White light transmitting composite film layer and preparation method and application thereof
A composite film layer and white light technology, which is applied in coating, metal material coating process, vacuum evaporation coating, etc., can solve the problem that cannot meet the appearance requirements of high-end light-emitting products, and the coating vacuum coating evaporation parameters cannot meet PVD Indium-plated layer transparent white light and other issues, to achieve the effect of various structures
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
preparation example Construction
[0066] When the medium layer is a transparent coating containing 0.5-8% blue pigment and 0-2% purple pigment, the preparation method of the white light-transmitting composite film layer comprises the following steps:
[0067] Injecting transparent plastic to form a transparent panel 1;
[0068] Coating a transparent primer slurry on one side of the transparent panel 1 to form a transparent primer layer 2;
[0069] Evaporating indium plating on the transparent primer layer 2 by physical vapor deposition (PVD) to form an indium plating layer 3;
[0070] Add blue pigment and purple pigment to the transparent paint (add 0.5-8 parts of blue pigment and 0-2 parts of purple pigment to 100 parts of transparent paint) and mix evenly, and then coat it on the indium-plated layer 3 to form a dielectric layer 4. Obtain a white light-transmitting composite film layer.
[0071] Examples of transparent plastics are polycarbonate, PVC, PET or PP transparent plastics.
[0072] Before PVD eva...
Embodiment 1
[0107] The preparation method of the white light-transmitting composite film layer of this embodiment is specifically as follows:
[0108] Injection-molding transparent polycarbonate plastic to form a transparent panel with a thickness of 5mm;
[0109] Spray transparent primer slurry on one side of the transparent panel, and form a transparent primer layer with a thickness of 20 μm after curing;
[0110] Evaporate indium plating on the transparent primer layer by physical vapor deposition to form a PVD indium plating layer with a thickness of 20nm;
[0111] Add 2 parts of light sky blue pigment (average particle size 300nm) with CMYK value of C40 M0 Y10 K0 and 0.5 part of pure purple pigment (average particle size 300nm) with CMYK value of C55 M85 Y0 K0 in 100 parts of transparent paint and mix After uniformity, it is sprayed on the PVD indium plating layer, and after curing, a 15 μm dielectric layer is formed to obtain a white light-transmitting composite film layer.
Embodiment 2
[0113] The preparation method of the white light-transmitting composite film layer of this embodiment is specifically as follows:
[0114] Injection-molding transparent polycarbonate plastic to form a transparent panel with a thickness of 6mm;
[0115] Evaporate indium plating on the transparent panel by physical vapor deposition to form a PVD indium plating layer with a thickness of 25nm;
[0116] With 3 parts of CMYK value C60 M0 Y10 K0 water blue pigment (average particle diameter is 200nm) and 0.6 part of CMYK value is C45 M70 Y50 K0 caramel purple pigment (average particle diameter is 400nm) with 100 parts of transparent polycarbonate The ester plastic is mixed evenly, extruded and calendered to form a transparent plastic film, and then laminated on the PVD indium-coated layer to form a dielectric layer with a thickness of 18 μm, that is, a white light-transmitting composite film layer is obtained.
PUM
Property | Measurement | Unit |
---|---|---|
particle size | aaaaa | aaaaa |
thickness | aaaaa | aaaaa |
thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction