A technology of lamination and coating, applied in the direction of coating, device for coating liquid on the surface, etc., can solve the problems of film peeling, insufficient corrosion resistance of organic solvents, reduced efficiency of components, etc., and achieves low birefringence, The effect of high penetration and high solvent resistance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0035] Example one:
[0036] Preparation of light-hardening coating composition:
[0037] First, take a reaction flask and mix 57.1 mmol of dipentaerythritolpentaacrylate, 59.2 mmol of trimethylolpropane triacrylate, and 346 mmol of 2-Hydroxyethyl methacrylate. And photoinitiator 2,2-dimethoxy-2-phenyl-acetophenone (2,2-dimethoxy-2-phenyl-acetophenone, BDMK) 19.5mmol was placed in the reaction flask, then, the above compound Mix and stir at room temperature for 2 hours to obtain a light yellow transparent ultraviolet light hardening coating composition.
[0038] Formation of optical coating laminate:
[0039] Then, the above-mentioned ultraviolet light hardening coating composition is coated on a plastic substrate (such as TAC) using a spin coating method (2000rpm, 2min), using a concentrated high-pressure mercury lamp (120W / cm), and the irradiation energy is 1712mJ / cm 2 , It is hardened to form a protective layer on the plastic substrate with a thickness of 5-8μm, and the above-...
Example Embodiment
[0040] Embodiment two:
[0041] Preparation of light-hardening coating composition:
[0042] First, take a reaction flask and mix 51.9 mmol of dipentaerythritol hexaacrylate, 74.0 mmol of trimethylolpropane triacrylate, and 1,6-hexanediol dimethacrylate (1, 6-Hexanediol dimethacrylate) 19.7mmol, 2-Hydroxyethyl methacrylate (2-Hydroxyethyl methacrylate) 242mmol, UE-11 (provided by Deqian Company, the main ingredient is epoxy dimethacrylate) 4mmol and photostart Ciba Irgacure 184 (the main ingredient is hydroxycyclohexyl phenyl ketone) 17.2mmol was placed in the reaction flask, and then, the above compounds were mixed and stirred at room temperature for 2 hours to obtain a light yellow transparent ultraviolet light hardening coating composition . Formation of optical coating laminate:
[0043] The above-mentioned ultraviolet curable composition is uniformly coated on a plastic substrate (such as TAC) using a spin coating method (2000rpm, 2min) or a wire bar coating method, and irrad...
PUM
Property | Measurement | Unit |
---|---|---|
Thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap