Hydrocracking catalyst containing monox-alumina

A silicon oxide-containing, hydrocracking technology, applied in the fields of hydrocarbon oil cracking, petroleum industry, etc., can solve the problem of low selectivity of middle distillates, and achieve the effect of improved hydrocracking activity and good selectivity

Inactive Publication Date: 2006-06-28
CHINA PETROLEUM & CHEM CORP +1
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The purpose of the present invention is to overcome the disadvantages of existing hydrocracking catalyst activity and low selectivity to middle distillates, and provide a hydrocracking catalyst containing silica-alumina with high activity and selectivity to middle distillates. catalyst

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hydrocracking catalyst containing monox-alumina
  • Hydrocracking catalyst containing monox-alumina

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0042] 800 grams of NaY type molecular sieve (SiO 2 / Al 2 o 3 =4.8, crystallinity is defined as 100%, Changling Oil Refinery product) is placed in 4000 milliliters, concentration is in the ammonium chloride (Beijing Chemical Plant product, analytical pure) aqueous solution of 1.0 mole, exchange 1 hour under stirring at 90 ℃, Filter, wash with deionized water until no chlorine ions are detected, dry at 120°C, and bake at 550°C for 4 hours. Repeat above-mentioned process twice to obtain the Y-type molecular sieve A of sodium content (in sodium oxide) 0.35% by weight (measured by flame atomic absorption spectrometry), record sample crystallinity with X-ray diffraction method and be 76%, get Y-type molecular sieve A 200 grams were placed in 1000 ml of ammonium fluoride (product of Beijing Chemical Plant, analytically pure) aqueous solution with a concentration of 0.2 moles, stirred at room temperature for 1 hour, filtered, dried at 120°C, and calcined at 600°C for 4 hours to obt...

example 2

[0044] Take by weighing 12 grams of example 1 disordered Y-type molecular sieve B and 100 grams of SB powder (gibbsite produced by Condea, Germany) and mix to obtain the precursor Si-2 of silicon oxide-alumina (dry basis 74% by weight) , the Si-2 was calcined at 550°C for 4 hours, its X-ray diffraction spectrum is shown in figure 1 b, the silicon oxide content and k value are shown in Table 1

example 3

[0046] According to example 12 in CN1020269C, zeolite containing five-membered ring structure containing rare earth was synthesized to obtain zeolite D containing five-membered ring structure containing rare earth; according to exactly the same conditions, the crystallization temperature was 90°C to obtain partially crystallized zeolite E containing five-membered ring structure containing rare earth. The rare earth-containing five-membered ring structure zeolite E has a silica content of 93.3% by weight, an alumina content of 4.5% by weight, RE 2 o 3 1.5% by weight (RE 2 o 3 Represents rare earth oxides, wherein lanthanum oxide accounts for 26% by weight of the total amount of rare earth oxides, cerium oxide accounts for 51% by weight of the total weight of rare earth oxides, and other rare earth oxides account for 23% by weight of the total weight of rare earth oxides). The degree of crystallinity of the partially crystallized ZSM-5 molecular sieve E was determined to be 6...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention is a kind of hydrocracking catalysts, which contains nonox-alumine, Y type of crystalline silica, iron or cobalt or niccolum from VIII lombardic and molybdenum or tung component from VIB lombardic. The K value of nonox-alumine is0.4,consulting catalyser's pivot, by weight, the content of nonox-alumine is 10%-90% and Y type is 1%-70%. Consulting oxid, by weight, the content of metal component from VIII lombardic is 1%-10% and metal component from VIB is 5%-40%. The catalyser has higher ac of hydrocrack and better selectivity to center cut oil.

Description

technical field [0001] The present invention relates to a hydrocracking catalyst, and more particularly to a silica-alumina-containing hydrocracking catalyst. Background technique [0002] In recent years, the trend of heavy and inferior crude oil has become increasingly obvious worldwide. At the same time, the demand for middle distillates and reforming and steam cracking raw materials has continued to increase, which promotes the use of high-quality and light-quality heavy distillates. The hydrocracking technology for the purpose of hydrocracking has developed rapidly, and the hydrocracking catalyst is one of the most important and key factors. [0003] Hydrocracking catalyst is a dual-functional catalyst, which has cracking activity and hydrogenation activity at the same time, that is, it contains acidic components and hydrogenation active components at the same time, and its acidity is mainly composed of heat-resistant inorganic oxides and / or va...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C10G47/04
Inventor 毛以朝史建文聂红石亚华李大东王奎熊震霖胡志海
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap