Diamond grinding tool of ceramic-metallic bond and preparation method of grinding tool

A technology of metal bond and ceramic bond, applied in metal processing equipment, grinding/polishing equipment, abrasives, etc., can solve the problems of high brittleness, long production cycle, poor wettability of diamond, etc., to improve strength and hardness, Improves toughness and strength, and is easy to shape and sharpen

Active Publication Date: 2011-08-17
长沙百通新材料科技有限公司
View PDF6 Cites 31 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, in the field of high-precision grinding, metal-bonded diamond abrasive tools are mainly used in China. Although this type of abrasive tool has the characteristics of strong bonding force, long grinding life, and good shape retention, it is easy to block due to excessive viscosity. Poor sharpness, difficult to trim and other shortcomings, often cause workpiece burns and low processing efficiency during processing
Vitrified bonded grinding tools are mainly used abroad. Vitrified bonded diamond grinding tools have great advantages over metal bo

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Diamond grinding tool of ceramic-metallic bond and preparation method of grinding tool
  • Diamond grinding tool of ceramic-metallic bond and preparation method of grinding tool
  • Diamond grinding tool of ceramic-metallic bond and preparation method of grinding tool

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] The specific process of this example is as follows image 3 shown.

[0031] Table 1: Ceramic-metal bond components and proportions

[0032] components

SiO 2

Al 2 o 3

B 2 o 3

Li 2 o

Na 2 o

K 2 o

ZnO

Ti

Al

wt%

44

9

19

6

7

3

5

5

2

[0033] Analytical pure SiO 2 、Al 2 o 3 、HBO 3 , Li 2 CO 3 、Na 2 CO 3 、K 2 CO 3 and ZnO as raw materials, calculated according to the formula in the above table, weighed, mixed evenly, put into a crucible, heated to 1300 ° C in a high-temperature frit furnace, kept for 2 hours, water quenched after the raw materials were completely melted, and then wet milled on a ball mill ( 1000r / min) for 24h, dry the wet-milled slurry in an oven at 100°C for 12h, dry-grind for 4h, and pass through a 200-mesh sieve to make a basic vitrified bond.

[0034] Add Ti powder (particle size ≤ 20 μm) and Al powder (particle size ≤ 20 μm)...

Embodiment 2

[0038] Table 2: Ceramic-metal bond components and proportions

[0039] components

SiO 2

al 2 o 3

B 2 o 3

Li 2 o

Na 2 o

K 2 o

ZnO

Ti

Al

wt%

48

12

12

3

8

4

2

8

3

[0040] Analytical pure SiO 2 、Al 2 o 3 、HBO 3 , Li 2 CO 3 、Na 2 CO 3 、K 2 CO 3 and ZnO as raw materials, calculated according to the above formula, weighed, mixed evenly, put into a crucible, heated to 1300 °C in a high-temperature frit furnace, kept for 2 hours, water quenched after the raw materials were completely melted, and then wet milled on a ball mill (1000r / min) for 24 hours, dry the wet-milled slurry in an oven at 100°C for 12 hours, then dry-mill it for 4 hours and pass it through a 200-mesh screen to make a basic vitrified bond.

[0041]Add Ti powder (particle size ≤ 20 μm) and Al powder (particle size ≤ 20 μm) designed in the formula to the basic vitrified bond, and mix them ...

Embodiment 3

[0046] Table 3: Ceramic-metal bond components and proportions

[0047] components

SiO 2

al 2 o 3

B 2 o 3

Li 2 o

Na 2 o

K 2 o

ZnO

Ti

Al

wt%

41

8

18

6

9

6

3

6

3

[0048] Analytical pure SiO 2 、Al 2 o 3 、HBO 3 , Li 2 CO 3 、Na 2 CO 3 、K 2 CO 3 and ZnO as raw materials, calculated according to the above formula, weighed, mixed evenly, put into a crucible, heated to 1300 °C in a high-temperature frit furnace, kept for 2 hours, water quenched after the raw materials were completely melted, and then wet milled on a ball mill (1000r / min) for 24 hours, dry the wet-milled slurry in an oven at 100°C for 12 hours, then dry-mill it for 4 hours and pass it through a 200-mesh screen to make a basic vitrified bond.

[0049] Add Ti powder (particle size ≤ 20 μm) and Al powder (particle size ≤ 20 μm) designed in the formula to the basic vitrified bond, and mix them ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Granularityaaaaaaaaaa
Granularityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a diamond grinding tool of a ceramic-metallic bond and a preparation method of the grinding tool. The preparation method comprises the following steps of: firstly, preparing the ceramic-metallic bond by ball milling the following components in percentage by weight: 40 to 50 percent of silicon dioxide (SiO2), 8 to 15 percent of aluminium oxide (Al2O3), 12 to 20 percent of diboron trioxide (B2O3), 3 to 6 percent of lithium oxide (Li2O), 6 to 12 percent of sodium oxide (Na2O), 3 to 6 percent of potassium oxide (K2O), 2 to 8 percent of zinc oxide (ZnO), 1 to 10 percent of titanium (Ti) and 1 to 5 percent of aluminium (Al); secondly, mixing the ceramic-metallic bond with a diamond abrasive to obtain a mixed material, and then adding 3 to 5 mass percent of wetting agent into the mixed material to obtain a raw material of the grinding tool; and finally, carrying out hot-forming and cooling de-moulding on the raw material of the grinding tool respectively to obtain the diamond grinding tool of the ceramic-metallic bond. The diamond grinding tool of the ceramic-metallic bond provided by the invention has the advantages of the diamond grinding tool of a metallic bond and the grinding tool of a ceramic bond.

Description

technical field [0001] The invention relates to a ceramic-metal bonded diamond grinding tool and a preparation method thereof. Background technique [0002] Diamond grinding tools are widely used in the processing of engineering ceramic materials, crystal materials, semiconductor materials, hard alloy materials and composite materials. At present, in the field of high-precision grinding, metal-bonded diamond abrasive tools are mainly used in China. Although this type of abrasive tool has the characteristics of strong bonding force, long grinding life, and good shape retention, it is easy to block due to excessive viscosity. The disadvantages of poor sharpness and difficult trimming often cause workpiece burns and low processing efficiency during processing. Vitrified bonded grinding tools are mainly used abroad. Vitrified bonded diamond grinding tools have great advantages over metal bonded diamond grinding tools in terms of grinding accuracy and grinding efficiency. Due t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B24D3/14B24D3/06B24D18/00
Inventor 万隆王志起刘小磐胡伟达翟浩冲张国威
Owner 长沙百通新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap