5-triazine-2,4(1H,3H)-dione / isocyanate sulfone polycondensate comp...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention discloses environment-friendly artificial leather characterized in that the artificial leather comprises a base cloth layer and a surface layer which are connected through a bonding layer; raw materials of the surface layer comprise, by weight, 100 parts of polyvinyl chloride resin, 15 to 25 parts of a pyrido[1,5-A]-1,3,5-triazine-2,4(1H,3H)-diketone / sulfuryl isocyanate polycondensate, 10 to 15 parts of amino-terminated hyperbranched polyamide, 10 to 20 parts of an environment-friendly plasticizer, 3 to 5 parts of silicon boride, 8 to 12 parts of pearl powder, 1 to 3 parts of a coupling agent and 2 to 5 parts of a foaming agent. The invention also discloses a preparation method of the environment-friendly artificial leather. The environment-friendly artificial leather disclosed by the invention is good in comprehensive performance, good in wear resistance, cold resistance, impact resistance, fine and smooth texture, stereoscopic impression and softness, excellent in performance stability, long in service life and high in economic value, social value and ecological value.

Description

technical field [0001] The invention relates to the technical field of synthetic leather, in particular to an environment-friendly artificial leather and a preparation method thereof. Background technique [0002] In recent years, with the development of the economy and the improvement of living standards, people's requirements for decorative materials are getting higher and higher, and the demand for leather products is increasing. Leather is not only a tool that can be used to shelter from the cold, but also a A means for people to advertise their achievements, it is a symbol of fashion nobility. Leather includes natural leather and artificial leather according to its source. Natural leather mainly comes from animal fur, which is limited in quantity and expensive. Artificial leather is artificially synthesized leather, which simulates the tissue structure and performance of natural leather, and can be used as a suitable material for leather substitutes. It is generally a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B27/12B32B27/30B32B27/20B32B27/22B32B7/12B32B33/00C08J9/10C08J9/14C08J9/12C08J9/30C08L27/06C08L79/04C08L77/00C08K13/02C08K5/1515C08K3/38C08K3/00
CPCB32B5/02B32B5/022B32B7/12B32B27/12B32B27/20B32B27/22B32B27/304B32B2307/3065B32B2307/554B32B2307/558C08J9/0023C08J9/0033C08J9/0061C08J9/0066C08J9/0095C08J9/103C08J9/12C08J9/142C08J9/30C08J2203/04C08J2327/06C08J2477/00C08J2479/04
Inventor 路雪芹
Owner 路雪芹
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com