Galvanized greenblack passivation solution and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A passivation solution, dark green technology, applied in the direction of metal material coating process, etc., can solve the problems of darkening of the coating, white corrosion, and the preparation method of galvanized dark green passivation solution has not yet been seen. Good adhesion and colorful effect
Active Publication Date: 2012-10-03
WEIFANG UNIVERSITY
View PDF0 Cites 1 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
However, zinc is a chemically active metal. If the workpiece is not post-treated after galvanizing, the coating will soon become dark and white corrosion will appear one after another.
Have not yet seen the report of galvanized dark green passivation solution and its preparation method
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0024] Embodiment 1, the component of every liter of passivation solution in the present embodiment is:
[0025] Chromic anhydride 20(g / L);
[0026] Phosphoric acid / (d=1.7) 11(ml / L);
[0027] Nitric acid / (d=1.4) 2.5(ml / L);
[0028] Sulfuric acid / (d=1.84) 2.5(ml / L);
[0029] Glacial acetic acid 4-5(ml / L);
[0030] Silver nitrate 0.008(g / L);
[0031] The balance is deionized water.
[0032] According to the amount of preparing 2000L passivation solution in this embodiment, its preparation method is as follows:
[0033] a. In a volume of 3m 3 Pre-inject 1000L deionized water into the passivation tank, then add the required amount of chromic anhydride according to the proportion of the above components, stir thoroughly to dissolve it, and then add the required amount of phosphoric acid, nitric acid, sulfuric acid, glacial acetic acid and nitric acid in sequence Silver, among which silver nitrate should be put into the beaker and dissolved in deionized water before adding to...
Embodiment 2
[0039] Embodiment 2, the component of every liter of passivation solution of the present embodiment is:
[0040] Chromic anhydride 25(g / L);
[0041] Phosphoric acid / (d=1.7) 10(ml / L);
[0042] Nitric acid / (d=1.4) 2 (ml / L);
[0043] Sulfuric acid / (d=1.84) 2 (ml / L);
[0044] Glacial acetic acid 4-5(ml / L);
[0045] Silver nitrate 0.007(g / L);
[0046] The balance is deionized water.
[0047] Other technical features of this embodiment are the same as those of Embodiment 1.
Embodiment 3
[0048] Embodiment 3, the component of every liter of passivation solution in the present embodiment is:
[0049] Chromic anhydride 23(g / L);
[0050] Phosphoric acid / (d=1.7) 10(ml / L);
[0051] Nitric acid / (d=1.4) 2.2(ml / L);
[0052] Sulfuric acid / (d=1.84) 2.3(ml / L);
[0053] Glacial acetic acid 4-5(ml / L);
[0054] Silver nitrate 0.008(g / L);
[0055] The balance is deionized water.
[0056] Other technical features of this embodiment are the same as those of Embodiment 1.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Login to View More
Abstract
The invention discloses a galvanized greenblack passivation solution and a preparation method thereof. The galvanized greenblack passivation solution mainly contains the following components: chromic anhydride, phosphoric acid, nitric acid, sulfuric acid, glacial acetic acid and silver nitrate. The preparation method of the galvanized greenblack passivation solution comprises the following steps of: previously infusing an appropriate amount of deionized water into a passivation groove; sequentially adding a certain amount of the chromic anhydride, the phosphoric acid, the nitric acid, the sulfuric acid, the glacial acetic acid and the silver nitrate; then complementally adding the deionized water to the passivation groove to reach a preset water level, and uniformly stirring. Passive filmformed on a galvanized workpiece has the advantages of elegant and glossy appearance, gentle luminosity, green tone with black, good adhesive force, very high surface hydrophobicity and good corrosion resistance and is just like a paint layer and different from an army green passive film and a black passive film.
Description
technical field [0001] The invention belongs to the technical field of electroplating, in particular to a galvanized dark green passivation solution and a preparation method thereof. Background technique [0002] Because the steel substrate is easy to rust, it is usually protected by electro-galvanizing in industry, that is, the steel substrate is protected by the sacrifice of zinc. However, zinc is a chemically active metal. If the workpiece is not post-treated after galvanizing, the coating will soon become dark and white corrosion will appear one after another. In order to avoid this phenomenon, a passivation solution is often used to passivate the galvanized layer of the workpiece, so that a passivation film is formed on the surface of the galvanized layer to improve its corrosion resistance. After the passivation film is formed, not only the corrosion resistance of the galvanized layer can be greatly improved, but also the appearance of the galvanized layer becomes col...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More 
Login to View More