Root-puncture-resistant self-healing waterproof coiled material and preparation method thereof

A root puncture-resistant and waterproof membrane technology, which is applied in building insulation materials, roof insulation materials, roofs using flexible materials, etc., can solve the problem of wind resistance, weak self-healing performance, root resistance and shortened service life , anti-root life and short service life and other problems, to achieve excellent root anti-year, strong anti-ultraviolet ability, and good anti-immersion performance

Inactive Publication Date: 2020-07-03
WEIFANG HUAGUANG WATERPROOF MATERIALS
View PDF9 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] At present, the root puncture-resistant waterproof membrane still has the following defects in the preparation: the root puncture-resistant self-healing waterproof membrane, (1) the root-resistant period and service life are short, and the root-resistant period and service life are shortened after thermal aging; ( 2) Poor anti-immersion performance, low tensile strength, easy to age; (3) Weak wind resistance and self-healing performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Root-puncture-resistant self-healing waterproof coiled material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Embodiment 1 A kind of root puncture-resistant self-healing waterproof membrane

[0031] A root puncture-resistant self-healing waterproof coiled material of the present invention comprises a copper foil base, a root-blocking waterproof base, a thermal insulation adhesive layer and a mineral particle layer, and the root-blocking waterproof base is arranged above and below the copper foil base On both sides, the thermal insulation adhesive layer and the mineral particle layer are respectively arranged on the upper side of the root-blocking waterproof base. That is, a root-resistant self-healing waterproof membrane of the present invention consists of a mineral particle layer, a root-blocking waterproof base layer, a copper foil base, a root-blocking waterproof base layer, and a thermal insulation adhesive layer from top to bottom.

[0032] The raw materials required for the root-blocking waterproof base include: 10# asphalt, 60# asphalt, composite root-blocking agent, SB...

Embodiment 2

[0045] Embodiment 2 A kind of root puncture-resistant self-healing waterproof membrane

[0046] A root puncture-resistant self-healing waterproof coiled material of the present invention, the raw materials required for the root-blocking waterproof base, by weight, include: 50 parts of 10# asphalt, 40 parts of 60# asphalt, 5 parts of composite root-blocking agent, 30 parts of SBS, 3 parts of PVA, 6 parts of KH-560 coupling agent, 10 parts of filler, 3 parts of active agent, 3 parts of light stabilizer, 8 parts of coconut oil fatty acid, 4 parts of sodium perfluorooctanoate aqueous solution, dicumyl peroxide 20 copies;

[0047] All the other are with embodiment 1.

Embodiment 3

[0048] Embodiment 3 A kind of root puncture-resistant self-healing waterproof membrane

[0049] A root puncture-resistant self-healing waterproof coiled material of the present invention, the raw materials required for the root-blocking waterproof base, by weight, include: 50 parts of 10# asphalt, 50 parts of 60# asphalt, 6 parts of composite root-blocking agent, 30 parts of SBS, 3 parts of PVA, 7 parts of KH-560 coupling agent, 10 parts of filler, 3 parts of active agent, 4 parts of light stabilizer, 7 parts of coconut oil fatty acid, 5 parts of sodium perfluorooctanoate aqueous solution, dicumyl peroxide 20 copies;

[0050] All the other are with embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
boiling pointaaaaaaaaaa
flash pointaaaaaaaaaa
Login to View More

Abstract

The invention provides a root-puncture-resistant self-healing waterproof coiled material. The root-puncture-resistant self-healing waterproof coiled material is prepared from No.10 asphalt, No.60 asphalt, a composite root retarder, SBS, PVA, a KH-560 coupling agent, a filler, an active agent, a light stabilizer, coconut oil fatty acid, a sodium perfluoro-octanoate water solution and dicumyl peroxide. The preparation method comprises the steps of premixing, high-speed shearing and mixing, the high-speed shearing speed is 8-10 Kr / min, the environment humidity is kept at 60.5 + / - 0.5%; in the mixing process, the jacking pressure is 0.75-0.8 MPa, and the rotating speed is 65-70 rmp / min. The root-puncture-resistant self-healing waterproof coiled material has excellent root puncture resistance and a long service life, after thermal aging, the root puncture resistant is enhanced and the service life is prolonged; the coiled material also has a large excellent tensile force and good wind uplift resistance, the maximal peak tensile force is 1017-1105 N / 50 mm, the wind uplift resistance reaches 12.5-14.8 KPa, and the application range is wide.

Description

technical field [0001] The invention belongs to the technical field of root puncture-resistant waterproof materials, and relates to a root puncture-resistant waterproof coiled material, in particular to a root puncture-resistant self-healing waterproof coiled material and a preparation method thereof. Background technique [0002] Root puncture-resistant waterproof membrane, with long-term plant root (or rhizome) puncture resistance, strong adhesion, good stability, low temperature flexibility and heat resistance, strong chemical corrosion resistance and radiation resistance, more than 20 years To still show good root resistance waterproof performance. [0003] The Chinese patent with the application number CN201710153758.2 proposes a kind of asphalt rubber roll material resistant to plant root puncture, which includes 0.5mm vinyl acetate emulsion coating film, 0.5mm thick spunlace polyamide fiber non-woven fabric, 2mm Thick SBR asphalt rubber membrane, 0.5 thick epoxy resi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L95/00C08L53/02C08L29/04C08L33/02C08K13/02C08K5/09C08K5/098C08K5/14C08K5/5435C08K3/04C08K3/16C08K5/42C08K3/38C08K5/101E04D5/10E04D13/16C09J7/29C09J7/30C09J123/16C09J175/04C09J11/04C09J11/06
CPCC08K2003/162C08K2003/166C08K2003/387C08K2201/003C08L95/00C08L2201/08C08L2205/025C08L2205/035C08L2207/04C09J11/04C09J11/06C09J123/16C09J2423/10C09J2475/00C09J2495/006C09J7/29C09J7/30E04D5/10E04D13/16C08L53/02C08L29/04C08L33/02C08K13/02C08K5/09C08K5/098C08K5/14C08K5/5435C08K3/042C08K3/16C08K5/42C08K3/38C08K5/101C08L75/04C08K5/3435
Inventor 刘建华杨建修
Owner WEIFANG HUAGUANG WATERPROOF MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com