Antimony Silicate Modified High Gradient Zinc Oxide Pressure Sensitive Material

A pressure-sensitive material, antimony silicate technology, applied in the direction of varistors, etc., can solve the problems of wasting raw material resources, small varistor voltage gradient, etc., and achieve the effect of saving raw materials, small leakage current, and meeting electrical parameters

Inactive Publication Date: 2011-11-30
SHANDONG UNIV
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The present invention aims at the shortage of small varistor voltage gradient and waste of raw material resources in the existing zinc oxide varistor technology, and provides a modified antimony silicate with large varistor voltage gradient, which can meet application requirements and save material resources. ZnO varistor with high gradient

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] The composition of antimony silicate modified high gradient zinc oxide pressure sensitive material is (weight ratio): 91% ZnO, 2.70% Bi 2 o 3 , 2.00% Co 2 o 3 , 0.70% MnO 2 , 0.60% Cr 2 o 3 and 3.00% antimony silicate.

[0013] Through weighing, mixing and crushing, granulation, molding, sintering (sintering temperature: 1050°C, heat preservation for 120 minutes), upper electrode, welding lead wire, encapsulation and solidification to make a disc with a diameter of 12mm, after testing, its varistor parameters : Varistor voltage gradient V 1mm 350V / mm, leakage current I L (0.75V 1mA Bottom) less than 1μA, nonlinear coefficient 80-90, impulse current waveform of 8 / 20μs, current up to 8kA, change rate of varistor voltage less than 10%.

Embodiment 2

[0015] The composition of antimony silicate modified high gradient zinc oxide pressure sensitive material is (weight ratio): 91.3% ZnO, 2.71% Bi 2 o 3 , 1.92% Co 2 o 3 , 0.58% MnO 2 , 0.55% Cr 2 o 3 and 2.94% antimony silicate.

[0016] Through weighing, mixing and crushing, granulation, molding, sintering (sintering temperature: 1050°C, heat preservation for 120 minutes), upper electrode, welding lead wire, encapsulation and solidification to make a 34mm square piece, after testing, its varistor voltage gradient V 1mm 360V / mm, leakage current I L (0.75V 1mA Bottom) less than 1μA, non-linear coefficient 80~90, residual voltage ratio (the ratio of the residual voltage at the two ends of the device to the varistor voltage when the 8 / 20μs wave impacts a large current) V 10kA / V 1mA 1.85, V 20kA / V 1mA is 2.0.

Embodiment 3

[0018] The composition of antimony silicate modified high gradient zinc oxide pressure sensitive material is (weight ratio): 91.6% ZnO, 2.80% Bi 2 o 3 , 1.90% Co 2 o 3 , 0.60% MnO 2 , 0.40% Cr 2 o 3 and 2.70% antimony silicate.

[0019] Through weighing, mixing and crushing, granulation, molding, sintering (sintering temperature: 1050°C, heat preservation for 120 minutes), upper electrode, welding lead wire, encapsulation and solidification to make a disc with a diameter of 12mm, after testing, its varistor parameters : Varistor voltage gradient V 1mm 345V / mm, leakage current I L (0.75V 1mA Bottom) less than 1μA, nonlinear coefficient 80-90, impulse current waveform of 8 / 20μs, current up to 8kA, change rate of varistor voltage less than 10%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to view more

Abstract

The invention provides a high-gradient zinc oxide pressure-sensitive material modified by antimony silicate. The high-gradient zinc oxide pressure-sensitive material modified by antimony silicate is composed of the following components by weight: 91% to 92% of ZnO , 2.65%~2.80% Bi2O3, 1.85%~2.00% Co2O3, 0.50%~0.70% MnO2, 0.40%~0.60% Cr2O3 and 2.55%~3.00% antimony silicate. The production process of the above antimony silicate modified high-gradient zinc oxide pressure-sensitive material device is: weighing, mixing and crushing, granulation, molding, sintering, upper electrode, welding lead wire, encapsulation curing and testing, sintering temperature: 1050 ℃, keep warm for 120 minutes. The present invention adds an appropriate amount of antimony silicate and an optimized material ratio to the zinc oxide pressure-sensitive material, and its electrical properties are significantly improved. Multiple electrical parameters are excellent and have a high-voltage sensitive voltage gradient, which can not only meet the electrical requirements of general-purpose pressure-sensitive devices. parameters, while saving raw materials, compared with the existing general technology, raw materials can be saved by 70% to 95%.

Description

technical field [0001] The invention relates to a zinc oxide pressure-sensitive material. Background technique [0002] Varistors are materials used to make piezoresistors, which are electronic devices that are very sensitive to voltage; within a certain temperature and a specific voltage range, their current increases sharply with the increase of voltage. The resistance drops sharply as the voltage increases, so it is called a piezoresistor. Zinc oxide (ZnO) varistor is a new type of varistor developed in the past ten years. It has the characteristics of wide voltage sensitive voltage range, large nonlinear coefficient, strong flow capacity, fast response time, and small leakage current. It has been widely used in all fields of electricity consumption (where there are electrical appliances, it should be used as protection), and its function is to absorb overvoltage, pulse voltage, surge voltage, induced lightning voltage, and operating overvoltage, thereby Effectively pro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): H01C7/10C04B35/453C04B35/622
Inventor 陈洪存王伟伟李默宋飞耿建培王春明苏文斌
Owner SHANDONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap