Bacteriostatic plastic film and preparation method thereof

A technology of plastic film and bacteriostatic agent, applied in the field of plastic film, can solve problems such as toxicity and less research and development of bacteriostatic properties, and achieve the effects of improving bacteriostatic properties, good composite bacteriostatic properties, and good plasticizing effect.

Inactive Publication Date: 2021-05-14
王凯
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, most of the current plastic films contain toxic plasticizers, and there is little research on antibacterial properties

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A kind of antibacterial plastic film, it is made up of the raw material of following weight part:

[0023] Tributyl citrate 7, low-density polyethylene 110, divinylbenzene 2, octylisothiazolinone 1, 1H,1H,2H,2H-perfluorodecyltriethoxysilane 2, organically modified phosphine Bacteria Lotion 50.

[0024] Described organic modification antibacterial agent emulsion is made up of the raw material of following weight part:

[0025] Chitosan 10, tetrabutyl titanate 40, oil phase solution 70, emulsifier 1, oleic acid diethanolamide 1.

[0026] The preparation method of described oil phase solution is:

[0027] Take 0.8 parts by weight of tert-butyl hydroquinone, add it into 20 parts by weight of rosemary essential oil, stir evenly, add 1 part by weight of calcium stearate, and keep stirring at 40° C. for 10 minutes.

[0028] The preparation method of described organic modification antibacterial agent emulsion, comprises the following steps:

[0029] (1) Take chitosan, add i...

Embodiment 2

[0036] A kind of antibacterial plastic film, it is made up of the raw material of following weight part:

[0037] Tributyl citrate 9, low density polyethylene 140, divinylbenzene 3, octylisothiazolinone 2, 1H,1H,2H,2H-perfluorodecyltriethoxysilane 4, organically modified Bacteria lotion 60.

[0038] Described organic modification antibacterial agent emulsion is made up of the raw material of following weight part:

[0039] Chitosan 15, tetrabutyl titanate 50, oil phase solution 80, emulsifier 2, oleic acid diethanolamide 2.

[0040] The preparation method of described oil phase solution is:

[0041] Take 1 part by weight of tert-butyl hydroquinone, add it into 30 parts by weight of rosemary essential oil, stir evenly, add 1-2 parts by weight of calcium stearate, and keep stirring at 50 DEG C for 20 minutes.

[0042] The preparation method of described organic modification antibacterial agent emulsion, comprises the following steps:

[0043] (1) Take chitosan, add it to dei...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a bacteriostatic plastic film, which is prepared from the following raw materials in parts by weight: 7 to 9 parts of tributyl citrate, 110 to 140 parts of low-density polyethylene, 2 to 3 parts of divinyl benzene, 1 to 2 parts of octyl isothiazolinone, 2 to 4 parts of 1H,1H,2H,2H-perfluorodecyltriethoxysilane and 50 to 60 parts of organic modified bacteriostatic agent emulsion. The organic modified bacteriostatic agent emulsion contains chitosan and titanium sol, has good composite bacteriostatic performance, has good compatibility between low-density polyethylene matrixes, and can effectively improve the bacteriostatic performance of a finished film, and the added titanium sol can further improve the mechanical strength and toughness of the finished product, the tensile strength is improved, and the film is good in environmental protection property and excellent in comprehensive performance.

Description

technical field [0001] The invention belongs to the field of plastic films, in particular to a bacteriostatic plastic film and a preparation method thereof. Background technique [0002] Plastic films are films made of polyvinyl chloride, polyethylene, polypropylene, polystyrene, and other resins that are used for packaging and as laminations. Plastic packaging and plastic packaging products account for an increasing share in the market, especially composite plastic flexible packaging, which has been widely used in food, medicine, chemical and other fields, among which food packaging accounts for the largest proportion, such as beverage packaging , quick-frozen food packaging, cooking food packaging, fast food packaging, etc., these products have brought great convenience to people's lives. [0003] However, most of the current plastic films contain toxic plasticizers, and there is little research on antibacterial properties. Contents of the invention [0004] The object...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/06C08L5/08C08K5/11C08K3/22C08K5/46C08K13/02C08J5/18
CPCC08J5/18C08J2323/06C08J2405/08C08K5/11C08K5/46C08K13/02C08K2003/2241
Inventor 王凯
Owner 王凯
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap