Environmental-friendly clinker-free cement and preparation method thereof
A clinker-free cement and environmentally friendly technology, applied in cement production, etc., can solve problems such as limited application range, high price, and material cracking, and achieve the effects of wide source of raw materials, excellent performance, and increased strength
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0053] a) The granulated blast furnace slag is dried, crushed and ground to obtain a specific surface area of 420m 2 / kg of slag powder;
[0054] b) drying and grinding the carbide slag, and sieving it with a 0.08mm sieve to obtain carbide slag powder;
[0055] c) The slag powder prepared in step a) and the calcium carbide slag powder and gypsum and additives prepared in step b) are prepared according to the 1# formula in Table 1, but excluding the water reducer, and mixed uniformly; that is Clinker-free cement can be produced.
[0056] The clinker-free cement and standard mortar were mixed, formed and cured; the cured specimens were tested for performance according to the methods and requirements specified in GB / T17671-1999, and the test results are shown in Table 2.
Embodiment 2
[0058] a) The granulated blast furnace slag is dried, pulverized and ground to obtain a specific surface area of 450m 2 / kg of slag powder;
[0059] b) drying and grinding the carbide slag, and sieving it with a 0.08mm sieve to obtain carbide slag powder;
[0060] c) The slag powder obtained in step a) and the calcium carbide slag powder and gypsum and additives prepared in step b) are formulated according to the 2# formula in Table 1, but the water reducer is not included, and mixed uniformly; that is Clinker-free cement can be produced.
[0061] The clinker-free cement and standard mortar are mixed, formed and cured; the cured specimens are subjected to performance testing according to the methods and requirements stipulated in GB / T17671-1999. The test results are shown in Table 2.
Embodiment 3
[0063] a) The granulated blast furnace slag is dried, pulverized and ground to obtain a specific surface area of 480m 2 / kg of slag powder;
[0064] b) drying and grinding the carbide slag, and sieving it with a 0.08mm sieve to obtain carbide slag powder;
[0065] c) The slag powder obtained in step a) and the calcium carbide slag powder and gypsum and additives prepared in step b) are formulated according to the 3# formula in Table 1, but the water reducer is not included, and mixed uniformly; Clinker-free cement can be produced.
[0066] The clinker-free cement and standard mortar are mixed, formed and cured; the cured specimens are subjected to performance testing according to the methods and requirements stipulated in GB / T17671-1999. The test results are shown in Table 2.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap