Refractory castable material containing ferrovanadium dregs

A technology of refractory castables and vanadium-iron slag, applied in the field of refractory castables, can solve the problems of resource waste, failure to be recycled, environmental pollution, etc., and achieve excellent refractory performance

Inactive Publication Date: 2011-08-10
PANZHIHUA IRON AND STEEL +1
View PDF2 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

A large amount of ferrovanadium slag is accumulated and cannot be recycled, whi

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Refractory castable material containing ferrovanadium dregs

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0010] Hereinafter, exemplary embodiments according to the present invention will be described in detail.

[0011] The refractory castable according to the present invention is mainly formed of coarse aggregate, fine aggregate, and a binder formed from fine powder of vanadium iron slag.

[0012] The vanadium iron slag used in the present invention contains 78% to 83% Al by weight percentage 2 O 3 , 10%~17% CaO, 1.0%~2.5% MgO, 0.2%~0.8% FeO, 0.6%~0.8% SiO 2 And 1.3% to 4.0% vanadium oxide. In addition, the vanadium iron slag is mainly composed of 35% to 40% calcium aluminate phase, 45% to 55% calcium dialuminate phase, 4% to 7% α-Al 2 O 3 It is composed of 7% to 8% glassy phase, 1% to 3% metal phase and 3% to 5% spinel phase.

[0013] The coarse aggregate, fine aggregate and binder will be described in detail below.

[0014] The refractory castable according to the present invention contains 30-50% coarse aggregate, 20-40% fine aggregate and 10-30% binder formed from vanadium iron slag...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a refractory castable material containing ferrovanadium dregs. The refractory castable material containing the ferrovanadium dregs comprises coarse aggregate, fine aggregate and a bonding agent formed by fine powder of the ferrovanadium dregs. The refractory castable material has excellent fireproof performance. A great amount of ferrovanadium dregs can be recycled.

Description

technical field [0001] The invention relates to a refractory castable, in particular to a refractory castable containing ferrovanadium slag. Background technique [0002] At present, with the rapid development of my country's metallurgical industry, the consumption of refractory materials is increasing, but the resources available for refractory materials are relatively small. Therefore, scientific and technical personnel have been working hard to develop resources that can be used as refractory materials. [0003] In addition, when using vanadium-titanium magnetite to smelt ferrovanadium, a large amount of ferrovanadium slag will be produced. A large amount of ferrovanadium slag is piled up and cannot be recycled, which not only causes environmental pollution, but also causes waste of resources. Contents of the invention [0004] The object of the present invention is to overcome the above and / or other deficiencies, and provide a novel refractory castable containing fer...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B35/66
Inventor 郝建璋高坤洪俊辉黎建明张金阳
Owner PANZHIHUA IRON AND STEEL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap