Synthesis method for zeolite

A technology for synthesizing zeolite and seed crystals, which is applied in the direction of crystalline aluminosilicate zeolite, mercerized crystalline aluminosilicate zeolite, etc., to achieve the effects of cost reduction, environmental friendliness, and saving dissolution

Inactive Publication Date: 2007-09-12
BEIJING UNIV OF CHEM TECH
View PDF6 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although this method does not use the aqueous solution colloidal process, it needs to be roasted at high temperature to form a colloid

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Synthesis method for zeolite
  • Synthesis method for zeolite
  • Synthesis method for zeolite

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] The synthesis of embodiment 1 mordenite

[0024] Weigh solid SiO 2 4.9 grams (0.08mol), Al 2 o 3 1.36 g (0.01 mol), 0.96 g (0.024 mol) of sodium hydroxide, put it into a blender for mechanical mixing, after fully stirring, put the mixture on a support, feed water vapor, and maintain the system temperature at 170 ° C to start crystallization , the crystallization time is 6 days, and the mordenite-type zeolite can be obtained (the structure determined by XRD is shown in Figure 1).

Embodiment 2

[0025] The synthesis of embodiment 2 mordenite

[0026] Weigh SiO 2 10.0 g (0.16 mol), Al 2 o 3 1.36 g (0.01 mol), 3.2 g (0.08 mol) of sodium hydroxide, put it into a blender for mechanical mixing, after fully stirring, put the mixture on a stand, feed water vapor, and maintain the system temperature at 260 ° C to start crystallization , the crystallization time is 3 days, and the mordenite-type zeolite can be obtained (the structure determined by XRD is shown in Figure 2).

Embodiment 3

[0027] Embodiment 3: the synthesis of ZSM-5 type zeolite

[0028] Weigh SiO 2 18.0 g (0.3 mol), Al 2 o 3 1.36 grams (0.01mol), 3.6 grams (0.09mol) of sodium hydroxide, 0.8 grams of ZSM-5 seed crystals, 6.6 grams (0.09mol) of butylamine, put it into a stirrer and carry out mechanical mixing, after fully stirring, the The mixture was placed on a support, fed with water vapor, and the crystallization started at a system temperature of 150°C. The crystallization time was 1 day to obtain a ZSM-5 zeolite (the structure determined by XRD is shown in Figure 3).

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

This invention relates to a method for synthesizing zeolite, which mixes a solid Si source and Al source under a high alkali condition, mixes them fully and crystallizes them in vapour to synthesize many kinds of zeolite products of silk zeolite, ZSM-5 or MCM-22, beta.

Description

technical field [0001] The present invention relates to a method for synthesizing zeolite. Various zeolite products such as mordenite, ZSM-5, MCM-22, and beta zeolite can be obtained. Background technique [0002] Zeolites are very useful inorganic materials and are widely used in many fields such as catalysis and separation. The synthesis of zeolite generally adopts a hydrothermal synthesis method, such as patents CN1074388C, CN1328961A, CN1166563C, CN1530323A, etc., which use nitrogen-containing organic matter as a template to synthesize molecular sieves. The entire synthesis process is carried out in an aqueous medium. This method uses organic amine templates , silicon source, and aluminum source are dissolved in water. The template agent is a polar substance that is easily soluble in water. After dissolving in water, its effective components will be lost with the discharge of the mother liquor, resulting in a low utilization rate of the expensive template agent. Moreov...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C01B39/26
Inventor 陈标华曹刚黄崇品李冰洁
Owner BEIJING UNIV OF CHEM TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap