Method for sintering polytetrafluoroethylene

A polytetrafluoroethylene and sintering furnace technology, which is applied in the chemical and chemical industry, can solve the problems of highly toxic, non-wear-resistant polytetrafluoroethylene, affecting product performance, appearance, etc., to achieve good sealing effect, strengthen the sealing effect, The effect of suppressing the evolution of hydrogen fluoride

Active Publication Date: 2011-10-05
广东新志密封技术有限公司
View PDF3 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The difference in process conditions such as sintering temperature and cooling rate directly affects the molecular weight, crystallinity and porosity of the product, and these three affect the physical, mechanical and electrical properties of the product. At the same time, the completion of the sintering process also affects the product. The size and distribution of residual stress in the product, so the improper control of the sintering process will lead to warping, deformation and even cracking of the product, whi

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for sintering polytetrafluoroethylene
  • Method for sintering polytetrafluoroethylene

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0027] Example 1

[0028] This embodiment provides a method for sintering polytetrafluoroethylene, which uses a sintering device, see figure 1 ,

[0029] The sintering furnace includes the sintering device including a sintering furnace body (1), a nitrogen delivery device (6), a program control device, and a condenser;

[0030] The sintering furnace body includes four zones: a drying zone (2), a preheating zone (3), a sintering zone (4), and a cooling zone (5);

[0031] Said drying zone (2) and preheating zone (3), preheating zone (3) and sintering zone (4), sintering zone (4) and cooling zone (5) are each provided with an isolated furnace (8), isolation Furnace (9), isolated furnace (10);

[0032] The program control device includes: a temperature detection and control device, the temperature detection and control device includes: a temperature sensor, the temperature sensor is multiple, respectively installed in the inner drying zone (2), preheating zone (3), Sintering zone (4), co...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a method for sintering a polytetrafluoroethylene sealing ring. The invention employs a sintering furnace which comprises a sintering furnace body, a nitrogen conveying device and a program control device. The sintering furnace body comprises four zones such as a drying zone (2), a preheating zone (3), a sintering zone (4) and a cooling zone (5). The method comprises the following steps: (1) preparing polytetrafluoroethylene stock;(2)drying polytetrafluoroethylene stock in the drying zone; (3) preheating stock in the preheating zone; (4) sintering stock in sintering zone; (5)cooling. According to the invention, the sintering sealing effect and automatic control can be enhanced for effectively inhibiting the escape of hydrogen fluoride during the sintering process, metal powder modified materials filled in polytetrafluoroethylene is avoided an oxidation generated by contacting with air in a high temperature through a heat nitrogen cycle, thereby the usage performance and the appearance of the products can be improved.

Description

technical field [0001] The invention relates to the technical field of chemistry and chemical engineering, in particular to a method for sintering polytetrafluoroethylene. Background technique [0002] Polytetrafluoroethylene (PTFE) has excellent chemical stability, corrosion resistance, sealing, high lubrication and non-stickiness, electrical insulation and good aging resistance, and excellent temperature resistance (can be used at +250°C to -180°C Long-term work at high temperature), but its fluidity is poor, it is easy to decompose, and it is a polymer material that generates corrosive gas when decomposed. In the molding process, the temperature must be strictly controlled. If the temperature is not properly controlled, hydrogen fluoride will decompose and escape, causing poisoning of animals and humans within 2 square kilometers. At present, the recycling technology of polytetrafluoroethylene is not yet mature, and it is generally formed at one time, so there is no room...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B29C71/02C08L27/18
Inventor 周完成周安梁军
Owner 广东新志密封技术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap