Wool product for preventing electric radiation and manufacturing technology thereof

A technology of electronic radiation and production technology, applied in the field of functional wool, can solve the problems of bulky and hard, difficult to wear, etc., and achieve the effect of beautiful appearance, not easy to pilling, and health protection

Pending Publication Date: 2017-10-10
JIAXING ZHULANG CLOTHING CO LTD
View PDF6 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The problem to be solved by the present invention is that the existing anti-electron radiation wool products are too bulky and hard to wear

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0058] S1, configure chloroform / methanol solvent, immerse the wool fiber with a mass ratio of 10% in the solvent, and use a Soxhlet extractor to reflux extract the wool fiber. The extraction time is controlled at 2h. After the extraction is completed, the wool fiber is deionized Wash with water, wash three times, and then put it in an oven to dry at 50 degrees Celsius;

[0059] S2, configure the ionic liquid, heat the ionic liquid to 50°C, immerse the wool fiber in S1 into the ionic liquid, stir and react for 20 minutes, wash with ethanol first after the reaction is completed, and then wash with deionized water, repeat this twice Wash and dry in an oven at 50 degrees Celsius;

[0060] S3, configure the protease treatment solution, heat the protease treatment solution to 40°C, immerse the wool fiber in S2 in the protease treatment solution, stir and react for 30 minutes, after the reaction is completed, raise the temperature to 100°C, keep it for 15 minutes, and then use deioni...

Embodiment 2

[0066] S1, configure chloroform / methanol solvent, immerse the wool fiber with a mass ratio of 15% in the solvent, and use a Soxhlet extractor to reflux extract the wool fiber. The extraction time is controlled at 2h. After the extraction is completed, the wool fiber is deionized Wash with water, wash three times, and then put it in an oven to dry at 50 degrees Celsius;

[0067] S2, configure the ionic liquid, heat the ionic liquid to 50°C, immerse the wool fiber in S1 into the ionic liquid, stir and react for 20 minutes, wash with ethanol first after the reaction is completed, and then wash with deionized water, repeat this twice Wash and dry in an oven at 50 degrees Celsius;

[0068] S3, configure the protease treatment solution, heat the protease treatment solution to 40°C, immerse the wool fiber in S2 in the protease treatment solution, stir and react for 30 minutes, after the reaction is completed, raise the temperature to 100°C, keep it for 15 minutes, and then use deioni...

Embodiment 3

[0074] S1, configure chloroform / methanol solvent, immerse the wool fiber with a mass ratio of 20% in the solvent, and use the Soxhlet extractor to reflux extract the wool fiber. The extraction time is controlled at 2h. After the extraction is completed, the wool fiber is deionized Wash with water, wash three times, and then put it in an oven to dry at 50 degrees Celsius;

[0075] S2, configure the ionic liquid, heat the ionic liquid to 50°C, immerse the wool fiber in S1 into the ionic liquid, stir and react for 20 minutes, wash with ethanol first after the reaction is completed, and then wash with deionized water, repeat this twice Wash and dry in an oven at 50 degrees Celsius;

[0076] S3, configure the protease treatment solution, heat the protease treatment solution to 40°C, immerse the wool fiber in S2 in the protease treatment solution, stir and react for 30 minutes, after the reaction is completed, raise the temperature to 100°C, keep it for 15 minutes, and then use deio...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a wool product for preventing electric radiation. The wool product comprises 10-20% of wool fiber, 30-40% of modified polyester fiber, 25-35% of silver-coated filament and 15-35% of bamboo pulp fiber, wherein the silver-coated filament is coated with the modified polyester fiber to form core spun yarn, the core spun yarn, the wool fiber and the bamboo pulp fiber are blended to form fabric with a function of preventing the electric radiation. Through the coordination of a manufacturing technology, the wool product which has a high electromagnetic shielding effect, comfortable in handfeel, is suitable for being worn can be obtained.

Description

technical field [0001] The invention relates to the field of functional wool, in particular to an electronic radiation-proof wool product and a production process thereof. Background technique [0002] Wool fiber is a deformed product of sheep's skin, which has excellent warmth retention. It is mostly used in autumn and winter clothing. Wool fiber has the advantages of good elasticity, strong hygroscopicity, and good warmth retention. It is one of the earliest natural textile raw materials for ice cups. First, it has excellent textile processing performance. Wool products have the advantages of soft luster, rich and elastic handle, good drapability, heat preservation and moisture resistance, and stain resistance. [0003] In recent years, with the rapid development of science and technology, various electrical appliances and electronic equipment have been greatly popularized, and electromagnetic radiation has become the second pollution source after air pollution, water poll...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D04B1/14D04B1/16D02G3/44D02G3/36D02G3/04D01F6/92D01F1/10D06M16/00D06M101/12
CPCD01F1/103D01F6/92D02G3/04D02G3/36D02G3/441D04B1/14D04B1/16D06M16/003D06M2101/12D10B2331/04D10B2401/13D10B2201/01D10B2211/02
Inventor 张杰
Owner JIAXING ZHULANG CLOTHING CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com