Method for preparing ferrite bismuth lanthanum-titanate lead solid solution ceramic under strong magnetic field action

A technology of bismuth lanthanum ferrite and solid solution is applied in the field of preparing bismuth lanthanum ferrite-lead titanate solid solution ceramics, which can solve the problem that the strong magnetic field has not been applied, and achieves high crystalline properties, improved ferromagnetic and magnetoelectric coupling energy. Effect

Inactive Publication Date: 2007-09-19
SHANGHAI UNIV
View PDF0 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, in terms of material preparation, strong magnetic fields are mainly used in the solidification of metals, recrystallization of iron and steel materials, and solid-state phase transitions, while strong magnetic fields have not been used in the preparation of inorganic electronic functional materials.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing ferrite bismuth lanthanum-titanate lead solid solution ceramic under strong magnetic field action
  • Method for preparing ferrite bismuth lanthanum-titanate lead solid solution ceramic under strong magnetic field action
  • Method for preparing ferrite bismuth lanthanum-titanate lead solid solution ceramic under strong magnetic field action

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Preparation of 0.57(Bi 0.9 La 0.1 )FeO 3 -0.43PbTiO 3 Solid solution ceramics, the preparation steps of this embodiment are as follows:

[0027] (1) weighing and batching according to the stoichiometric ratio of the above chemical formula; using Bi with a purity greater than 99.9% 2 o 3 , La 2 o 3 , Fe 2 o 3 , PbCO 3 and TiO 2 Powder; the mass of each oxide is:

[0028] Bi 2 o 3 19.6198g;

[0029] La 2 o 3 1.5275g;

[0030] Fe 2 o 3 7.4743g;

[0031] PbCO2 3 18.8594g;

[0032] TiO 2 5.6393 g.

[0033] Add absolute ethanol as a ball milling agent, and use zirconia balls as a ball milling medium; the weight ratio of the three is powder: zirconia balls: ethanol = 1:1.5:1; put it in a ball mill for 24 hours to make the oxide fully Blend and grind finely.

[0034] (2) After drying the above mixture at 80°C, raise the temperature to 450°C at a rate of 5°C / min, keep it warm for 2 hours, then raise th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Curie pointaaaaaaaaaa
piezoelectric charge coefficientaaaaaaaaaa
Curie pointaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for producing ferric acid bismuth lanthanum-lead titanate solid solution ceram in an intense magnetic field, belonging to the technical field of inorganic non-metal material and solid solution ceram material. The designed chemical formula of ferric acid bismuth lanthanum-lead titanate solid solution ceram is: (1-x)(Bil-yLay)FeO3-xPbTiO3; wherein: 0.2<=x<=0.6, y=0-0.4; weighing and preparing materials according to the chemical dosage rate of the chemical formula; weighing and mixing the Bi2O3, La2O3, Fe2O3, PbCO3 and TiO2 powder with a purity more than 99.9%, adding ethanol as abrasive, zirconia grain as abrasing medium; ball milling for 24 hours in the ball mill, mixing sufficiently and levigating; calcining and synthesizing in 750 DEG C in the magnetic intensity of 7-14T for 24 hours; ball milling for 24 hours; then doing a secondary ball milling; then prilling, tabletting; finally sintering the pressed compact in 1080-1100 DEG C, meanwhile introducing the intense magnetic field and obtaining the ferro-electricity ferromagnetism ceramic material.

Description

technical field [0001] The invention relates to a method for preparing bismuth lanthanum ferrite-lead titanate solid solution ceramics under the action of a strong magnetic field, belonging to the technical field of inorganic non-metallic materials and solid solution ceramic materials. Background technique [0002] Multiferroic materials integrate the properties of ferroelectricity, ferromagnetism and ferroelasticity, and have unique coupling effects between multiple fields (force, electricity, magnetism, heat and light), showing many important coupling properties, such as magnetoelectricity , piezoelectric, pyroelectric and piezoelectric effects, etc., are important advanced functional materials. The coupling performance of these materials provides a great degree of freedom for device design, so that they can be developed into various sensors, transducers, drivers and information storage, and are used in aerospace, automobile industry, biology, medicine, information and oth...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/622C04B35/63C04B35/64C04B35/472C04B35/40
Inventor 程晋荣陈建国俞圣雯孟中岩
Owner SHANGHAI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com