Synthesis method of boron-containing beta zeolite

A synthetic method and technology of zeolite beta, applied in chemical instruments and methods, molecular sieves and alkali exchange compounds, inorganic chemistry, etc., can solve the problems of unfavorable large-scale industrial production, expensive templating agent, and high cost of zeolite beta, and reduce the total cost. Synthesis time, increased crystal synthesis and production speed, effects of high crystallinity

Active Publication Date: 2011-05-04
CHINA PETROLEUM & CHEM CORP +1
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0010] The above synthesis methods generally have problems such as large amount of template agent, low solid yield, and long synthesis cycle. Because the template agent is expensive, the cost of producing zeolite beta is high, which is not conducive to large-scale industrial production. The long synthesis cycle causes high energy consumption and Low production efficiency

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Tetraethylammonium hydroxide (TEAOH) is used as template, and the raw materials are borax, sodium hydroxide and silica sol.

[0026] The molar ratio of feeding is:

[0027] SiO 2 / B 2 o 3 =10;TEAOH / B 2 o 3 =5; Al 2 o 3 / B 2 o 3 = 1

[0028] Na 2 O / B 2 o 3 = 2; H 2 O / B 2 o 3 =500.

[0029] The first stage reaction conditions: 110°C, time: 10 hours

[0030] Second stage reaction conditions: 140°C, time: 30 hours

[0031] The third stage reaction condition: 180°C, time: 48 hours.

[0032] The main properties of the products obtained are listed in Table 1.

Embodiment 2

[0034] Tetraethylammonium hydroxide (TEAOH) is used as template, and the raw materials are borax, sodium hydroxide and silica gel.

[0035] The feeding ratio is:

[0036] SiO 2 / B 2 o 3 =30;TEAOH / B 2 o 3 =3.6; Al 2 o 3 / B 2 o 3 =0

[0037] Na 2 O / B 2 o 3 = 2; H 2 O / B 2 o 3 =200.

[0038] The first stage reaction conditions: 120°C, time: 20 hours

[0039] Second stage reaction conditions: 140°C, time: 40 hours

[0040] The third stage reaction condition: 180°C, time: 8 hours.

[0041] The main properties of the products obtained are listed in Table 1.

Embodiment 3

[0043]Tetraethylammonium hydroxide (TEAOH) is used as a template, and the raw materials are boric acid, sodium hydroxide and water glass.

[0044] The feeding ratio is:

[0045] SiO 2 / B 2 o 3 =55;TEAOH / B 2 o 3 =1.8; Al 2 o 3 / B 2 o 3 =0.5

[0046] Na 2 O / B 2 o 3 =12;H 2 O / B 2 o 3 =400.

[0047] The first stage reaction conditions: 140°C, time: 30 hours

[0048] Second stage reaction conditions: 150°C, time: 48 hours

[0049] The reaction condition of the third stage: 180°C, the time: 20 hours.

[0050] The main properties of the products obtained are listed in Table 1.

[0051] Table 1 obtains the main physical and chemical properties of the product

[0052] sample

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a synthesis method of boron-containing beta zeolite. The method comprises the following steps of: putting sodium hydroxide, TEAOH serving as a template agent and a silicon source into a reaction kettle, stirring and adding a boron source to gelatinate; sealing, heating and performing a hydrothermal synthesis method; and filtering, washing and drying so as to obtain the boron-containing beta zeolite, wherein the hydrothermal synthesis method is performed at three stages at which the reaction temperature rises in turn. The synthesis method of the boron-containing beta zeolite can shorten synthesis time on a large scale, reduces the using amount of the template agent, has high production efficiency and is suitable for mass production.

Description

technical field [0001] The invention relates to a method for synthesizing zeolite beta, in particular to a method for synthesizing boron-containing zeolite beta. Background technique [0002] Beta zeolite was first synthesized in 1967 and was invented by Wadlinger et al. of Mobil Corporation. In the ten years after the invention of β zeolite, due to the complexity of its structure, the basic and applied research on β zeolite has not received due attention. By the late 1980s, with the gradual discovery of the structure of zeolite beta, after the structure of zeolite beta was understood by people, its wide application value prompted people to continuously seek the improvement of its synthesis method. Synthetic reports also gradually increased. Beta zeolite, as a three-dimensional large-pore zeolite, has a unique topological structure and a high ratio of silicon to aluminum, so it exhibits good thermal stability, hydrophobicity, acid resistance, coking resistance and catalyti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C01B39/12
Inventor 谷明镝
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com