Primary alkaline battery positire electrode material beta-NiOOH and its preparation technology
A technology of positive electrode material and preparation process, applied in the direction of alkaline battery electrode, electrode manufacturing, battery electrode, etc., can solve the problems that have not been seen yet, and achieve the effects of reducing self-discharge, improving stability, and increasing positive electrode discharge capacity
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0018] Embodiment 1: will not contain Co, Zn spherical Ni(OH) 2 5Kg into 40L 1MNa(OH) 2 In the solution reactor, the temperature of the solution is controlled at 60°C, and 40Kg of strong oxidizing agent is added. When the pH value of the reaction solution drops to 13, 10M NaOH solution is gradually added to control the pH value of the reaction solution to 13-14, and the reaction is carried out for 24 hours. After aging, washing, drying, and sieving, the product is numbered 1#.
Embodiment 2
[0019] Embodiment 2: Containing Co 4.0%, Zn 4.0% spherical Ni(OH) 2 5Kg put into 40L 1M Ni(OH) 2 In the solution reactor, the temperature of the solution is controlled at 60°C, and 40Kg of strong oxidizing agent is added. When the pH value of the reaction solution drops to 13, 10M NaOH solution is gradually added to control the pH value of the reaction solution to 13-14, and the reaction is carried out for 24 hours. After aging, washing, drying and sieving, the product is number 2#.
Embodiment 3
[0020] Embodiment 3: Containing Co 1.5%, Zn 4.0% spherical Ni(OH) 2 5Kg was put into 40L 1M Na(OH) 2 In the solution reactor, the temperature of the solution is controlled at 60°C, and 40Kg of strong oxidizing agent is added. When the pH value of the reaction solution drops to 13, 10M NaOH solution is gradually added to control the pH value of the reaction solution to 13-14, and the reaction is carried out for 24 hours. After aging, washing, drying, and sieving, the product is numbered 3#.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap