A technology of vinyl acetate and acetic acid, which is applied in the field of preparing vinyl acetate by gas phase reaction, can solve problems such as reduction, and achieve the effects of large bulk porosity, reduced pressure drop loss, and high space-time yield

Inactive Publication Date: 2003-07-09
CHINA PETROLEUM & CHEM CORP
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the actual operation process, one kind of performance is often improved but another performance is reduced.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for producing vinyl acetate
  • Method for producing vinyl acetate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0022] The present invention will be further described below by some embodiments, in the embodiments: [Examples 1-6] carrier preparation:

[0023] Add extrusion aids and binders to the silica gel powder, mix well, and form the carrier precursor by extrusion. Dry the carrier at room temperature for 48 hours, then dry it at 100°C for 24 hours, and place it in a muffle furnace for 730 °C for 2 hours. After cooling, put it into an autoclave, add a solution made of acetic acid and ammonium acetate, take out the carrier at 165°C and 0.6MPa for 14 hours at constant temperature and pressure, wash it with distilled water until it is neutral, and then roast it at 300°C for 3 hours. After cooling, the desired carrier is obtained. The physical characteristics of the carriers prepared in each embodiment are shown in Table 1. Catalyst preparation:

[0024] With Na containing the equivalent of 6.35 g palladium 2 PdCl 4 and HAuCl equivalent to 2.96 g of gold 4 Prepare 450ml of aqueo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention uses ethylene, acetic acid and oxygen gas or oxygen-containing gas as raw material, adopts a gas phase reaction method and makes the reaction raw material mixed gas pass through the fixed bed layer consisting of the following described catalyst to make reaction to obtain the vinyl acetate. The carrier of said catalyst is SiO2 or mixture of SiO2-Al2O3, its active component contains Pd and KOAc, and it is formed into shell-type non-unfirom distribution. Said catalyst is a kind of globules, and the radius R of globe body is 2-4 mm, 3-8 grooves whose cross-section is made into the form of arch are cut along the radial direction on the surface of the globe body around the central shaft of the globe body, and the distanced between grooves is greater than 1.5 mm.

Description

technical field [0001] The invention relates to a method for preparing vinyl acetate by gas phase reaction using ethylene, acetic acid and oxygen or oxygen-containing gas as raw materials. Background technique [0002] In the reaction of preparing vinyl acetate by gas phase reaction using ethylene, acetic acid and oxygen or oxygen-containing gas as raw materials, the suitable catalyst is that the active component contains Pd and KOAc, and may contain Au, Ba, Cd, or their corresponding salts class of compounds. These active components are usually supported on SiO 2 , or SiO 2 with Al 2 o 3 on the mixture. The active components of this type of catalyst have already matured. After the 1970s, people mostly studied the distribution of the active components on the carrier, and the active components were egg yolk, egg white and eggshell. Etc. Non-uniform distribution of the catalyst is pushed out. The apparent activity, selectivity and anti-poisoning ability of catalysts wit...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C07C67/05C07C69/15
Inventor 杨运信张丽斌姚建东宋朝江孙春华
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka