Montmorillonite/beta molecular sieve composite material and preparation thereof
A technology of beta molecular sieve and composite material is applied in the field of montmorillonite/beta molecular sieve composite material and its preparation, and achieves the effects of simple process, wide source and simple preparation process
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0027] (1) Preparation of directing agent: silicon source, aluminum source, template agent, sodium hydroxide and water were prepared according to (60-90) SiO 2 : Al 2 O 3 : (8~14)R: (1~4)Na 2 O: (600~1000)H 2 The molar ratio of O is mixed at room temperature and under mechanical stirring conditions, and the stirring is continued until the raw materials are evenly mixed, then transferred to the synthetic bomb, and heated at 120 to 150 ° C under airtight conditions for 2 to 8 days, preferably 2 to 3 days. , to make a guide agent.
[0028] Said silicon source is white carbon black or silica sol; aluminium source is sodium metaaluminate or aluminium hydroxide, preferably sodium metaaluminate; said template R is tetraethylammonium hydroxide (TEAOH) or Tetraethylammonium bromide, preferably tetraethylammonium hydroxide.
[0029] (2) Preparation of molecular sieve gel: silicon source, aluminum source, sodium hydroxide and water were prepared according to (10-60) SiO 2 : Al 2 O...
Example Embodiment
[0041] Example 1
[0042] (1) Preparation of directing agent:
[0043] ①Weigh 0.9g of sodium aluminate into a 250ml conical flask, add 60ml of 25% TEAOH, and magnetically stir to dissolve completely; ②Weigh 0.48g of NaOH and 14.4g of white carbon black into the conical flask, and stir with magnetic stirring for 0.5 hours, the gel was charged into a synthesis kettle and heated at 140 °C for 2 days to prepare a directing agent.
[0044] (2) Preparation of montmorillonite / β molecular sieve composite material:
[0045] ① Dissolve 1.1g of sodium aluminate in 100ml of distilled water, add 4.56g of NaOH, and then add 102ml of silica sol (SiO 2 The content is 1.956M), dissolved by magnetic stirring; 2. get 6ml of the guiding agent and add to the above solution, and magnetically stir for 0.5 hours; 3. add 6.0 g of refined sodium-based montmorillonite microspheres to step 2. in the conical flask to obtain gel, magnetic After stirring for 0.5 h, the gel was put into a synthesis kettle...
Example Embodiment
[0048] Example 2
[0049] (1) Preparation of directing agent:
[0050] ①Weigh 0.9g of sodium aluminate into a 250ml conical flask, add 60ml of 25% TEAOH, and magnetically stir to completely dissolve; ②Weigh 0.48g NaOH and 14.4g white carbon black into the conical flask; ③Magnetically stir 0.5 hours, the gel was charged into a synthesis kettle and heated at 140 °C for 2 days.
[0051] (2) Preparation of montmorillonite / β molecular sieve composite material:
[0052] ①Weigh 4.56g of NaOH, dissolve it in 20ml of water, add 1.1g of sodium aluminate, and then add 132ml of silica sol (SiO 2 The content is 1.956M), dissolved by magnetic stirring; 2. get 6 mL of guiding agent and add to the above solution, and magnetically stir for 0.5 hours; 3. add 3.0 g of natural sodium-based montmorillonite microspheres into step 2. conical flask to obtain gel, magnetic After stirring and mixing, the gel was put into a synthesis kettle and crystallized at 140 °C for 4 days.
[0053] (3) The abo...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology