A technology of stainless steel slag and cooling method, applied in the direction of improving process efficiency, etc., can solve problems such as prone to explosion, and achieve the effect of eliminating potential safety hazards
Inactive Publication Date: 2011-11-02
SHANXI TAIGANG STAINLESS STEEL CO LTD
View PDF2 Cites 5 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
This cooling method draws water at a relatively high temperature. Due to the heat accumulation inside the steel slag surface and the cold crust, it is easy to explode. In order to ensure the cooling effect and eliminate potential safety hazards, it is urgent to study a reasonable stainless steel slag tank. craft
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0009] (1) Natural cooling (stand still and air-cooled) for 42 hours, that is, the slag is discharged from the AOD furnace for smelting stainless steel, and the AOD slag is poured into 16.5m 3 In the slag tank, transport to the slag yard, and cool naturally (stand in air) for 42 hours.
[0010] (2) Boiling for 23 hours, the slag tank will be lifted to the workshop for heating and stewing for 23 hours, and the flow rate of the water nozzle is 1.2t / h;
[0011] (3) Turn over the tank, turn over the cooled AOD furnace stainless steel slag, pour out the stainless steel slag, the amount of red slag is 9.14%, and the remaining 90.86% of the stainless steel slag can be directly processed for steel slag: breaking, magnetic separation, iron recovery, Beneficial metals of chromium and nickel.
Embodiment 2
[0013] (1) Natural cooling (standby air cooling) for 38 hours, that is, the slag is discharged from the AOD furnace for smelting stainless steel, and the AOD slag is poured into 11m 3 In the slag tank, transported to the slag yard, and cooled naturally (stand still in air) for 38 hours.
[0014] (2) Stew with water for 20 hours, then lift the slag tank to the workshop for water and heat for 20 hours, and the flow rate of the water nozzle is 0.8t / h;
[0015] (3) Turn over the tank, turn over the cooled AOD furnace stainless steel slag, pour out the stainless steel slag, the amount of red slag is 8.84%, and the remaining 91.16% of the stainless steel slag can be directly processed for steel slag: breaking, magnetic separation, iron recovery, Beneficial metals of chromium and nickel.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a method for cooling stainless steel slag in a tank, which belongs to a stainless steel production process. The method comprises: discharging stainless steel slag into a slag tank, transporting the stainless steel slag to a slag field and naturally cooling (standing for air cooling) for 36 to 42 hours; hoisting the slag tank to a water pumping and hot stewing workshop, and performing water pumping and hot stewing for 18 to 24 hours, wherein the flow of the water pumping spray is 0.8 to 1.3 ton/h; and turning cooled stainless steel slag in the tank, wherein the content of red slag is reduced to less than 10 percent, and the left over 90 percent of stainless steel slag can be directly subjected to steel slag treatment, crushing and magnetic separation and favorable metals including iron, chromium and nickel are recovered. When the method is used, the cooling and hot stewing effect of the stainless steel slag is ensured, safety hazards are eliminated, the red slag content in the stainless steel slag is reduced to less than 10 percent, and direct on-line treatment capacity reaches over 90 percent.
Description
technical field [0001] The invention belongs to a stainless steel production process, and in particular relates to a cooling method in a stainless steel slag tank. Background technique [0002] In order to reduce the dust pollution during the cooling process of stainless steel slag, the cooling method in the tank is usually adopted. This kind of cooling method draws water at a higher temperature. Due to the accumulation of heat inside the steel slag surface and the cold crust, it is easy to explode. In order to ensure the cooling effect and eliminate potential safety hazards, it is urgent to study a reasonable stainless steel slag tank internal cooling. craft. Contents of the invention [0003] In order to eliminate the potential safety hazard caused by internal heat accumulation due to cold crusting on the surface of steel slag, the invention provides a cooling method in a stainless steel slag tank. [0004] The operation steps of the present invention are as follows:...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more