A preparation method of high color fastness water-based acrylate resin color paste, resin color paste and its application and use method

A technology of water-based acrylate and resin color paste, which is applied in the direction of textiles and papermaking, can solve the problems of weak coloring power and uneven coloring of water-based acrylic resin color paste, achieve obvious environmental protection effects, improve the coloring power of weak, The tight effect

Active Publication Date: 2022-04-22
WANHUA CHEM GRP CO LTD
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the deficiencies in the prior art, the present invention provides a method for preparing a water-based acrylate resin color paste with high color fastness. The prepared water-based acrylate resin color paste is a polymer with a core-shell structure, and the water-based color paste greatly improves the The coloring power of water-based acrylic resin color paste is not strong, the problem of uneven coloring, the color fastness performance has been significantly improved, and the utilization efficiency of pigments has been greatly improved, and the discharge of dust and waste water has been reduced, which has brought obvious benefits to the upstream and downstream industries. environmental effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A preparation method of high color fastness water-based acrylate resin color paste, resin color paste and its application and use method

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0066] The present invention also provides a method for preparing the above-mentioned water-based acrylate resin color paste, wherein the water-based acrylate resin color paste is a polymer emulsion with a core-shell structure. Processes and equipment for solution polymerization and radical emulsion polymerization are known to those skilled in the art. The preparation method of aqueous acrylate resin color paste of the present invention comprises the following steps:

[0067] 1) Preparation of core polymer:

[0068] 1-1) mixing the core layer acrylate monomers to obtain a core layer monomer mixture;

[0069] 1-2) Under the condition of 75 ~ 85 ℃, the mixture of nuclear layer monomer and initiator is dropped into the reaction bottle containing ethanol solvent at the same time to undergo copolymerization reaction. After the feeding is completed, keep it warm for 20 ~ 60 minutes, and then add the pigment and emulsifier The mixture is kept warm for 20-60 minutes, and then a cert...

Embodiment 1

[0120] The preparation method of aqueous acrylic resin color paste, comprises the following steps:

[0121] 1) Preparation of core polymer:

[0122] 1-1) Mix 47 parts of styrene monomer, 50 parts of n-butyl acrylate monomer, 1 part of acrylic acid monomer and 2 parts of acetoacetoxyethyl methacrylate monomer to obtain a mixture of core layer monomers ;

[0123] 1-2) At 82°C, add 25 parts of ethanol solvent to the bottom of the kettle, add the above-mentioned core layer monomer mixture and 0.3 parts of ammonium persulfate / 5 parts of deionized water dropwise, and at the same time, a copolymerization reaction occurs, and the dropping time is 2h , Keep warm for 0.5h after feeding.

[0124] 1-3) Under the condition of 82°C, add the pigment emulsifier mixed solution, add dropwise for 0.5h, and continue to react for 0.5h. The pigment emulsifier mixed solution is prepared by mixing 5 parts of pigment iron red Red 101, 1 part of emulsifier SDS and 15 parts of deionized water. Conti...

Embodiment 2

[0130] The preparation method of aqueous acrylic resin color paste, comprises the following steps:

[0131] 1) Preparation of core polymer:

[0132] 1-1) uniformly mix 12 parts of styrene monomer, 85 parts of n-butyl acrylate monomer, 1 part of acrylic acid monomer and 2 parts of N-methylolacrylamide monomer to obtain a mixture of core layer monomers;

[0133] 1-2) Under the condition of 82°C, add 30 parts of ethanol solvent to the bottom of the kettle, add the above-mentioned nuclear layer monomer mixture and 0.3 parts of AIBN / 5 parts of deionized water dropwise, and the copolymerization reaction occurs at the same time, the dropping time is 2h, and the feeding Keep warm for 0.5h after completion.

[0134] 1-3) Under the condition of 82°C, add the pigment emulsifier mixed solution, add dropwise for 0.5h, and continue to react for 0.5h. The pigment emulsifier mixed solution is prepared by mixing 2 parts of pigment iron red Red 101, 0.5 part of emulsifier SDS and 12 parts of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of high color fastness water-based acrylate resin color paste, resin color paste and its application and use method. The water-based acrylate resin color paste is a core-shell structure polymer, and the core polymer is acrylate The composition of polymer and pigment, the shell polymer is a water-based acrylate polymer synthesized by emulsion polymerization. In the present invention, by adding pigments during the reaction process, the molecular chains and pigments in the polymer solution synthesized by solution polymerization are more uniformly dispersed and combined more closely, and the pigments are evenly dispersed and wrapped in the latex particles after the polymer self-emulsifies to form latex particles. It reduces the uneven dispersion of pigments and the phase separation caused by aggregation during the film-forming process of the slurry, and greatly improves the color fastness of the water-based acrylic resin colorant.

Description

technical field [0001] The invention belongs to the technical field of adhesives, and in particular relates to a water-based acrylate resin color paste with high color fastness, a preparation method and its use as a coating composition and a coating and using method. Background technique [0002] The color paste is a coating paste that disperses various types of pigments into the textile adhesive, and the pigments are fully mixed evenly, so that the resin has a certain coloring power and hiding power. In the textile industry, the color paste is coated on the base fabric, and after drying to form a film, the pigment is fixed on the surface of the fabric fiber by the adhesive, which not only makes the fabric present a variety of colors, but also gives the fabric fastness, wear resistance, and hand feeling. and other quality improvements. With the development of social economy and people's pursuit of a higher quality of life, the application of color paste is becoming more and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F265/06C08F220/18C08F212/08C08F220/56C08F220/06C08F220/28C08F220/58C08F257/02C08F220/14D06N3/04
CPCC08F265/06C08F257/02D06N3/042D06N2209/0823C08F220/1802C08F212/08C08F220/56C08F220/06C08F220/283C08F220/1804C08F220/58C08F220/14
Inventor 徐明磊纪学顺马吉全王少鹏王海梅
Owner WANHUA CHEM GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com