A kind of self-brazing aluminum alloy foil and its manufacturing method

A technology of aluminum alloy foil and manufacturing method, which is applied in the direction of manufacturing tools, metal rolling, furnaces, etc., can solve problems such as poor performance, high production cost, instability, etc., and achieve the goals of simplifying the production process, prolonging the life, and improving production efficiency Effect

Active Publication Date: 2022-04-12
JIANGSU ALCHA ALUMINUM CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, composite brazing aluminum foil is prepared by composite rolling of two or three different aluminum alloy materials, and its performance is often poor and unstable.
In addition, under the requirements of the modern automobile industry to further reduce weight and reduce costs, the top international automotive heat exchange system production companies continue to require that the limit thickness of aluminum sheet, strip and foil be continuously reduced, and the limit thickness of fins be gradually reduced to 0.05mm. Brings great challenges to the rolling of clad aluminum, resulting in higher production costs for the clad brazed aluminum foil process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of self-brazing aluminum alloy foil and its manufacturing method
  • A kind of self-brazing aluminum alloy foil and its manufacturing method
  • A kind of self-brazing aluminum alloy foil and its manufacturing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A self-brazing aluminum alloy foil, the composition and mass percentage of the aluminum foil are: Fe: 0.25%; Si: 2.1%; Mn: 1.25%; Zn: 1.5%; Cu: 0.3%; Ti: 0.01 %; RE: 0.05%; Zr: 0.05%; the rest is Al. The preparation process comprises the following steps:

[0024] (1) Smelting and refining, the raw materials are added to the melting furnace for melting according to the weight percentage of each component, and continuous casting and rolling are carried out on the continuous casting and rolling machine. The casting and rolling temperature is 680°C, and the casting and rolling speed is 0.55m / min. The thickness of the cast-rolled plate is controlled to be 6.8mm. In order to control the quality of the cast-rolled plate and prevent defects such as sticking rolls and large cracks at the edge, the temperature of the front box when the plate is erected: 750°C, the length of the cast-rolled area: 47mm, the cooling water pressure: 0.3MPa, and wipe it with dry refractory cotton bef...

Embodiment 2

[0031] A self-brazing aluminum alloy foil, the composition and mass percentage of the aluminum foil are: Fe: 0.23%; Si: 2.2%; Mn: 1.30%; Zn: 1.4%; Cu: 0.35%; Ti: 0.015 %; RE: 0.03%; Zr: 0.05%; the rest is Al. The preparation process comprises the following steps:

[0032] (1) Smelting and refining, put the raw materials into the melting furnace for melting according to the weight percentage of each component, and carry out continuous casting and rolling on the continuous casting and rolling machine, the casting and rolling temperature is 675°C, and the casting and rolling speed is 0.62m / min. The thickness of the cast-rolled plate is controlled to be 7.2mm. In order to control the quality of the cast-rolled plate and prevent defects such as sticking rolls and large cracks at the edge, the temperature of the front box when the plate is erected: 755°C, the length of the cast-rolled area: 48mm, the cooling water pressure: 0.4MPa, and wipe with dry refractory cotton before the pla...

Embodiment 3

[0039] A self-brazing aluminum alloy foil, the composition and mass percentage of the aluminum foil are: Fe: 0.33%; Si: 2.3%; Mn: 1.45%; Zn: 1.6%; Cu: 0.4%; Ti: 0.02 %; RE: 0.06%; Zr: 0.03%; the rest is Al. The preparation process comprises the following steps:

[0040](1) Smelting and refining, the raw materials are added to the melting furnace for melting according to the weight percentage of each component, and continuous casting and rolling are carried out on the continuous casting and rolling machine. The casting and rolling temperature is 680°C, and the casting and rolling speed is 0.77m / min. The thickness of the cast-rolled plate is controlled to be 6.7mm. In order to control the quality of the cast-rolled plate and prevent defects such as sticking rollers and large cracks at the edge, the temperature of the front box when the plate is erected: 758°C, the length of the cast-rolled area: 49mm, the cooling water pressure: 0.5MPa, and wipe with dry refractory cotton befor...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a self-brazing aluminum alloy foil, which consists of the following components in mass percentage: Fe: 0.2-0.4%, Si: 2.1-2.3%, Mn: 1.25-1.45%, Zn: 1.4-1.6%, Cu: 0.3-0.4%, Ti: 0.01-0.02%, RE: 0.03-0.07%, Zr: 0.03-0.07%, the rest is Al, and the thickness of the self-brazing aluminum alloy foil is 0.05-0.10mm. The invention also discloses a preparation method of the self-brazing aluminum alloy foil. The self-brazing aluminum alloy foil material of the invention is a single-layer foil material and can realize self-brazing, has high tensile strength and yield strength after brazing, and has good sagging resistance.

Description

technical field [0001] The invention relates to an aluminum alloy foil and a manufacturing method thereof, in particular to a self-brazing aluminum alloy foil and a manufacturing method thereof. Background technique [0002] In recent years, with the continuous aggravation of the global energy crisis, the automobile industry has always focused on the development of lightweight materials. As an important part of the car, the radiator is gradually made of aluminum to achieve the dual purpose of reducing the weight of the car and reducing the cost. The fins in radiators are generally made of composite brazed aluminum foil. At present, most of the aluminum alloy composite foils produced in the world are double-sided coated with Al-Si alloy (skin material) on Al-Mn alloy (core material). . During brazing, the aluminum alloy composite foil is heated to about 600°C, and the Al-Si alloy with a lower melting point melts, and flows to the joint gap through capillary movement under t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22C21/02C22C1/02B22D11/00B21B1/22B21B3/00C21D8/02C22F1/043C21D1/26C21D9/46
CPCC22C21/02C22C1/026B22D11/003B21B1/22B21B3/00C21D8/0247C21D8/0221C22F1/043C21D1/26C21D9/46B21B2003/001
Inventor 张全成钱敏科吴永新陈惠新时坚
Owner JIANGSU ALCHA ALUMINUM CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap