Preparation method for lamination blocking type package materials

A packaging material and barrier technology, which is applied in the field of preparation of laminated barrier packaging materials, can solve the problems of high surface state and fiber morphology, and achieve the effect of reducing the difficulty of degradation, lowering requirements, and reducing difficulty in recycling

Active Publication Date: 2012-03-21
GREATVIEW BEIJING TRADING CO LTD
View PDF5 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] For this reason, there are two technical problems to be solved by the present invention, one is to directly prepare the printing surface and supporting layer with cardboard, which will have high requirements on the surface state and fiber shape of the cardboard itself; the other is to reduce the waste of aluminum foil , avoiding the environmental problems caused by the difficult degradation and recycling of aluminum foil

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method for lamination blocking type package materials
  • Preparation method for lamination blocking type package materials

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0026] A preparation method of a laminated barrier packaging material, the preparation method is as follows:

[0027] Step 1: Extrude coating on at least one side of the substrate of the support layer, and at the same time perform surface treatment on the substrate of the substrate after coating;

[0028] Step 2: Coating the barrier coating solution on the surface of the film in step 1, and drying to obtain a barrier layer;

[0029] Step 3: extruding a composite heat-sealing layer on the outer surface of the prepared barrier layer;

[0030] Step 4: compound a light-shielding layer on one side of the support layer base material in step 1, and make the surface tension reach more than 38 dynes after pretreatment;

[0031] Step 5: Coating the printing layer coating solution on the outer surface of the prepared light-shielding layer, and drying to obtain the printing layer;

[0032] Step 6: extruding the protective layer on the outer surface of the printing layer to compound the ...

Embodiment 1

[0051] like figure 1 As shown, it includes a heat-sealing layer 8, an adhesive layer 5 tightly compounded on the heat-sealing layer 8 from bottom to top, a barrier layer, an adhesive layer 5, and a support layer 4, and the upper side of the support layer 4 is from bottom to top Covered with a light-shielding layer 3, a printing layer 2 and a protective layer 1 in sequence, wherein the printing layer 2 is a mixture of nano-alumina and polyvinyl alcohol, the weight ratio of nano-silicon oxide and polyvinyl alcohol is 1:5, and the weight ratio of nano-silicon oxide The specific surface area is 220m 2 / g, the degree of polymerization of polyvinyl alcohol is 3000, its degree of alcoholysis is 87%, the thickness of the printing layer 2 is 10um; the protective layer 1 is a polypropylene layer, the purpose is to protect the printing layer 2 from being scratched and damaged, the protective layer 1 has a thickness of 10um, and the light-shielding layer 3 includes a mixture of polyolefi...

Embodiment 2

[0053] structured as figure 1 Shown, wherein the difference with embodiment 1 is:

[0054] The protective layer 1 is a polyethylene layer, and the thickness of the protective layer 1 is 20um;

[0055] The printing layer 2 is a mixture of nano-silicon oxide and poly(meth)acrylic acid, the weight ratio of nano-silicon oxide and poly(meth)acrylic acid is 2:1, and the specific surface area of ​​nano-silicon oxide is 175m 2 / g, wherein the thickness of the printing layer 2 is 15um;

[0056] The light-shielding layer 3 includes polyolefin resin, carbon black and titanium dioxide, wherein carbon black is 10% of the light-shielding layer, titanium dioxide is 20% of the light-shielding layer, and the balance is polyolefin. Carbon black and titanium dioxide are mixed and co-extruded respectively. The thickness is 30um;

[0057] The support layer 4 is a biaxially stretched foamed polyester material, and the thickness of the support layer is 40um;

[0058] The thickness of the bonding...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method for lamination blocking type package materials, which comprises the steps that: a laminated film is extruded at least one side surface of a support layer base material, simultaneously, the surface treatment is carried out on the laminated support layer base material, blocking type coating liquid is coated onto the surface of the laminated film, a blocking layer is prepared through baking, a composite hot sealing layer is extruded on the outer surface of the prepared blocking layer, a light shading layer is compounded on one side surface of the support layer base material, in addition, the surface tension reaches higher than 38 dynes through pretreatment, in addition, printing layer coating liquid is coated on the outer side surface of the light shading layer, a printing layer is obtained after baking, and a protection layer is extruded on the outer side surface of the printing layer, so the printing layer and the protection layer are compounded. The light shading layer and the printing layer are compounded on the support layer, the requirement on paper boards by printing is reduced, the resolution ratio of images can be greatly improved, simultaneously, the cost is reduced, in addition, an oxide coating is used for replacing an aluminum foil to be used as the blocking layer, the problems of difficult recovery and difficult degradation caused by aluminum foil discharge are reduced, and simultaneously, high oxygen blocking performance is provided.

Description

technical field [0001] The invention relates to a preparation method of a packaging material, more specifically, to a preparation method of a laminated barrier packaging material. Background technique [0002] Aseptic packaging material is a multi-layer laminated packaging material, which is mainly composed of paper, plastic and aluminum foil. It has excellent oxygen and moisture barrier functions, so the food it packs, including liquid food, has a long shelf life. [0003] However, this multi-layer aseptic packaging material has its own limitations. First, it needs to use cardboard directly as the printing receiving surface and support layer, which has high requirements for the surface state and fiber morphology of the cardboard itself. Ordinary It is difficult for cardboard to meet the specific printing requirements, and papermaking consumes a lot of technical materials, and the chemicals used in papermaking are very harmful to the environment; secondly, it uses aluminum f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B27/06B32B27/30B32B27/18B32B33/00B32B7/10B65D65/40
CPCB32B27/08B32B27/20B32B27/32B32B27/34B32B27/36B32B2250/24B32B2307/7244B32B2439/70Y02W30/80
Inventor 不公告发明人
Owner GREATVIEW BEIJING TRADING CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com