A preparation method for producing large-diameter quartz tubes by multi-stage continuous fusion integration

An integrated, large-diameter technology, used in glass manufacturing equipment, manufacturing tools, glass furnace equipment, etc., can solve the problems of multiple pickling of quartz powder, impurity detection, etc., to reduce production links, reduce pollution, and improve labor efficiency. Effect

Active Publication Date: 2022-01-28
东海县奥兰石英科技有限公司
View PDF15 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The technical problem to be solved by the present invention is to overcome the defects in the prior art that the treatment of quartz powder requires multiple pickling and impurity detection, and to provide a preparation method for producing large-diameter quartz tubes by multi-stage continuous fusion integration

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0022] A preparation method for producing a large-diameter quartz tube by a multi-stage continuous melting integration method, comprising the following steps:

[0023] S1. The quartz powder is baked at 1500-1700°C in the first layer continuous furnace to achieve the non-melting heat temperature range of the quartz powder, and to eliminate the escape of the quartz powder in the hot state through the reflux of hydrogen gas between the crystal lattices of the quartz powder. Various gas impurities produced and formed; the first layer of continuous melting furnace adopts ordinary continuous melting furnace, and quartz powder is put into high-temperature baking according to the process flow; the quartz powder in the first layer of continuous melting furnace is automatically fed into the second layer of continuous melting furnace. There is no physical connection between the first-tier continuous melting furnace and the second-tier continuous melting furnace; the temperature of this st...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method for producing large-diameter quartz tubes by a multi-stage continuous melting integration method. The four-stage continuous melting device is innovatively used to directly add quartz powder into the continuous melting furnace for production, and the quartz is effectively removed by three-stage high-temperature heating. The various metal impurities and non-metal impurities contained in the powder are used for the purpose of removing impurities after high-temperature gasification, replacing the serious defects of the current application of many processes, less impurity removal, and various processes, reducing the production process and achieving one-time treatment. Impurities, greatly reducing environmental pollution, improving labor efficiency, the best effect of one-time molding production, reaching the domestic leading level.

Description

technical field [0001] The invention relates to a preparation method for producing a large-diameter quartz tube by a multi-stage continuous melting integration technology. Background technique [0002] At present, in the quartz glass industry, the production of quartz tubes with different specifications of Φ3-480mm needs to go through many production links such as pickling of quartz powder, purification, drying, medium and high magnetic iron removal, purity testing, melting in continuous furnace, forming traction, etc. Many processes, high processing costs, low production efficiency and other issues. [0003] The method for processing quartz powder in the prior art usually includes the following steps: First, after the quartz rough is mechanically crushed, the quartz block is soaked in strong acids such as hydrofluoric acid and hydrochloric acid for 96 hours to remove surface impurities of the quartz block ; Next, dry and mechanically crush and sieve to 80-120 mesh; soak 80...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03B20/00C03B5/16C03B5/235
CPCC03B20/00C03B5/16C03B5/235
Inventor 孙启兵
Owner 东海县奥兰石英科技有限公司