A kind of round steel grain boundary oxidation detection method

A grain boundary oxidation and detection method technology, which is applied in the direction of measuring devices, test crystals, and material analysis by measuring secondary emissions, can solve problems such as large deviations in detection results, reduce grain boundary oxidation misjudgments, reduce Detect the effects of fluctuations and deviations

Active Publication Date: 2022-01-11
SGIS SONGSHAN CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The results of grain boundary oxidation are only checked for "yes" or "no" according to the observation situation, without detailed description and depth measurement. Different inspectors have very different understandings of grain boundary oxidation due to limited experience, and the test results are usually different. There is a large deviation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of round steel grain boundary oxidation detection method
  • A kind of round steel grain boundary oxidation detection method
  • A kind of round steel grain boundary oxidation detection method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] Take the grain boundary oxidation detection of spheroidized material 10B21 and diameter φ5.5mm disc wire rod as an example.

[0048] 1. Sampling

[0049] The diameter of the disc is φ5.5mm, and the transverse full-section sample is directly intercepted;

[0050] 2. Sample preparation

[0051] The sample is thermally mounted with edge-preserving mounting material, and the sample is roughly ground, finely ground, finely ground, polished, cleaned, etc. by an automatic grinding and polishing machine to prepare a polished surface with high surface finish and rounded edge of the sample. State samples, no need to etch;

[0052] 3. Sample observation

[0053] Use a metallographic microscope to observe the prepared sample, gradually zoom in from low magnification to high magnification, and observe in detail along the arc of the sample surface. From the surface of the round steel, continuous or intermittent black, yellow, blue, Grain boundary coarsening such as gray is grain ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a round steel grain boundary oxidation detection method, including: S1: sampling, the sample detection surface is a cross-sectional sample perpendicular to the longitudinal axis of the round steel, and samples with different diameters are sampled respectively; S2: sample preparation , prepare the sample into a metallographic sample with high surface finish and rounded edges; S3: observe the grain boundary oxidation, and the continuous or discontinuous grain boundary coarsening structure of different colors along the grain boundary is the grain boundary oxidation; S4: For grain boundary oxidation measurement, select the deepest uniform grain boundary oxidation area to measure randomly five times, and take the average value as the grain boundary oxidation depth; S5: Data processing, determine the final result of grain boundary oxidation according to the sampling rules and positions. It can meet the deep processing and use requirements of Youte round steel.

Description

technical field [0001] The invention relates to the technical field of a material detection method, more specifically, it relates to a method for detecting oxidation of round steel grain boundaries. Background technique [0002] When steel materials are rolled, heated or heat treated, if the heating temperature is too high and the time is too long, oxidation will occur at the grain boundaries on the surface of the material. Grain boundary oxidation is an oxidation process that occurs preferentially along the grain boundaries of metals or alloys. The reason for oxidation is that foreign oxygen atoms diffuse faster along the grain boundaries than inside the grains, thereby forming metal oxides along the grain boundaries. After grain boundary oxidation of metal materials, the surface strength, ductility and closure are greatly reduced, and the toughness of the metal drops sharply. Grain boundary oxidation is irreversible. Materials with severe grain boundary oxidation can only ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G01N21/84G01N23/22G01N23/2251
CPCG01N21/84G01N23/22G01N2021/8477
Inventor 肖命冬曾赞喜林晏民罗新中李富强朱祥睿张兆洋章玉成麻国晓陆伟成杨明梅
Owner SGIS SONGSHAN CO LTD
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com