Ceramic-phase-containing iron-based amorphous nanocrystalline composite coating and preparation thereof

A nanocrystalline composite, iron-based amorphous technology, applied in coatings, metal material coating processes, melt spraying and other directions, can solve the problems of high construction cost, high porosity, inconvenient on-site construction, etc., and achieve coating combination. The effect of high strength, improving performance and prolonging service life

Active Publication Date: 2008-11-05
CENT IRON & STEEL RES INST
View PDF1 Cites 43 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, a single ceramic coating is limited in its application because of its high porosity, low fracture toughness and large thermal expansion coefficient difference with the base metal material; metal-ceramic composite coatings, such as Cr3C2-(NiCr), Metal-ceramic composite coatings such as WC-Co can obtain high coating quality ...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ceramic-phase-containing iron-based amorphous nanocrystalline composite coating and preparation thereof
  • Ceramic-phase-containing iron-based amorphous nanocrystalline composite coating and preparation thereof
  • Ceramic-phase-containing iron-based amorphous nanocrystalline composite coating and preparation thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0024] 1. The weight percentage of selected ingredients is Cr 16.99%, Mo 1.98%, W 3.80%, Mn 0.38%, B 3.10%, C 0.80%, Si 0.43%, and the weight of Co-wrapped WC powder in the drug core accounts for 5.20% of the total weight, The balance is Fe, and the above ingredients are prepared into drug core filaments. The total composition of the drug skin and drug core meets the above ingredients. The particle size of Co-coated WC powder in the drug core is 44 μm to 124 μm, and the particle size of other powders is between 26 μm and 150 μm. , The drug core weight accounts for 37.07%. The arc spraying process parameters are: arc voltage 34V, working current about 200A, atomizing gas pressure 0.7MPa, and spraying distance 200mm. The bonding strength between the sprayed coating and the substrate is above 46MPa, and the micro-Vickers hardness is greater than 900HV0.3kg. It has the characteristics of high hardness, good wear resistance, and good erosion resistance. It is suitable for high-tempe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the field of thermal spraying and particularly relates to a composite amorphous and nano-crystalline coating layer with ceramic phase and ferrum base and a preparation method thereof. Carbide or oxide ceramics of Co or Ni ladles are firstly added into a flux core, a flux-cored wire is prepared together with the flux core and a ferrum-base alloy with amorphous ingredients and used as a spraying material, and the electric arc spraying method is adopted for leading the flux-cored wire to be melted, atomized into fused drops and finally deposited on a substrate, thus preparing the composite amorphous and nano-crystalline coating layer with ceramic-phase structure and ferrum base, which has the performance of high bond strength, good wear resistance, corrosion resistance and oxidation resistance as well as remarkably prolonged service life of the substrate, and the composite amorphous and nano-crystalline coating layer with ceramic phase and ferrum base can be widely applied to the restoration and the protection of device parts in the fields of metallurgy, electric power and petroleum, etc.

Description

technical field [0001] The invention belongs to the field of thermal spraying, in particular to an iron-based amorphous nanocrystalline composite coating containing a ceramic phase and a preparation method thereof. Background technique [0002] The failure of materials mostly occurs on the surface. Wear and corrosion are the most common forms of failure of materials or mechanical parts during use, which cause huge losses to the national economy every year. Surface engineering technology is an important way to improve the surface properties of materials, among which thermal spraying technology is one of the most important technologies. A layer of metal or cermet coating can be deposited on the surface of the material by thermal spraying, so that it has properties such as wear resistance, corrosion resistance, and oxidation resistance, thereby protecting the base material. With the rapid development of current industrial technology, higher requirements are put forward for the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23C4/04
Inventor 齐飞霞韩伟倪晓俊
Owner CENT IRON & STEEL RES INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap