High strength starch-based degrading and environment-protecting material and preparation method
An environmentally friendly material and starch-based technology, applied in the field of rapidly degradable raw materials, can solve problems such as product quality not meeting requirements, environmental and health damage, and environmental white pollution, so as to improve product quality, control degradation cycle, and reduce production costs. Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0023] A high-strength starch-based degradable environmental protection material, its composition includes: starch, polyvinyl alcohol, plant pond, plasticizer, degradation control agent, polycaprolactone and polyhydroxybutyrate copolymer, hexabutyl hexabutyl Sugar, the parts by weight of the starch are 51-80, the parts by weight of the polyvinyl alcohol are 12-20, the parts by weight of the plant sugar are 2-10.5, the parts by weight of the plasticizer The parts by weight of the degradation control agent are 2.5-8, the parts by weight of the degradation control agent are 0.2-1, the parts by weight of the polycaprolactone and polyhydroxybutyrate copolymer are 5-9, the parts by weight of the The parts by weight of the hexabutyl-hexetan are 0.2-0.5.
Embodiment 2
[0025] A high-strength starch-based degradable environmental protection material, its preparation process is: take 51kg of natural polymer starch, 12kg of polyvinyl alcohol, 2kg of plant sugar, 2.5kg of plasticizer, 0.2kg of degradation control agent, 5kg of Copolymer of polycaprolactone and polyhydroxybutyrate, 0.2kg of hexabutyl hexetan, the raw materials are subjected to polymerization reaction, blending and copolymerization modification, the equipment used is an oil heating high mixing and cold mixing machine, the temperature Add natural polymer starch and polyvinyl alcohol polyvinyl alcohol at 70°C and mix at high speed, then add polycaprolactone and polyhydroxybutyrate copolymer at 80°C and mix at high speed, continue heating to 100°C for 2 times Add plant sugar (xylose, maltose or starch sugar), plasticizer (salad oil), degradation control agent and hexabutyl chitosan, and carry out polymerization reaction, blending and copolymerization modification, the temperature is 1...
Embodiment 3
[0027] A high-strength starch-based degradable environmental protection material, its preparation process is: take 60kg of natural polymer starch, 18kg of polyvinyl alcohol, 8kg of plant sugar, 6kg of plasticizer, 0.8kg of degradation control agent, 8kg of polyvinyl alcohol Caprolactone and polyhydroxybutyrate copolymer, 0.4kg of hexabutyl hexetan, the raw materials are subjected to polymerization reaction blending copolymerization modification, the equipment used is an oil heating high mixing and cold mixing machine, the temperature is at Add natural polymer starch and polyvinyl alcohol polyvinyl alcohol at 80°C, and mix at high speed, then add polycaprolactone and polyhydroxybutyrate copolymer at 100°C, and mix at high speed, continue heating to 110°C and mix three times Plant sugar (xylose, maltose or starch sugar), plasticizer (salad oil), degradation control agent and hexabutyl chitosan are added, and the polymerization reaction is carried out for blending and copolymeriza...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com