Ultraviolet-resistant corrosion-resistant thin coating type water-based fireproof coating material and preparation method thereof

A technology of UV-resistant and fire-resistant coatings, applied in fire-resistant coatings, anti-corrosion coatings, epoxy resin coatings, etc., can solve problems such as affecting the adhesion and fire resistance of coatings

Inactive Publication Date: 2021-12-28
烟台华恒节能科技有限公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, for thin-coated fire retardant coatings, adding too much scale-like substance to the bas...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ultraviolet-resistant corrosion-resistant thin coating type water-based fireproof coating material and preparation method thereof
  • Ultraviolet-resistant corrosion-resistant thin coating type water-based fireproof coating material and preparation method thereof
  • Ultraviolet-resistant corrosion-resistant thin coating type water-based fireproof coating material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A thin-coated water-based fireproof coating with UV resistance and corrosion resistance, comprising the following components in parts by weight: 50 parts of deionized water, 30 parts of water-based epoxy resin, 30 parts of chlorinated rubber emulsion, 15 parts of polytetrafluoroethylene emulsion, polytetrafluoroethylene emulsion, 10 parts of acrylic acid, 4 parts of polyethylene, 3 parts of chlorosulfonated polyethylene, 16.5 parts of basalt flakes, 2 parts of ultraviolet absorber UV-327, 1 part of light stabilizer UV-3853, 0.5 parts of ceramic powder, 0.5 parts of nano zirconium phosphate , 0.5 parts of nano-zirconia, 0.5 parts of nano-barium sulfate, 2 parts of polydimethylsiloxane and 2 parts of acrylic leveling agent. Among them, the preparation method of basalt scales is as follows: put basalt ore particles into a high-temperature fluidized furnace, heat to 1300°C after vacuuming, cool the melt to -30°C with low-temperature nitrogen, and then naturally place it to r...

Embodiment 2

[0023] A kind of anti-ultraviolet and corrosion-resistant thin coating water-based fireproof coating, comprising the following components in parts by weight: 60 parts of deionized water, 40 parts of water-based epoxy resin, 20 parts of chlorinated rubber emulsion, 10 parts of polytetrafluoroethylene emulsion, polytetrafluoroethylene 15 parts of acrylic acid, 5 parts of polyethylene, 2 parts of chlorosulfonated polyethylene, 8.5 parts of flake graphite, 10.5 parts of UV-5310 for ultraviolet absorber, 2 parts of nano-zirconia, 1 part of polyether type defoamer and carboxymethyl fiber Vegetable 0.5 parts.

[0024] The preparation method of the ultraviolet-resistant and corrosion-resistant thin-coated water-based fireproof coating of this embodiment is: weigh each component by weight: deionized water, water-based epoxy resin, chlorinated rubber emulsion, polytetrafluoroethylene emulsion, polyacrylic acid , polyethylene and chlorosulfonated polyethylene, add ultraviolet absorber UV...

Embodiment 3

[0026] A kind of anti-ultraviolet and corrosion-resistant thin coating water-based fireproof coating, comprising the following components in parts by weight: 30 parts of deionized water, 25 parts of water-based epoxy resin, 40 parts of chlorinated rubber emulsion, 20 parts of polytetrafluoroethylene emulsion, polytetrafluoroethylene 5 parts of acrylic acid, 3 parts of polyethylene and 4 parts of chlorosulfonated polyethylene, 15.4 parts of basalt flakes, 3 parts of ceramic powder, 0.3 parts of nano zirconium phosphate, 3.3 parts of ultraviolet absorber UV-15777, 11 parts of light stabilizer UV-54111, poly 2 parts dimethyl siloxane and 2 parts carboxymethyl cellulose. Among them, the preparation method of basalt scales is: put basalt ore particles into a high-temperature fluidized furnace, heat to 800°C after vacuuming, cool the melt to -50°C with low-temperature nitrogen, and then naturally place it to room temperature. The cooled basalt ore solids are stripped and sliced ​​by...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
The average particle sizeaaaaaaaaaa
Thicknessaaaaaaaaaa
The average particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses an ultraviolet-resistant corrosion-resistant thin coating type water-based fireproof coating material, which comprises a water film, a flaky substance and an auxiliary agent, wherein the water film is prepared from the following substances in parts by weight: 30 to 60 parts of deionized water, 25 to 40 parts of a waterborne epoxy resin, 20 to 40 parts of chlorinated rubber emulsion, 10 to 20 parts of polytetrafluoroethylene emulsion, 5 to 15 parts of polyacrylic acid, 3 to 5 parts of polyethylene and 2 to 4 parts of chlorosulfonated polyethylene, the scaly substance is selected from one of flake graphite, glass flakes, flake mica or basalt flakes, the auxiliary agent comprises one or more of an ultraviolet light absorber, a light stabilizer, wear-resistant micro powder, a defoaming agent and a leveling agent, the mass percentage of the water film is 82-93%, the mass percentage of the scaly substance is 5-10%, and the mass percentage of the assistant is 2-8%. According to the invention, large-area basalt scales are used as an additive component of a thin-coating type water-based fireproof coating material, so that the salt spray resistance of the coating material can be improved on the premise of ensuring the adhesive force of the coating material, and the coating material has multiple properties.

Description

technical field [0001] The invention relates to the field of coatings, in particular to an ultraviolet-resistant and corrosion-resistant thin-coated water-based fireproof coating and a preparation method thereof. Background technique [0002] The fire retardant coating is applied to the surface of the material to make the material have fire resistance, which can slow down the spread of flame or prevent burning for a certain period of time. Building fire prevention is an important application field of fireproof coatings, mainly fireproof coatings for steel structures. In order to achieve the purpose of fireproofing steel structures, fireproof coatings are mostly thick-coated coatings. Since this type of coating has sufficient thickness (8-45mm), so A certain amount of functional materials can be added to the coating to make the coating have composite functions, such as adding zinc powder or scaly substances to make the coating have the function of anti-corrosion and salt spra...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D163/00C09D115/02C09D127/18C09D133/02C09D123/06C09D123/34C09D5/18C09D5/08C09D7/61
CPCC09D163/00C09D115/02C09D5/18C09D5/08C09D7/61C09D7/70C08K2201/011C08K2003/328C08K2003/2244C08K2003/3045C08L2201/02C08L2201/08C08L15/02C08L27/18C08L33/02C08L23/06C08L23/34C08K7/00C08K3/34C08K3/32C08K3/22C08K3/30C08K3/013C08L63/00
Inventor 任朋成
Owner 烟台华恒节能科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap