A kind of iron nitride nanopowder and preparation method thereof

A nano-powder, iron nitride technology, applied in chemical instruments and methods, nitrogen compounds, nanotechnology and other directions, can solve the problems of complex process and low purity of iron nitride nano-powder, and achieve simple process and improved Product particle agglomeration, less agglomeration effect

Active Publication Date: 2022-05-03
HEBEI LIFU CHEM TECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a nano-iron nitride powder and its preparation method to solve the problems of low phase purity and complicated process of the iron nitride nano-powder prepared in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of iron nitride nanopowder and preparation method thereof
  • A kind of iron nitride nanopowder and preparation method thereof
  • A kind of iron nitride nanopowder and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Weigh 50g of metal Fe powder with a purity of 99.99wt% and a particle size of 50nm in a glove box, and then weigh 10g of a reaction additive NH with a purity of 99.9%. 4 F powder (additive A), after fully mixing for 20 minutes, spread it in a molybdenum crucible. Put the mixed materials into the quartz sintering furnace, vacuumize to 20KPa, feed nitrogen-hydrogen mixed gas with a volume ratio of 1:1, control the flow rate at 1.5L / min, and then raise the temperature to 350°C at a rate of 5°C / min , then turn off N 2 , into NH 3 , H 2 and NH 3 The volume ratio is 1:3, and the temperature is raised to 550°C at a rate of 2°C / min, and kept for 3h, then turn off the NH 3 and H 2 , into N 2 The temperature was lowered to 200°C at a rate of 5°C / min, and then naturally cooled to room temperature to obtain a sintered product, which was pulverized and classified to obtain iron nitride below 100nm, which was characterized as follows: figure 1 and figure 2 shown.

[0024] R...

Embodiment 11-15

[0032] With reference to the preparation method of Example 1, the particle size of the raw iron powder was changed, and other process conditions were the same as in Example 1. The N content and particle morphology of the obtained iron nitride powder were tested, and the obtained results are shown in Table 2. shown.

[0033] Table 2

[0034]

[0035] It can be seen from Table 2 that the particle size of the raw material iron powder directly affects the particle size of the product, and the product particle size can be adjusted by changing the particle size of the raw material as required.

Embodiment 16-29

[0037] With reference to the preparation method of embodiment 1, change sintering temperature, H 2 and NH 3 The volume ratio and other process conditions are the same as in Example 1. The N content and particle morphology of the obtained iron nitride powder were tested, and the results are shown in Table 3.

[0038] table 3

[0039]

[0040]

[0041] It can be seen from Table 3 that by changing the sintering temperature and H 2 and NH 3It can be seen from the volume ratio that as the sintering temperature increases, the nitrogen content first increases and then decreases, and the particles agglomerate and the particle size becomes larger; when the sintering temperature is 550°C and the holding time is 3h, H 2 and NH 3 The volume ratio is 1:3, the particle uniformity is the best, the agglomeration is less, and the dispersion is good.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention provides a nano iron nitride powder and a preparation method thereof, the main phase of the powder is Fe 4 N, and 5.81wt%≥nitrogen content≥4.9wt%, the particle size of the powder is below 100nm. The preparation method of the present invention is specific iron powder by adding additive NH 4 F, and control the reaction atmosphere, control the reaction process to sinter, and finally crush and classify to obtain the product. The iron nitride prepared by the invention has high phase purity, uniform particle size, good dispersibility, simple preparation method, easy operation, low cost, greatly improved phase purity of iron nitride powder, controllable particle size and high output , the batch performance is stable, and it can be industrialized and mass-produced.

Description

technical field [0001] The invention relates to a nitride nanometer material, in particular to an iron nitride nanometer powder and a preparation method thereof. Background technique [0002] Iron nitride has good hardness and corrosion resistance. At the same time, iron nitride is also a good magnetic material, especially nanoscale iron nitride is an ideal raw material for preparing magnetic liquids and magnetic devices. Ferronitride ferrofluid is a new type of functional material developed in the past ten years. Because it has both magnetism and fluidity, it has advantages that general solid magnetic materials do not have. It is widely used in chemical industry, machinery, instrumentation, environmental protection and medical treatment, etc. has been widely applied. In the field of catalysis, iron nitride is an effective catalyst for many reactions (for example, for ammonia synthesis, Fischer-Tropsch synthesis, and electrocatalytic redox reactions), among which magnetic f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C01B21/06B82Y40/00
CPCC01B21/0622B82Y40/00C01P2004/64C01P2004/03C01P2002/72
Inventor 杨志平许明亮郭静刘学千李璇璇赵金鑫蒋丽涛尤泳王大伟
Owner HEBEI LIFU CHEM TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap