High-strength, high-hardness and weather-resistant porcelain insulator and preparation method thereof

An insulator and high-hardness technology, applied in the field of composite insulators, can solve the problem of insulators being easily damaged

Active Publication Date: 2021-06-08
江西省萍乡市华东出口电瓷有限公司
View PDF8 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, the insulator is also a part that is easily damaged. How to provide a high-strength, high-hardness weather-resistant insulator is a very important issue in engineering applications.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength, high-hardness and weather-resistant porcelain insulator and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A high-strength, high-hardness weather-resistant porcelain insulator. The raw materials for manufacturing the insulator include kaolin, potassium feldspar, silicon dioxide, quartz stone, zirconia and modified vanadium-cerium composite oxide powder. The raw materials are calculated in parts by weight: 10 parts of kaolin, 3 parts of potassium feldspar, 20 parts of silicon dioxide, 6 parts of quartz stone, 9 parts of zirconia, 13 parts of modified vanadium-cerium composite oxide powder; each raw material is Powder through a 100-mesh sieve.

[0023] Wherein, the preparation method of the modified vanadium-cerium composite oxide powder is:

[0024] 1) Prepare oxalic acid aqueous solution, the concentration of oxalic acid in the oxalic acid aqueous solution is 20g / 500mL, and the rest is water; keep the oxalic acid aqueous solution water bath at a constant temperature to 80°C, then add ammonium metavanadate to the oxalic acid aqueous solution to form precursor solution I, The...

Embodiment 2

[0033] A high-strength, high-hardness weather-resistant porcelain insulator. The raw materials for manufacturing the insulator include kaolin, potassium feldspar, silicon dioxide, quartz stone, zirconia and modified vanadium-cerium composite oxide powder. The raw materials are calculated in parts by weight: 12 parts of kaolin, 4 parts of potassium feldspar, 22 parts of silicon dioxide, 8 parts of quartz stone, 10 parts of zirconia, 15 parts of modified vanadium-cerium composite oxide powder; each raw material is Powder through a 100-mesh sieve.

[0034] Wherein, the preparation method of the modified vanadium-cerium composite oxide powder is:

[0035] 1) Configure an aqueous oxalic acid solution, the concentration of oxalic acid in the aqueous oxalic acid solution is 24g / 500mL, and the rest is water; keep the aqueous oxalic acid solution at a constant temperature of 80°C in a water bath, then add ammonium metavanadate to the aqueous oxalic acid solution to form a precursor sol...

Embodiment 3

[0044] A high-strength, high-hardness weather-resistant porcelain insulator. The raw materials for manufacturing the insulator include kaolin, potassium feldspar, silicon dioxide, quartz stone, zirconia and modified vanadium-cerium composite oxide powder. The raw materials are calculated in parts by weight: 14 parts of kaolin, 6 parts of potassium feldspar, 23 parts of silicon dioxide, 10 parts of quartz stone, 11 parts of zirconia, and 18 parts of modified vanadium-cerium composite oxide powder; each raw material is Powder through a 100-mesh sieve.

[0045] Wherein, the preparation method of the modified vanadium-cerium composite oxide powder is:

[0046] 1) Configure an aqueous oxalic acid solution, the concentration of oxalic acid in the aqueous oxalic acid solution is 26g / 500mL, and the rest is water; keep the aqueous oxalic acid solution at a constant temperature in a water bath to 80°C, then add ammonium metavanadate to the aqueous oxalic acid solution to form a precurso...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-strength, high-hardness and weather-resistant porcelain insulator. The insulator is prepared from the following raw materials: kaolin, potassium feldspar, silicon dioxide, quartz stone, zirconium oxide and modified vanadium-cerium composite oxide powder. According to the invention, the raw material formula of the porcelain insulator is improved, and the obtained insulator has high compressive strength and high breakdown voltage value, and is not easy to break down and damage. The insulator is good in weather resistance and suitable for areas with severe temperature changes, and the maintenance cost is greatly reduced.

Description

technical field [0001] The invention relates to the technical field of composite insulators, in particular to a high-strength, high-hardness weather-resistant porcelain insulator and a preparation method thereof. Background technique [0002] Insulators play an important role in high-voltage transmission lines. Firstly, they provide mechanical support for the wires that transmit current; secondly, they function as insulation to prevent grounding currents. Because high-voltage transmission lines have long transmission distances and large spans, a large number of insulators are required, and the normal operation of the entire power system is closely related to the working status of the insulators. During the operation of the insulator, there are not only the horizontal tension of the conductor and the vertical load of the conductor, but also the impact of climate change and the long-term corrosion of various chemical substances. Therefore, the insulator is also a component th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B33/13C04B33/16C04B33/26C04B33/34C04B41/86
CPCC04B33/131C04B33/16C04B33/26C04B33/34C04B41/86C04B41/5022C04B2235/3472C04B2235/3244C04B2235/3239C04B2235/3229C04B2235/449C04B2235/6562C04B2235/6567C04B2235/96
Inventor 谢琦谢锡云李军刘敏徐勇
Owner 江西省萍乡市华东出口电瓷有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com