Process for manufacturing corrosion resistant low-chromium tubing and casing in CO2 and H2S coexisted environment

A preparation process and corrosion-resistant technology, applied in the direction of manufacturing tools, process efficiency improvement, pipes, etc., can solve the problems of complicated corrosion inhibitor filling process, large one-time investment of high-alloy steel, insufficient strength of glass fiber reinforced plastic, etc. The effect of improving the corrosion resistance of CO2/H2S and the corrosion resistance of CO2

Active Publication Date: 2009-04-15
XIAN MAURER PETROLEUM ENG LAB
View PDF0 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the complex filling process of corrosion inhibitors and high long-term investment, the damage of the coating layer during use will cause local corrosion hidden dangers and other problems. The safest protective measure is still to use corrosion-resistant materials
However, the strength of FRP is insufficient, and the one-time investment of high-alloy steel is too large

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Embodiment 1: a kind of CO 2 and H 2 The preparation process of the corrosion-resistant low-chrome oil casing in the S coexistence environment comprises the following steps in sequence,

[0033] 1. Steelmaking: raw materials include the following components (wt%), C: 0.20%, Si: 0.37%, Mn: 0.47%, P: 0.011%, S: 0.003%, Cr: 2.95%, Mo: 0.67%, Cu: 0.11%, Ni: 0.009%, Al: 0.036%, Nb: 0.044%, Ti: 0.03%, B: 0.002%, V: 0.07%; the control components (wt%) are: As: 0.012%, Sn: 0.008%, Ca treatment, Ca / S ratio is 1.5; the rest is iron.

[0034] Use electric arc furnace to directly reduce iron and pig iron to obtain base metal with low concentration of residues and inclusions, refine base metal in ladle furnace, then secondary alloying, and finally degassing, wherein: feed Si-Ca wire inclusion metamorphosis The treatment is to spheroidize manganese sulfide inclusions, reduce the sensitivity of HIC ladder cracks, and the Ca / S ratio is ≥ 1.5;

[0035] II. Rolling: Rolling is the se...

Embodiment 2

[0038] a CO 2 and H 2 The preparation process of the corrosion-resistant low-chrome oil casing in the S coexistence environment comprises the following steps in sequence,

[0039] I. Steelmaking:

[0040] Including the following components (wt%), C: 0.22%, Si: 0.50%, Mn: 0.50%, P: 0.015%, S: 0.004%, Cr: 3.10%, Mo: 0.42%, Cu: 0.15%, Ni: 0.05%, Al: 0.044%, Nb: 0.047%, Ti: 0.03%, B: 0.002%, V: 0.09%; control components are: As: 0.014%, Sn: 0.01%, Ca treatment, Ca / S The ratio is 1.5; the rest is iron.

[0041] Use electric arc furnace to directly reduce iron and pig iron to obtain base metal with low concentration of residues and inclusions, refine base metal in ladle furnace, then secondary alloying, and finally degassing, wherein: feed Si-Ca wire inclusion metamorphosis The treatment is to spheroidize manganese sulfide inclusions, reduce the sensitivity of HIC ladder cracks, and the Ca / S ratio is ≥ 1.5;

[0042] II. Rolling: During the rolling process, the thickness of the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of oil pipe material, in particular to a process for preparing a corrosion resistant low-chromium oil sleeve under the coexisting environment of CO2 and H2S. The invention overcomes the problems existing in the prior art. The technical proposal provided by the invention is that the process for preparing the corrosion resistant low-chromium oil sleeve under the coexisting environment of CO2 and H2S orderly comprises the following steps: 1. steel-making, wherein an electrified arc furnace is used to directly reduce iron and pig iron to obtain base metal, the base metal is refined in a ladle furnace and alloyed twice, and finally gas in the base metal is removed; 2. rolling, wherein the correct size of the material required is obtained by the step; and, 3. heat treatment and finishing. Compared with the prior art, the process has the advantages that the material prepared by the process has good CO2 / H2S corrosion resistance and economical efficiency; when used in the underground mining, the material can replace the common carbon steel; and the cost is no more than 150 percent higher than that of the oil sleeve material in the same level, but the material can bring much more benefits.

Description

Technical field: [0001] The invention relates to the technical field of petroleum pipes, in particular to CO 2 and H 2 Preparation process of corrosion-resistant low-chrome oil casing in S coexistence environment. Background technique: [0002] With the deepening of oil and gas field development, CO 2 / H 2 The number of oil and gas wells in S is increasing, and accidents caused by corrosion damage of oil and casing occur frequently, which seriously affects the safe production of oil and gas fields, and becomes more and more serious with the deepening of development. for CO 2 / H 2 The protective measures taken for S corrosion mainly include: the use of corrosion-resistant materials (including the use of glass fiber reinforced plastics and alloy steel with high alloy composition), the addition of corrosion inhibitors and the use of anti-corrosion coatings. However, due to the complexity of the corrosion inhibitor filling process and the high long-term investment, the dam...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B23P17/00C22C38/54C21C5/52C21C7/04C21D9/08C21D1/18F16L9/02
CPCY02P10/20
Inventor 韩勇赵国仙李平全吕祥鸿
Owner XIAN MAURER PETROLEUM ENG LAB
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap