Formula of compoiste adhering magnet

A technology of bonded magnets and formulations, applied in the direction of magnetic objects, magnetic materials, and inorganic materials, can solve the problems of poor fluidity of ingredients, low magnetic properties, and accelerated thermal decomposition of binders, etc., and meets the low requirements of equipment , Wide range of magnetic properties, good machinability

Active Publication Date: 2005-07-27
HENGDIAN GRP DMEGC MAGNETICS CO LTD
View PDF0 Cites 35 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The invention mainly aims at the problems of poor fluidity of ingredients, high molding temperature, accelerated thermal decomposition speed of binder, and low magnetic properties in the prior art during molding; it provides a lubricant that adopts organic and inorganic lubricants so that The fluidity of the ingredients is good at high and low temperatures, the molding temperature is low, which can effectively alleviate the pyrolysis of the binder, and the composite bonded magnet formula with high magnetic properties

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Formula of compoiste adhering magnet
  • Formula of compoiste adhering magnet
  • Formula of compoiste adhering magnet

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] First, mix 95 grams of anisotropic Nd-Fe-B magnetic powder with 5 grams of anisotropic strontium ferrite magnetic powder, add 1.0 gram of silane coupling agent to surface treat the magnetic powder, add 0.9 gram of oleic acid after drying and knead for 10 Minutes, and then add 1.0 g of epoxy resin thereto, and mix for another 20 minutes to obtain a composite resin bonded magnet mixture, and measure the fluidity of the mixture according to the ASTM-D1238 standard. Then inject the mixture into a molding mold, compress and mold in a magnetic field of 15KOe, and harden the molded body at 100°C for 1 hour to obtain a composite bonded magnet. The tensile strength of each formula is under the condition of non-orientation magnetic field, according to the above-mentioned molding process conditions, according to the ASTM-D790 standard molding test sample, and then test the bending strength of the test sample under the test conditions specified in the ASTM-D790 standard.

Embodiment 2

[0034] Anisotropic strontium ferrite powder (52wt%), isotropic NdFeB powder (particle size 90μm) (40wt%), silane coupling agent (0.7wt%), thermoplastic resin nylon-12 (6wt%) , phenolic antioxidant (0.7wt%), and organic lubricant EBS (0.6wt%) were mixed uniformly with a high-speed mixer. The fluidity of the mixture was measured according to ASTM-D1238 standard.

[0035] Then, each formulation mixture having the composition shown in Table 2 was sufficiently kneaded at 250° C. using a twin-screw kneader to obtain a composite bonded magnet mixture. Next, pelletizing is performed to obtain pellets with an average particle diameter of 2-6 mm. The samples were then molded in an injection molding machine. The molding temperature was 265°C. An orientation magnetic field of 10000Oe is applied during molding. The size of the molded sample is Φ10mm×10mm.

[0036] The corrosion resistance of the sample is to put the sample in the constant temperature and humidity standard test box, st...

Embodiment 3

[0047] The anisotropic Nd-Fe-B permanent magnetic powder (50wt%) and strontium ferrite magnetic powder (50wt%) were respectively treated with an appropriate amount of silane coupling agent, the two magnetic powders were mixed, and then 1.5wt% of thermosetting resin was added Epoxy resin (containing curing agent and accelerator) and 0.5wt% polyamide elastomer, added 0.1wt% stearic acid lubricant, mixed, pressed in a 16KOe magnetic field, and cured to obtain a bonded composite magnet.

[0048] The flowability of the ingredients is measured according to ASTM-D1238 standard. The tensile strength of the sample is to form the test piece according to the ASTM-D638 standard under the condition of non-orientation magnetic field, and then test the tensile strength of the test piece under the test conditions specified in the ASTM-D638 standard.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention is related to a permanent magnet consisting of more than two kinds of permanent magnetic powder, special binder, organic or inorganic lubricant, and other additives. The invention has following features: 1) the organic or inorganic lubricant makes the ingredient have good fluidity, low forming temperature, and high loading level of magnetic powder; 2) the production cost is low and the application of magnetic property is wide.

Description

technical field [0001] The invention relates to a bonded permanent magnet, especially a composite bonded permanent magnet made of two or more permanent magnet powders, a special binder, an internal organic lubricant and other additives. Background technique [0002] With the development of high technology, people have higher and higher requirements for electronic information products. At present, electronic information complete machine products are developing in the direction of "light, thin, short and small". This puts forward higher requirements for permanent magnet materials used in the electronic information industry. Compared with sintered permanent magnets, bonded permanent magnets, especially high-performance bonded permanent magnets, can obtain products with high dimensional accuracy without post-processing due to their excellent mechanical properties, and can prepare complex shapes and extremely thin rings. The advantages of shape-shaped products and continuous ma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): H01F1/032H01F1/057H01F1/08H01F1/10H01F1/113
Inventor 何时金颜冲包大新陆柏松郑增琨
Owner HENGDIAN GRP DMEGC MAGNETICS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap