Stain-resistant and flame-retardant building outer wall and preparation method thereof

A technology for building exterior walls and anti-fouling, applied in coatings, fire-retardant coatings, etc., can solve the problems of high sulfur dioxide content and dust.

Pending Publication Date: 2021-12-31
刘轩彤
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The problem with the existing exterior walls of buildings is that, for example, whether the anti-fouling performance can be improved without considering the high content of sulfur dioxide and dust in the air

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A pollution-resistant and flame-retardant building exterior wall and a preparation method thereof mainly include the following raw material components in parts by weight: 25 parts of layered copper-aluminum bimetallic hydroxide coating and 75 parts of expanded polystyrene composite board.

[0033] A pollution-resistant and flame-retardant building exterior wall and a preparation method thereof, the preparation method of the pollution-resistant and flame-retardant building exterior wall mainly includes the following preparation steps:

[0034] (1) Mix layered copper-aluminum double metal hydroxide powder and modified styrene-acrylic emulsion in a volume ratio of 1:10 to obtain a layered copper-aluminum double metal hydroxide coating;

[0035] (2) Mix and stir the heat-conducting filler and the flame-retardant glue according to the mass ratio of 1:1 to obtain a composite filler;

[0036](3) Inject the composite filler into the mature polystyrene foam filter beads at a mas...

Embodiment 2

[0043] A stain-resistant and flame-retardant building exterior wall and a preparation method thereof mainly include the following raw material components in parts by weight: 25 parts of magnesium aluminum carbonate type hydrotalcite paint and 75 parts of expanded polystyrene composite board.

[0044] A pollution-resistant and flame-retardant building exterior wall and a preparation method thereof, the pollution-resistant and flame-retardant building exterior wall and its preparation method mainly include the following preparation steps:

[0045] (1) Magnesium aluminum carbonate hydrotalcite and modified styrene-acrylic emulsion are mixed at a volume ratio of 1:10 to obtain magnesium aluminum carbonate hydrotalcite coating;

[0046] (2) Mix and stir the heat-conducting filler and the flame-retardant glue according to the mass ratio of 1:1 to obtain a composite filler;

[0047] (3) Inject the composite filler into the mature polystyrene foam filter beads at a mass ratio of 1:9, ...

Embodiment 3

[0053] A stain-resistant and flame-retardant building exterior wall mainly includes the following raw material components in parts by weight: 25 parts of layered copper-aluminum bimetallic hydroxide paint and 75 parts of expanded polystyrene composite boards.

[0054] A method for preparing a pollution-resistant and flame-retardant building exterior wall, the preparation method of the pollution-resistant and flame-retardant building exterior wall mainly includes the following preparation steps:

[0055] (1) Mix layered copper-aluminum double metal hydroxide powder and modified styrene-acrylic emulsion in a volume ratio of 1:10 to obtain a layered copper-aluminum double metal hydroxide coating;

[0056] (2) Inject the flame retardant glue into the mature polystyrene foam filter beads according to the mass ratio of 1:9, mix evenly, pour it into the mold to control the thickness to 3cm, let it stand at room temperature for 18h to foam, and demould after foam molding Expanded poly...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a stain-resistant and flame-retardant building outer wall and a preparation method thereof, and relates to the technical field of new materials. Layered copper-aluminum bimetal hydroxide is prepared, and smoke-abatement effective components exist in a lamellar structure of the layered copper-aluminum bimetal hydroxide, so that carbon formation on the surface of the material and formation of a heat-insulating protective layer are facilitated; the decomposed product is an alkaline porous substance for adsorbing sulfur dioxide in air; and the expanded polystyrene composite material is composed of expandable polystyrene foam beads and has the advantages of being easy and convenient to construct, good in heat preservation performance, resistant to pollution and easy to recycle, the expanded polystyrene composite material and the expanded polystyrene foam beads are matched after being mixed, the wall has better flame retardant performance, and the better heat conduction performance enables the color of the wall to appear more rapidly and accurately. The stain-resistant and flame-retardant building outer wall prepared by the invention has the effects of flame retardance, stain resistance and color change, can perform air purification and self-cleaning in a high-temperature environment with a large amount of sulfur dioxide harmful gas, and has a warning effect through color change.

Description

technical field [0001] The invention relates to the technical field of new materials, in particular to a pollution-resistant and flame-retardant building exterior wall and a preparation method thereof Background technique [0002] Volcanoes are one of the important manifestations of crustal tectonic movement, and play an extremely important role in all stages of the earth's historical evolution, whether it is an active volcano that is still active, or a volcano that has been active in geological history and is now dead; volcano Geomorphic landscapes are the geomorphic relics left by volcanic activities and volcanic activities. Volcanoes are one of the important manifestations of crustal tectonic movements. They play an extremely important role in all stages of the earth's historical evolution. Whether it is an active volcano , or a volcano that has been active in geological history and is now dead. With the development of modern economy, all parts of the country are competi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08J9/36C09D125/14C09D183/10C09D5/18C09D7/61C08L25/06C08L23/06C08L61/06C08K3/38C08K3/04C08K3/32C08J9/00
CPCC08J9/365C09D125/14C09D5/18C09D7/61C09D7/70C08J9/0066C08J9/0071C08J9/0061C08J2325/06C08J2423/06C08J2461/06C08K2003/385C08K3/041C08K2003/329C08J2425/14C08J2483/10C08K2201/011C08K2003/265C08K2003/0831C08L83/10C08K3/22C08K7/00C08K3/08C08K3/26
Inventor 刘轩彤
Owner 刘轩彤
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products