Daily-use ceramic and preparation method thereof

A kind of technology for ceramics and daily use, which is applied in the field of daily-use ceramics with jade texture and its preparation. It can solve the problem that ordinary raw materials cannot be prepared by one-time firing technology to prepare high-grade daily-use ceramics, and achieve good gloss and good thermal stability. , the effect of high transparency

Inactive Publication Date: 2007-02-28
HUAIREN JIAMING CERAMICS
View PDF0 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to solve the problem in the prior art that ordinary raw materials cannot be used to prepare high-grade daily-use ceramics by one-time firing technology, the present invention proposes a method for preparing daily-use ceramics by adding a small amount of mineralizer to ordinary raw materials. The ceramics produced by it have real The Porcelain and Texture of Bone China

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] (1) Preparation of raw materials: Quartz, talc, kaolin and bentonite are sorted and coarsely crushed respectively, and 25kg of quartz, 15kg of talc, 15kg of talc, 20kg of kaolin and 10kg of bentonite are weighed ;

[0026] (2) Make finished mud: mix each raw material weighed in step (1), coarsely grind, pass 8 mesh sieves, pulping, wet ball mill, pass 250 mesh sieves, press filter, rough refining, stale at room temperature for 7 Tian, ​​refined into finished mud;

[0027] (3) Forming: rolling forming;

[0028] (4) Firing: put the shaped products into blanks, fire them in a tunnel kiln at 1320°C for 24 hours, open the porcelain, and select qualified fired products;

[0029] (5) Decoration: Carry out overglaze coloring as required, color firing at 800°C, and select qualified finished products.

[0030] After analysis and detection, the prepared ceramics have the following chemical composition in weight percentage:

[0031] SiO 2 71.71%; Al 2 o 3 14.19%; Fe 2 o ...

Embodiment 2

[0036] (1) Raw material preparation: Quartz, talc, kaolin and bentonite are sorted and coarsely crushed respectively, and 20kg of quartz, 18kg of talc, 10kg of talc, 36kg of kaolin and 3kg of bentonite are weighed ;

[0037] (2) Make finished mud: mix each raw material weighed in step (1), coarsely grind, pass 8 mesh sieves, pulping, wet ball mill, pass 250 mesh sieves, press filter, rough refining, stale at room temperature for 7 Tian, ​​refined into finished mud;

[0038] (3) Molding: grouting molding;

[0039] (4) Firing: put the shaped products into blanks, fire them in a tunnel kiln at 1320°C for 24 hours, open the porcelain, and select qualified fired products;

[0040] (5) Decoration: Carry out overglaze coloring as required, color firing at 800°C, and select qualified finished products.

[0041] Entrust Tangshan City Product Quality Supervision and Inspection Institute to inspect the finished ceramics, and the results are shown in Table 2.

[0042] Test it...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a daily ceramics and preparing method, which is characterized by the following: adopting once sintering technology to prepare similar bone-ceramics; adding mineralizer based on common materials; allocating.

Description

technical field [0001] The invention relates to a daily-use ceramic and a preparation method thereof, more specifically, the invention relates to a daily-use ceramic with a jade texture that can be compared with real bone china and a preparation method thereof. Background technique [0002] my country has thousands of years of ceramic culture history. In the existing ceramic preparation technology, ordinary daily-use ceramics can only be prepared by using ordinary raw materials, and one-time firing is adopted. However, high-grade daily-use ceramics are fired twice. True bone china is a world-recognized high-grade porcelain. [0003] In the prior art, general primary firing technology cannot be adopted to prepare a high-grade product that can be compared with the real bone china fired for the second time. Contents of the invention [0004] In order to solve the problem in the prior art that ordinary raw materials cannot be used to prepare high-grade daily-use ceramics by...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/14C04B35/16C04B35/622C04B41/86
Inventor 曹希全陈玉龙
Owner HUAIREN JIAMING CERAMICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com