Water-containing undisturbed shield muck baking-free building material and preparation method thereof

A technology for building materials and shield slag, which is applied in chemical instruments and methods, cement production, sustainable waste treatment, etc. contact full effect

Active Publication Date: 2020-07-10
CHINA CONSTR FIFTH ENG DIV CORP LTD
View PDF8 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] When the dregs are dehydrated and reused, after the dry dregs are added with liquid, due to the clay in the dregs, there will be agglomeration phenomenon, which is not conducive to stirring, so it is difficult to achieve a uniform state
In addition, the cost of the separate dehydration process is high, and the screening after dehydration is also very difficult
[0006] Since the original slag contains water and has many coarse particles, it is conceivable that the strength of the product is difficult to meet the strength requirements of basic building materials; secondly, it is difficult to mix the hydrated original slag with the active waste slag reach a state of uniformity

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-containing undisturbed shield muck baking-free building material and preparation method thereof
  • Water-containing undisturbed shield muck baking-free building material and preparation method thereof
  • Water-containing undisturbed shield muck baking-free building material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0088] The water-containing undisturbed shield slag unburned brick in this embodiment is prepared through the following steps:

[0089] Weigh 70 parts of water-containing original shield slag (by dry weight), 30 parts of blast furnace slag, 4 parts of sodium hydroxide solid, 7.5 parts of solid sodium silicate powder, and 15.4 parts of water; The type is moderately weathered conglomerate shield slag with a moisture content of 23%, which is taken from a certain section of Changsha Metro Line 3; the particle size of the blast furnace slag is above 200 mesh; The purity is 99%; the modulus of sodium silicate powder is 2.85, and the fineness is 100 mesh.

[0090] Mix 30 parts of blast furnace slag and 7.5 parts of solid sodium silicate powder in a mixer; take 70 parts of undisturbed weathered conglomerate shield slag, add 15.4 parts of water, and add blast furnace slag and solid sodium silicate powder that are well stirred The mixture is crushed and mixed with a rotary wheel mill, ...

Embodiment 2

[0093] The water-containing undisturbed shield slag unburned brick in this embodiment is prepared through the following steps:

[0094] Weigh 70 parts of water-containing original shield slag (by dry weight), 30 parts of blast furnace slag, 4.0 parts of sodium hydroxide solid, 6.0 parts of solid sodium silicate powder, and 14.5 parts of water; The type is strongly weathered slate shield slag with a moisture content of 36%, which is taken from a certain section of Changsha Metro Line 6; the particle size of the blast furnace slag is above 200 mesh; The purity is 99%; the modulus of sodium silicate powder is 2.85, and the fineness is 100 mesh.

[0095] Mix 30 parts of blast furnace slag and 6.0 parts of solid sodium silicate powder in a mixer; take 70 parts of undisturbed strongly weathered slate shield slag, add 14.5 parts of water, and add the well-stirred blast furnace slag and solid sodium silicate powder The mixture is crushed and mixed with a rotary wheel mill, and the co...

Embodiment 3

[0098] The water-containing undisturbed shield slag non-burning test piece in this embodiment is obtained through the following steps:

[0099] The water-containing undisturbed shield muck is taken from the moderately weathered conglomerate muck on the left line of a certain section of Changsha Metro Line 3, and its moisture content is 23%. Weigh 70 parts of water-containing original shield slag (by dry weight), 30 parts of fly ash, 4.09 parts of sodium hydroxide solid, 7.54 parts of solid sodium silicate powder, and 31.5 parts of water; the particle size of fly ash is 200 above mesh; sodium hydroxide is analytically pure in the form of industrial-grade solid flakes, with a purity of 99%; the modulus of sodium silicate powder is 2.85, and the fineness is 100 mesh.

[0100] Mix 30 parts of fly ash and 7.54 parts of solid sodium silicate powder in a mixer; take 70 parts of undisturbed weathered conglomerate shield muck, add 31.5 parts of water, and add the well-stirred fly ash a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
densityaaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to a water-containing undisturbed shield muck baking-free building material and a preparation method thereof. The baking-free building material is prepared from the following rawmaterials in parts by weight: 1-80 parts of water-containing undisturbed shield muck, 1-30 parts of active waste residues, 0.1-5 parts of sodium hydroxide, 0.1-10 parts of sodium silicate and 1-20 parts of water. The method comprises the following steps: weighing the active waste residues, the sodium silicate, the water-containing undisturbed shield muck and the water, mixing, and crushing untilthe content of particles of 4.75 mm or above in the water-containing undisturbed shield muck does not exceed 10% to obtain a mixture I; adding the sodium hydroxide into the mixture I to obtain a mixture II; and pouring the mixture II into a mold to obtain the water-containing undisturbed shield muck baking-free building material. According to the method, intermediate dehydration and screening processes and links are omitted, and the production cost is greatly reduced. The invention also discloses the water-containing undisturbed shield muck unfired building material prepared by the method.

Description

technical field [0001] The invention relates to the technical field of building materials and solid waste treatment, in particular to a fire-free construction material containing water-containing original shield-tunnel dregs and a preparation method thereof. Background technique [0002] Since the water-containing undisturbed shield dregs produced during shield excavation have high mud content and high water content, if not treated in time, it will cause potential danger. First of all, the existing waste disposal sites in cities are seriously insufficient, and many cities are facing the status quo of no land to pile up; secondly, there is no grass growing near the waste disposal sites, which has seriously affected or even destroyed the surrounding ecological environment; finally, with the accumulation of muck The number is gradually increasing, and its risk is also higher. Once an accident occurs, the consequences will be disastrous. [0003] Due to the high water content o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/08C04B28/02C04B40/00C04B18/16C04B111/20C04B111/27
CPCC04B28/08C04B28/021C04B40/0028C04B2111/27C04B2111/29C04B18/16C04B22/062C04B12/04Y02W30/91C04B2111/00767C04B28/006C04B28/26B09B3/21Y02P40/10C04B18/0418C04B18/08C04B18/142C04B40/0263C04B14/361C04B18/141
Inventor 习智琴李水生傅炎朝
Owner CHINA CONSTR FIFTH ENG DIV CORP LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap