Anti-electron radiation garment material and preparation method thereof

A technology of electronic radiation and clothing, applied in clothing, clothing, protective clothing, etc., can solve the problems of breeding a large number of bacteria and affecting the health of users

Pending Publication Date: 2022-03-01
王珍丽
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The existing anti-electron radiation clothing fabrics have good anti-electron radiation capabilities, but after a long period of use, a large number of bacteria will grow on the surface of the fabric, which will affect the health of users

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-electron radiation garment material and preparation method thereof
  • Anti-electron radiation garment material and preparation method thereof
  • Anti-electron radiation garment material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] An electronic radiation-proof clothing fabric is prepared by spinning reinforced yarns;

[0040] The reinforcing yarn is made by the following steps:

[0041] Soak the cotton yarn in the dipping solution, and after soaking for 8 hours at a temperature of 35°C, take out the cotton yarn and dry it to obtain the reinforced yarn;

[0042]The dipping solution comprises the following raw materials in parts by weight: 30 parts of modified graphene, 1,000 parts of deionized water, 5 parts of softener, and 20 parts of water-based polyurethane;

[0043] The dipping solution is made by the following steps:

[0044] The modified graphene was dispersed in deionized water, softener was added, and under the condition of a frequency of 3MHz, after ultrasonic treatment for 5 minutes, water-based polyurethane was added, and the ultrasonic treatment was continued for 20 minutes to obtain an impregnating liquid.

[0045] Described modified graphene is made by the following steps:

[004...

Embodiment 2

[0052] An electronic radiation-proof clothing fabric is prepared by spinning reinforced yarns;

[0053] The reinforcing yarn is made by the following steps:

[0054] Soak the cotton yarn in the impregnating solution, and after soaking for 10 hours at a temperature of 35°C, take out the cotton yarn and dry it to obtain the reinforced yarn;

[0055] Described immersion liquid comprises the following raw materials by weight: 35 parts of modified graphene, 1050 parts of deionized water, 6 parts of softener, and 23 parts of water-based polyurethane;

[0056] The dipping solution is made by the following steps:

[0057] The modified graphene was dispersed in deionized water, softener was added, and under the condition of a frequency of 3MHz, after ultrasonic treatment for 10 minutes, water-based polyurethane was added, and the ultrasonic treatment was continued for 20 minutes to obtain an impregnating liquid.

[0058] Described modified graphene is made by the following steps:

...

Embodiment 3

[0065] An electronic radiation-proof clothing fabric is prepared by spinning reinforced yarns;

[0066] The reinforcing yarn is made by the following steps:

[0067] Soak the cotton yarn in the impregnating solution, and after soaking for 8 hours at a temperature of 40 °C, take out the cotton yarn and dry it to obtain the reinforced yarn;

[0068] Described immersion liquid comprises the following raw materials by weight: 40 parts of modified graphene, 1100 parts of deionized water, 8 parts of softener, and 28 parts of water-based polyurethane;

[0069] The dipping solution is made by the following steps:

[0070] The modified graphene was dispersed in deionized water, softener was added, and under the condition of a frequency of 5MHz, after ultrasonic treatment for 5 minutes, water-based polyurethane was added, and the ultrasonic treatment was continued for 30 minutes to obtain an impregnating liquid.

[0071] Described modified graphene is made by the following steps:

[...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an anti-electron-radiation garment fabric and a preparation method thereof, the anti-electron-radiation garment fabric is prepared by spinning reinforced yarns, and an impregnation liquid is prepared from the following raw materials in parts by weight: 30-50 parts of modified graphene, 1000-1200 parts of deionized water, 5-10 parts of a softening agent and 20-30 parts of waterborne polyurethane; graphene in the modified graphene can induce and enhance the peroxidation of lipid, influence the physiological function of bacterial cells, increase the concentration of active oxygen of the cells, oxidize fatty acid, cause the production of lipid peroxide, stimulate free radical reaction and damage bacterial cell membranes, so that bacteria are killed; zinc and silver ions can be combined with protein sulfydryl in bacteria, so that a respiratory system, an electron transport system and a substance transport system of the bacteria are damaged to cause bacterial death, and the intermediate 4 is a macromolecular antibacterial agent and is not easy to separate out from the fabric, so that the antibacterial effect of the fabric is better.

Description

technical field [0001] The invention relates to the technical field of fabric preparation, in particular to an electronic radiation-proof clothing fabric and a preparation method thereof. Background technique [0002] Electromagnetic radiation is an invisible and intangible pollution, known as the "invisible killer". Most household appliances such as TV sets and microwave ovens that people come into contact with in daily life, as well as radar systems, broadcast signal transceiver systems, radio frequency and microwave medical equipment, communication transmitting stations, etc., can produce various forms, different frequencies, and different intensities. of electromagnetic radiation. Studies have found that electromagnetic radiation pollution is the main cause of cardiovascular disease, diabetes, and cancer mutations, and it will also cause direct damage to the human reproductive system, nervous system, and immune system. Excessive electromagnetic radiation can also cause...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06M11/74D06M13/148D06M15/53D06M15/564A41D31/04A41D31/30D06M101/06
CPCD06M11/74D06M15/564D06M13/148D06M15/53D06M16/00A41D31/30A41D31/04D06M2101/06D06M2200/50
Inventor 王珍丽
Owner 王珍丽
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com