Furfurylamine type benzoxazine resin/maleimide compound composition

A technology of maleimide and benzoxazine, applied in the field of furfurylamine type benzoxazine resin/maleimide compound composition, can solve problems such as lowering curing temperature, achieve low porosity, shrinkage small effect

Inactive Publication Date: 2011-04-20
BEIJING UNIV OF CHEM TECH
View PDF10 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The copolymerization of maleimide compound and benzoxazine obviously reduces the curing temperature, but there is no report

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Furfurylamine type benzoxazine resin/maleimide compound composition
  • Furfurylamine type benzoxazine resin/maleimide compound composition
  • Furfurylamine type benzoxazine resin/maleimide compound composition

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0050] Configure octamaleimidized POSS (OMPS) and bisphenol A furfurylamine type benzoxazine resin composition with a ratio (mass ratio) of 0.5:99.5. The composition is tested by DSC, and the curing peak temperature is measured to be 231 ℃.

Embodiment 2

[0052] Configure octamaleimidized POSS (OMPS) and bisphenol A furfurylamine type benzoxazine resin composition with a ratio (mass ratio) of 1:99, and the composition is subjected to DSC test, and the curing peak temperature is measured to be 230 ℃.

Embodiment 3

[0054] Configure octamaleimidized POSS (OMPS) and bisphenol A furfurylamine type benzoxazine resin composition with a ratio (mass ratio) of 2:98, and the composition is subjected to DSC test, and the curing peak temperature is measured to be 226 ℃.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
temperatureaaaaaaaaaa
temperatureaaaaaaaaaa
temperatureaaaaaaaaaa
Login to view more

Abstract

The invention relates to a furfurylamine type benzoxazine resin/maleimide compound composition, which is prepared from furfurylamine type benzoxazine resin and a series of maleimide group-containing compounds. The composition can be cured at lower temperature and used in a plurality of fields of coatings, thermosetting plastics, substrate resin of composite materials, and the like.

Description

technical field [0001] The present invention relates to a furfurylamine type benzoxazine resin / maleimide compound composition. Specifically, the present invention relates to a composition obtained by blending a furfurylamine-type benzoxazine resin and a maleimide compound, and a composition prepared by mixing the composition with other thermosetting resins. Background technique [0002] Benzoxazines are intermediates of a class of six-membered heterocyclic compounds composed of nitrogen and oxygen atoms synthesized from phenolic compounds, aldehydes and primary amine compounds. Cyclopolymerization produces nitrogen-containing networks similar to phenolic resins, called benzoxazine resins. In addition to the excellent properties of traditional phenolic resins such as high heat resistance, flame retardancy, excellent electrical and chemical properties, low water absorption, and low cost, benzoxazine resin does not release small molecules during the curing process. Zero shrin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L79/04C08K5/549C08G73/06
Inventor 徐日炜王磊王晶冯韬吴一弦余鼎声
Owner BEIJING UNIV OF CHEM TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap