Multi-layered material having stereo-texture

A technology of multi-layer materials and multi-layer substrates, which is applied in the direction of layered products, synthetic resin layered products, and techniques for producing decorative surface effects, etc., can solve the problems of being susceptible to wear and oxidation, and is not easy to deform, Enhance the three-dimensional effect

Inactive Publication Date: 2007-04-18
陈福生 +2
View PDF2 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This method requires precise alignment, and the formed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Multi-layered material having stereo-texture
  • Multi-layered material having stereo-texture
  • Multi-layered material having stereo-texture

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0025] In FIG. 1, a PET film 10 is indicated on which an aluminum layer 11 is formed. In FIG. 2 , it is pointed out that an EVA adhesive layer 13 is formed on a PET base plate 12 . In FIG. 3 , it is indicated that the aforementioned layers are laminated to form a multi-layer substrate 1 .

[0026] in:

[0027] The PET film 10 is a thin film made of PET plastic or similar materials, which can be fully transparent or translucent so as to have see-through.

[0028] The aluminum layer 11 is formed on the bottom surface of the PET film 10 by electroplating aluminum metal, which provides a white gold glossy effect. Other metals can be used instead of aluminum, such as gold, silver, or copper, when other colors of gloss effect are desired.

[0029] The PET base 12 is a thin plate made of PET plastic or similar material, but thicker than the PET film 10 . In some practical applications, the thickness of the PET base 12 is 80-200 μm, and the thickness of the PET film 10 is 12-23 μm...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A multi-layer material with concave-convex veins on its surface is composed of a surficial PET membrane with concave-convey veins formed by ironing, an aluminum layer with same concave-convex veins, an EVA resin layer for supporting the convex part of said veins, and a PET substrate.

Description

technical field [0001] The invention relates to a technology for forming three-dimensional lines on an article, especially a multi-layer material with three-dimensional lines involving the integrated use of four materials: PET, PU, ​​EVA, and aluminum. Background technique [0002] The leather goods shown in the Taiwan Province of China Announcement No. 584065, the three-dimensional picture shown in the Taiwan Province of China No. M248633, and the reflective cloth shown in the Taiwan Province of China No. M255150 all use a special refraction layer or The reflective layer is used to produce a three-dimensional pattern effect, but the actual pattern is not a three-dimensional texture. [0003] In the Taiwan Province of China Announcement No. 403639 case, it is pointed out that a three-dimensional marker has a three-dimensional pattern, but it must first print a flat pattern, and then use a zinc plate with the same pattern to emboss the three-dimensional lines. This method re...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B32B5/00B32B3/30B32B27/18B44C1/18
Inventor 陈福生蔡永铭吴明良
Owner 陈福生
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap