Method for fabricating polyurea lithium based lubricating grease
A lithium-based grease, polyurea technology, applied in the direction of lubricating composition, base material, petroleum industry, etc., can solve the problems of inconvenient operation, unfavorable industrial promotion and application, etc., and achieve the effect of improving the performance and simplifying the process.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0016] Prepare 200g of lubricating grease with a thickener amount of 20%, including 10% of urea group and 10% of lithium organic acid.
[0017] Weigh 160g 500SN mineral oil (viscosity 11mm at 100°C 2 / s) and divided into three parts, put dodecylamine and MDI into mineral oil and heat and melt, mix and react when the temperature reaches 80°C and stir, add 12 hydroxystearic acid after the reaction is complete, wait for melting and the temperature is at 91 Add lithium hydroxide aqueous solution to react at ℃, continue heating until the temperature reaches 180℃ for 15 minutes, then heat to 200℃, add quenching oil, cool to room temperature and grind twice.
Embodiment 2
[0019] Prepare 200g of lubricating grease with a thickener amount of 18%, including 8% of urea group and 10% of lithium organic acid.
[0020] Take by weighing 164g α-olefin oil (100 ℃ viscosity 12mm 2 / s) and divided into three parts, put octadecylamine and TDI into mineral oil, heat and melt, mix and react when the temperature reaches 75°C and stir, add stearic acid after the reaction is complete, wait for melting and the temperature is at 95°C Add lithium hydroxide aqueous solution to react, continue heating until the temperature reaches 180°C for 15 minutes, then heat to 205°C, add quenching oil, cool to room temperature and grind twice.
Embodiment 3
[0022] Prepare 200g of lubricating grease with a thickener amount of 15%, including 5% of urea group, 5% of lithium stearate, and 5% of lithium benzoate.
[0023] Weigh 110g mineral oil (viscosity 12mm at 100°C 2 / s) and divided into two parts, weighed 60g ester oil as quenching oil. Put cyclohexylamine and TDI into mineral oil and heat to melt. When the temperature reaches 75°C, mix and react and stir. After the reaction is complete, add stearic acid and benzoic acid. After melting and the temperature is at 95°C, add lithium hydroxide aqueous solution To react, continue heating until the temperature reaches 180°C for 15 minutes, then heat to 205°C, add quenching oil, cool to room temperature and grind twice.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap