Preparation method of carbon black dispersion liquid for black polyimide film

A technology of polyimide film and dispersion liquid, which is applied in the field of preparation of carbon black dispersion liquid for black polyimide film, can solve the problem of deterioration of dispersion condition, difficulty and large workload of dispersant selection, and selection range of dispersant. Narrowing etc.

Pending Publication Date: 2022-07-15
山东万达微电子材料有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The problem with this method is that the introduced hyperbranched dispersant has poor high temperature resistance and can only meet the preparation of polyimide films with an imidization temperature below 290°C. For those with a higher imidization temperature (usually 350 The preparation of polyimide film is not applicable; the second is that the selection criteria of the dispersant are not determined according to the different pH values ​​of graphene oxide, which leads to the difficulty and heavy workload of dispersant selection for different graphene oxide
However, there are many difficulties in realizing the st

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of carbon black dispersion liquid for black polyimide film
  • Preparation method of carbon black dispersion liquid for black polyimide film
  • Preparation method of carbon black dispersion liquid for black polyimide film

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0051] Example 1

[0052] Experimental raw materials: N,N-dimethylacetamide (DMAc), pyromellitic dianhydride (PMDA), 4,4'-diaminodiphenyl ether (ODA), carbon black (brand: Orilon FW200; PH value 2.5);

[0053] Experimental equipment: double-layer glass reactor, circulating cooler, electric stirrer, sand mill;

[0054] Add 695g of DMAc to the double-layer glass reactor, add 60g of ODA, start the electric stirrer and stir at 150r / min for 30min, divide 45g of PMDA into two equal parts, slowly add the first part of dianhydride to the reactor, and stir for 15min. Then slowly add the second part of dianhydride into the reactor, stir for 30min, and control the polymerization temperature between 45±2°C during the reaction. After adding 200g of carbon black (brand: Orilong FW200, pH 2.5) and stirring evenly, the slurry was ground with a sand mill at 2800r / min for 10 hours.

[0055] The mass percentage of carbon black in the obtained dispersion was 20%, the molar ratio of PDMA to ODA...

Example Embodiment

[0057] Example 2:

[0058] This example is similar to the technical solution adopted in Example 1, except that the carbon black brand used is LampBLACK 101 (the pH value of the product is 7.5), and the quality of the PDMA used is 58.81 g (R=0.9 at this time). ).

[0059] After testing, the median particle size of carbon black in the prepared carbon black dispersion was 50 nm (D 50 = 50nm) for 90 days: no sedimentation.

Example Embodiment

[0060] Example 3: Preparation of carbon black dispersion for black polyimide film

[0061] This example is similar to the technical solution adopted in Example 1, except that the carbon black brand used is PRINTEX L6 (commodity pH value is 9.5), and the quality of the PDMA used is 64g (R is 0.98 at this time) .

[0062] After testing, the median particle size of carbon black in the prepared carbon black dispersion was 50 nm (D 50 =50nm), placed for 90 days without sedimentation.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Median particle sizeaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Dielectric strengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to a preparation method of a carbon black dispersion liquid for a black polyimide film, which is characterized by comprising the following steps of: dissolving a diamine monomer into a strong-polarity aprotic organic solvent, adding a dianhydride monomer in batches, controlling the molar ratio of the dianhydride monomer to the diamine monomer to be 0.7-0.98, controlling the reaction temperature to be 40-50 DEG C, and reacting for 40-60 minutes to obtain a carbon black dispersing agent of a polyamide acid system; the preparation method comprises the following steps: adding carbon black into a carbon black dispersant of a polyamide acid system, stirring, and grinding for 9-11 hours by using a grinding machine to obtain a carbon black dispersion liquid; the carbon black can realize high-stability dispersion in the aspect of preparing modified polyimide, and stable preparation of the high-performance carbon black-polyimide composite material is realized.

Description

technical field [0001] The present invention relates to a preparation method of carbon black dispersion liquid for black polyimide film. Background technique [0002] Polyimide (PI) is a general term for heterocyclic polymers containing imide groups in the main chain. It is one of the engineering plastics with the best heat resistance. With excellent mechanical strength and non-combustibility, it is widely used in films, coatings, advanced composite materials, fibers, engineering plastics and other fields. Polyimide can be divided into three categories: thermosetting polyimide, thermoplastic polyimide and modified polyimide, and it is developing rapidly. Among them, the composite modification of polyimide by filling to achieve the improvement of function and performance is the current research focus. [0003] The preparation of aromatic polyimide by polycondensation is the current mainstream process, which is prepared by the reaction of aromatic diamines with aromatic dian...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08J3/09C08J5/18C08G73/10C08L79/08C08K3/04
CPCC08J3/096C08J5/18C08G73/1007C08G73/105C08G73/1071C08J2379/08C08K3/04C08K2201/011
Inventor 初明辉王会宾王聪聪朱星驰
Owner 山东万达微电子材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap