Polyethylene resin composition and piping material, pipe and joint containing the same

一种聚乙烯树脂、组合物的技术，应用在管子/管接头/管件、管子、刚性管等方向，能够解决脆性破损、应力集中等问题

Active Publication Date: 2021-02-05
HITACHI-GE NUCLEAR ENERGY LTD
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The pipe material made of polyethylene receives stress from the pressure inside the pipe and the earth pressure from the outside when it is buried. Therefore, it is known that if there is a minute defect in the pipe, the stress will concentrate there and cause brittle damage.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyethylene resin composition and piping material, pipe and joint containing the same
  • Polyethylene resin composition and piping material, pipe and joint containing the same
  • Polyethylene resin composition and piping material, pipe and joint containing the same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0132] This embodiment relates to a polyethylene resin composition having the first feature.

[0133] In this embodiment, high-density polyethylene is used as the base material. This base material contained 0.5 mass parts of titanium oxide with respect to 100 mass parts of polyethylene resins. Here, HDPE is manufactured using a Ziegler catalyst with a density of 0.95 g / cm 3 , The melt flow rate is 0.5g / 10 minutes.

[0134] Furthermore, one or more types of additives (A), (B), (C) and (D) are mixed in the base material. At this time, the mixture was kneaded at a temperature of 150° C. for 10 minutes using a Banbury mixer, and then pelletized to obtain polyethylene resin composition pellets.

Embodiment 2

[0136] This embodiment relates to a polyethylene resin composition having the second feature.

[0137] In this embodiment, high-density polyethylene is used as the base material. This base material contained 0.5 mass parts of titanium oxide with respect to 100 mass parts of polyethylene resins. Here, HDPE is manufactured using a Ziegler catalyst with a density of 0.94 g / cm 3 More than 0.97g / cm 3 range.

[0138] Furthermore, the base material is mixed with an oil containing naphthenes in which the %CN of ring analysis by the n-d-M method is 20% or more and 100% or less among oils produced when refining naphthene-based crude oil. At this time, the mixture was kneaded at a temperature of 180° C. for 10 minutes using a Banbury mixer, and then pelletized to obtain polyethylene resin composition pellets.

[0139] However, in Examples 1 and 2, polyethylene resin composition pellets were supplied to an injection molding machine, and a 1B-type dumbbell-shaped test piece described i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
flash pointaaaaaaaaaa
densityaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention provides a polyethylene resin composition, and a pipe material, a pipe, and a joint containing the same. The polyethylene resin composition prevents brittle fracture cracking and stresscracking which are intrinsic defects of polyethylene. The polyethylene resin composition contains a base material mainly composed of high-density polyethylene and an additive, and the ratio of the additive is 0.1-10 parts by mass per 100 parts by mass of the high-density polyethylene. The additive is an oil obtained by mixing two or more of additives A to D, and contains at least one of an additive C and an additive D.

Description

[0001] This application is a divisional application of the invention application with the application number 201710566393.6 and the invention title "polyethylene resin composition and pipe material, pipe and joint containing it" filed on July 12, 2017. technical field [0002] The present invention relates to polyethylene resin compositions and pipe materials, pipes and joints containing the same. Background technique [0003] Pipes made of polyethylene are used to transport various fluids. Examples thereof include water and sewage pipes, gas pipes, water supply pipes, hot water supply pipes, chemical liquid pipes, and oil pipes. The safety requirements for various pipes are increasing year by year, so pipes made of PE80 are used for gas pipes, and pipes made of PE100 are used for water and sewage pipes. In addition, cross-linked polyethylene with excellent heat resistance is used as the piping material for the hot water supply pipe. Furthermore, polyethylene pipes also us...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)