High temperature resistance film for blister package of medical equipment and preparation method thereof

A technology for medical equipment and blister packaging, which is applied in the field of high-temperature sterilization-resistant blister packaging films for medical equipment and its preparation, can solve the problem of poor heat-sealing properties of the blister packaging films, affecting the health of patients, and ethylene oxide. Difficulty in penetration and other problems, to achieve the effect of excellent transparency and softness, good peeling fastness, and reduction of production links
CN101607616AInactive Publication Date: 2009-12-23NINGBO HUAFENG PACKAGE
0 Cites 18 Cited by

Patent Information

Authority / Receiving Office
CN Β· China
Patent Type
Applications(China)
Current Assignee / Owner
NINGBO HUAFENG PACKAGE
Publication Date
2009-12-23
Estimated Expiration
Not applicable Β· inactive patent

Smart Images

  • Figure 1
    Figure 1
  • Figure 2
    Figure 2
  • Figure 3
    Figure 3
Patent Text Reader

Abstract

The invention relates to a high temperature resistance film for blister package of medical sterilization equipment and a preparation method thereof. The first layer of the film is a heat-sealing layer A, and comprises blending resin of block copolymerized polypropylene and metallocene catalyzed polypropylene (mPP), wherein, the melting point of the block copolymerized polypropylene is more than 131 DEG C; the dosage of the mPP accounts for 20 to 50 percent of the blending rein by weight; the second layer of the film is a secondary inner layer B, and comprises homopolymerized polypropylene; the third layer of the film is an intermediate layer C, and comprises homopolymerized polypropylene; the fourth layer of the film is a binding layer D, and comprises polypropylene grafted by maleic anhydride; and the fifth layer is a weather resistance layer E, and comprises nylon 6 or 66. The film is prepared by adopting a bottom blowing water cooling type co-extrusion process or a casting method, wherein, after plastic is sufficiently melted, is inflated or cast by a die, the plastic is cooled at water temperature of between 15 and 18 DEG C. The preparation method is simple, and the product can endure high temperature steam sterilization for long time, and has good heat-sealing performance of dialyzing paper.
Need to check novelty before this filing date? Find Prior Art

Description

technical field

[0001] The invention relates to a high-temperature sterilization-resistant medical device blister packaging film and a preparation method thereof. Background technique

[0002] The medical equipment commonly used in operating rooms is usually packaged with ordinary polyethylene film when leaving the factory. Although it is produced in a purification workshop, it still does not meet the hygienic standards for surgical use. Therefore, these equipment must be thoroughly sterilized after packaging. Bacteria, in order to ensure the safety of the patient's life. The most commonly used method for disinfection and sterilization of packaged medical equipment is high-temperature sterilization, that is, high-temperature sterilization at about 131 degrees for 30 minutes, or penetration of ethylene oxide into the film to kill residual bacteria on the medical equipment. However, ordinary polyethylene film cannot withstand a high temperature of more than 100 degrees, and e...