High-strength environment-friendly antibacterial wallpaper base paper and preparation method thereof
A high-strength, environmentally friendly technology, applied in pulp beating methods, special paper, synthetic cellulose/non-cellulose material pulp/paper, etc., can solve the problem of usability and aesthetics decline, wallpaper water absorption curling and peeling, wallpaper use The scope is limited and other problems, to achieve the effect of significant hydrophobic effect, increase antibacterial ability, and increase hydrophobic effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0031]Example 1
[0032]A high-strength environmentally friendly antibacterial wallpaper material was prepared from the weight of the following weight: 60 copies of wood pulp, 20 modified chemical fibers, a resin, 5 gas adsorbents, 6 wet strength, dispersion 6 parts of the agent, 1 inhibitor, 1 degreaking agent.
[0033]The wood pulp is a coniferous wood pulp: broad-leaved wood pulp = 15:90.
[0034]The modified chemical fibers are polyester fibers, and the fineness is 1-5d, and the length is 3-5 mm.
[0035]The modified chemical fiber is prepared from the following method:
[0036]1) Soak the chemical fiber in a 20% ethanol solution, soak for 1 hour, the amount of ethanol solution is based on all immersion chemical fibers;
[0037]2) Add a quarter of the hydrochloride of the chemical fiber mass to the mixture of step (1). The chemical fiber is mixed with a mixture of 22% of the chemical fiber mass, and the chemical fiber is used after stirring at 30 ° C. Ion water is rinsed, dry and ready.
[0038]The ...
Example Embodiment
[0050]Example 2
[0051]A high-strength environmentally friendly antibacterial wallpaper, is prepared from the weight of the following weights: 70 copies of wood pulp, 30 modified chemical fibers, 15 parts of the resin, 7 gas adsorbents, 8 moisture, and dispersion 8 parts of the agent, 2 bismuth agents, and 3 synergists.
[0052]The wood pulp ratio is a coniferous wood pulp: a broad-leaved wood pulp = 17:95.
[0053]The modified chemical fibers are polyester fibers, and the fineness is 1-5d, and the length is 3-5 mm.
[0054]The modified chemical fiber is prepared from the following method:
[0055]1) Soak the chemical fiber in a 20% ethanol solution, soaked for 3 hours, the ethanol solution is used in all immersion chemical fibers;
[0056]2) Add a quarter of the hydrochloride of the chemical fiber mass to the mixture of step (1). The chemical fiber is mixed with a mixture of 22% of the chemical fiber mass, and the chemical fiber is used after stirring at 30 ° C. Ion water is rinsed, dry and ready.
[...
Example Embodiment
[0068]Example 3
[0069]A high-strength environmentally friendly antibacterial wallpaper material is prepared from the weight of the following materials: 80 wood pulp, 40 modified chemical fibers, 10 resin, 10 gas adsorbents, 10 moisture, and dispersion 10 parts of the agent, 3 of the apronium, 5 serviles.
[0070]The wood pulp is a coniferous wood pulp: broad - leaved wood pulp = 20:100.
[0071]The modified chemical fibers are polyester fibers, and the fineness is 1-5d, and the length is 3-5 mm.
[0072]The modified chemical fiber is prepared from the following method:
[0073]1) Soak the chemical fiber in a 20% ethanol solution, soaked for 3 hours, the ethanol solution is used in all immersion chemical fibers;
[0074]2) Add a quarter of the hydrochloride of the chemical fiber mass to the mixture of step (1). The chemical fiber is mixed with a mixture of 22% of the chemical fiber mass, and the chemical fiber is used after stirring at 30 ° C. Ion water is rinsed, dry and ready.
[0075]The gas adsorbe...
PUM
Property | Measurement | Unit |
---|---|---|
Fineness | aaaaa | aaaaa |
Length | aaaaa | aaaaa |
Fineness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap