Extrusion blown molded bottles with high stiffness and transparency

A technology of high melt strength and nucleating agent, applied in the field of new products containing the polypropylene composition, can solve the problems of uneven outer surface properties, limited conception, low transparency and the like

Active Publication Date: 2013-09-11
BOREALIS AG
View PDF13 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

As a result, extrusion blow molded products such as bottles typically show less clarity than any injection molded product
For example, extrusion blow molded bottles often have inhomogeneous surface properties (flow marks, melt cracks) on the inside and / or outside, resulting in lower overall clarity compared to injection molded bottles or injection stretch blow molded products (ISBM)
Some increase in clarity can be achieved by visbreaking of polymeric materials, but this concept is rather limited and has only been applied to relatively small bottles since a certain level of melt strength is necessary for proper handling
Therefore, larger bottles (capacities of 1 L or more) cannot be produced using visbroken polypropylene in the extrusion blow molding process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Extrusion blown molded bottles with high stiffness and transparency
  • Extrusion blown molded bottles with high stiffness and transparency
  • Extrusion blown molded bottles with high stiffness and transparency

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0045] The preparation of the random propylene copolymer (R-PP) and the visbreaking will be described in more detail below.

[0046] As another essential requirement of the present invention, high melt strength polypropylene (HMS-PP) must be used. This polymer type is characterized by a certain degree of branching. A possible high melt strength polypropylene (HMS-PP) is known as Y / H-polypropylene, described for example in EP 0 787 750, i.e. a single branched polypropylene type (Y-polypropylene, having a backbone and A type of polypropylene in which a single long side chain, similar in structure to "Y"), and its inner polymer chains are connected by bridging groups (structurally similar to "H"). These polypropylenes are characterized by a rather high melt strength. One parameter of the degree of branching is the branching index g'. The branching index g' is related to the number of branches in the polymer. The branching index g' is defined as g'=[IV] br / [IV] lin , where ...

Embodiment

[0132] 1. Definition / measurement method

[0133] Unless otherwise stated, the following definitions of terms and measurement methods apply to the above general description of the invention and to the following examples.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
traction forceaaaaaaaaaa
traction forceaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

A polypropylene composition comprising a random propylene copolymer, a high melt strength polypropylene having a branching index g′ of 0.9 or less and a clarifier, wherein the polypropylene composition has a MFR2 (230° C.) of at least 2.0 g / 10 min.

Description

technical field [0001] The present invention relates to a new polypropylene composition, its use and manufacture, and also to new articles comprising said polypropylene composition. Background technique [0002] It is well known in the art of polymers that different applications require specially tailored polymers to obtain individually required properties. For example, polymers for injection molding must have other properties of polymers for blow molding. [0003] Extrusion blow molding, for example, is a special process that allows bottles of different sizes and shapes to be produced in a flexible and inexpensive manner. The main disadvantage of this process is that its solidification step is very specific compared to conventional injection molding. [0004] In the extrusion blow molding process, the polymer melt is first extruded into the air through a tubular die to form a polymer hose, and then the above-mentioned polymer hose (typically called a "parison" in the tech...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/14B29C49/04
CPCB29C49/0005C08L2023/42B29K2023/12C08L23/142B29C49/04C08L23/10C08L2205/02B29C2049/7862C08L2666/06C08F210/06C08F210/16C08F2500/09C08F2500/11C08F2500/12
Inventor K·贝恩莱特纳M·屈尔梅莱M·基希贝格尔H·普拉默
Owner BOREALIS AG